Effect of rotation speed on friction behavior of rotary friction welding of AA6061-T6 aluminum alloy

  • Li Xun 
  • Li Jinglong 
  • Jin Feng 
  • Xiong Jiangtao 
  • Zhang Fusheng 
Research Paper
  • 44 Downloads

Abstract

The continuous drive rotary friction welding was conducted on AA6061-T6 aluminum alloy rods under different rotation speeds. The effect of rotation speed on friction behavior was investigated via analyzing the friction torque, temperature, microstructure and axial shortening. The results show that the curves of friction time and friction work as a function of rotation speed present like “V-shape” with the minimum values locating at around 900 rpm. Besides, the ratio of friction work in the first stage to that in the whole process increases and then decreases after reaching the maximum value at 900 rpm. As the rotation speed increases, the heat pattern gradually changes from the “scissor-shape” into “double-ellipse shape” that is acquired at 900 rpm and eventually into the “disc-shape.” Additionally, the axial shortening rate at the steady stage initially reaches a high constant value and then drops to another constant value that is nearly half of the high value when the rotation speed is not less than 1500 rpm. The high axial shortening rate can be ascribed to the process of filling the unbonded area remained at the interface after the first friction stage.

Keywords

Rotary friction welding Friction behavior Rotation speed Aluminum alloy 

Notes

Funding information

This work is supported by the National Natural Science Foundation of China (Grand No: 51475376, 51575451).

References

  1. 1.
    Williams JC, Starke EA (2003) Progress in structural materials for aerospace systems 1. Acta Mater 51(19):5775–5799CrossRefGoogle Scholar
  2. 2.
    Miller WS, Zhuang L, Bottema J, Wittebrood AJ, Smet PD, Haszler A, Vieregge A (2000) Recent development in aluminium alloys for the automotive industry. Mater Sci Eng A 280(1):37–49CrossRefGoogle Scholar
  3. 3.
    Threadgill PL, Leonard AJ, Shercliff HR, Withers PJ (2009) Friction stir welding of aluminium alloys. Int Mater Rev 54(2):49–93CrossRefGoogle Scholar
  4. 4.
    Dursun T, Soutis C (2014) Recent developments in advanced aircraft aluminium alloys. Mater Des 56(4):862–871CrossRefGoogle Scholar
  5. 5.
    Pakdil M, Am G, KoAk M, Erim S (2011) Microstructural and mechanical characterization of laser beam welded AA6056 Al-alloy. Mater Sci Eng A 528(24):7350–7356CrossRefGoogle Scholar
  6. 6.
    Rest CVD, Jacques PJ, Simar A (2014) On the joining of steel and aluminium by means of a new friction melt bonding process. Scripta Mater 77(12):25–28CrossRefGoogle Scholar
  7. 7.
    Vill VI (1962) Friction welding of metals. American Welding Society; trade distributor: Reinhold Pub. CoGoogle Scholar
  8. 8.
    Hasui A, Fukushima S (1977) On the torque in friction welding. Trans Jpn Weld Soc 8(1):26–32Google Scholar
  9. 9.
    Uday M, Ahmad Fauzi M, Zuhailawati H, Ismail A (2010) Advances in friction welding process: a review. Sci Technol Weld Join 15(7):534–558CrossRefGoogle Scholar
  10. 10.
    Kimura M, Choji M, Kusaka M, Seo K, Fuji A (2006) Effect of friction welding conditions on mechanical properties of A5052 aluminium alloy friction welded joint. Sci Technol Weld Join 11(2):209–215CrossRefGoogle Scholar
  11. 11.
    Kimura M, Choji M, Kusaka M, Seo K, Fuji A (2005) Effect of friction welding conditions and aging treatment on mechanical properties of A7075-T6 aluminium alloy friction joints. Sci Technol Weld Join 10(4):406–412CrossRefGoogle Scholar
  12. 12.
    Duffin F, Bahrani A (1973) Frictional behaviour of mild steel in friction welding. Wear 26(1):53–74CrossRefGoogle Scholar
  13. 13.
    M. Kimura, A. Ichihara, M. Kusaka, K. Kaizu (2012) Joint properties and their improvement of AISI 310S austenitic stainless steel thin walled circular pipe friction welded joint. Mater. Des 38(38–46)Google Scholar
  14. 14.
    Li W, Vairis A, Preuss M, Ma T (2016) Linear and rotary friction welding review. Int Mater Rev 61(2):71–100CrossRefGoogle Scholar
  15. 15.
    Crossland B (1971) Friction welding. Contemp Phys 12(6):559–574CrossRefGoogle Scholar
  16. 16.
    E. Ravikumar, N. Arunkumar, G. Sunnapa (2013) Characterization of mechanical properties of aluminium (AA 6061-T6) by friction welding. 3rd International Conference on mechanical, automotive and materials engineering (ICMAME)Google Scholar
  17. 17.
    Kimura M, Mio H, Kusaka M, Seo K, Fuji A (2002) Observation of joining phenomena in first phase of friction welding. Study of joining mechanism of friction welding (report 1). Q J Jpn Weld Soc 20(3):425–431CrossRefGoogle Scholar
  18. 18.
    Maalekian M, Kozeschnik E, Brantner H, Cerjak H (2008) Comparative analysis of heat generation in friction welding of steel bars. Acta Mater 56(12):2843–2855CrossRefGoogle Scholar
  19. 19.
    Kimura M, Inoue H, Kusaka M, Kaizu K, Fuji A (2010) Analysis method of friction torque and weld Interface temperature during friction process of steel friction welding. J Solid Mech Mater Eng 4:401–413CrossRefGoogle Scholar
  20. 20.
    Kimura M, Iijima T, Kusaka M, Kaizu K, Fuji A (2014) Joining phenomena and tensile strength of friction welded joint between pure titanium and low carbon steel. Mater Des 55(152–164)Google Scholar
  21. 21.
    Olson DL (1993) ASM handbook: welding, brazing, and soldering. Asm IntlGoogle Scholar
  22. 22.
    Leider PJ, Bird RB (1974) Squeezing flow between parallel disks. I. Theoretical analysis. Indonesia 13(4):336–341Google Scholar

Copyright information

© International Institute of Welding 2018

Authors and Affiliations

  • Li Xun 
    • 1
    • 2
  • Li Jinglong 
    • 2
  • Jin Feng 
    • 1
    • 2
  • Xiong Jiangtao 
    • 2
  • Zhang Fusheng 
    • 2
  1. 1.State Key Laboratory of Solidification ProcessingNorthwestern Polytechnical UniversityXi’anPeople’s Republic of China
  2. 2.Shaanxi Key Laboratory of Friction Welding TechnologiesNorthwestern Polytechnical UniversityXi’anPeople’s Republic of China

Personalised recommendations