Heat-affected zone crack healing in IN939 repaired joints using hot isostatic pressing
- 31 Downloads
Simulation defects in IN 939 superalloy were repaired by gas tungsten arc welding (GTAW) using Nimonic C263 as filler metal. The microstructures and chemical compositions of fusion zone under the condition of as-welded and post-weld heat treatment (PWHT) were investigated by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron probe X-ray microanalysis (EPMA). Moreover, the liquation cracking and strain age cracking in heat-affected zone (HAZ) were characterized as well. Post-weld hot isostatic pressing (HIP) was also applied to heal the HAZ cracks. The results show that elements segregation at as-welded joints could be significantly reduced by PWHT. HAZ cracks consisted of liquation cracking and strain age cracking. The liquation cracking was shorter than the strain age cracking. HIP is an effective way to heal the cracks in the repaired joints especially for liquation cracking. Though the strain age cracking can be healed by HIP, the healed trace concentrated with Al, Ti, B, and Zr elements can still be detected. Post-weld HIP is a necessary process to obtain crack-free joints.
KeywordsIN 939 superalloy Microstructure HAZ cracks HIP Crack healing
The authors thank Zhanhui Du for the X-ray non-destructive testing and hot isostatic pressing. The authors are also grateful to Professor Shunnan Zhang and Xianchao Hao for the valuable discussions.
- 1.Gibbons TBS, Stickler R (1982) IN939: Metallurgy, properties and performance, in: R.B.E. al. (Ed.) high temperature alloys for gas turbines 1982, Brussels and Luxembourg, pp. 369–393Google Scholar
- 3.Göran Sjöberg DI, Gabel J, Caballero O, Brooks JW, Ferté J-P, Lugan A (2004) Evaluation of the IN 939 alloy for large aircraft engine structures. Superalloys 2004:441–450Google Scholar
- 4.Kim Dae -Young HJ-H, -Soo KK, Joong-Geun Y (2000) A study on fusion repair process for a precipitation hardened IN738 Ni-based superalloy. J Eng Gas Turbines Power 122:5Google Scholar
- 9.Thamburaj R, Wallace w, Goldak JA (1983) Post-weld heat-treatment cracking in superalloys. Int Metals Rev 28(1):1–22Google Scholar
- 18.Reed RC, The superalloys fundamentals and applications, Cambridge University Press 2006Google Scholar
- 20.Guédou JY, Crozet C, Devaux A, Béchet D, Choné J (2014) Microstructure stability: optimisation of 263 Ni-based superalloy, MATEC Web of Conferences, EDP Sciences, p. 17006Google Scholar
- 21.Ojo OA, Richards NL (2012) Heat-affected zone cracking in welded nickel superalloys, Welding and joining of aerospace materials, Woodhead Publishing Limited, pp. 142–177Google Scholar