Effect of the surface charge of silica nanoparticles on oil recovery: wettability alteration of sandstone cores and imbibition experiments
- 260 Downloads
Recently, inorganic nanomaterials have emerged as promising wettability modifiers to improve oil recovery. Among them, silica nanoparticles (SNPs) have gained a privileged place due to their outstanding properties. Several studies have reported the effectiveness of SNPs on this particular application. However, there is an increasing interest of understanding the parameters that may play an important role on oil recovery using nanofluids. The impact of particle size, particle concentration and types of nanoparticles on oil recovery have been reported. Nevertheless, to our knowledge, the influence of the surface charge has not been investigated. In this work, the effect of the surface charge of SNPs on oil recovery was studied. Silica nanoparticles with different charge profiles (negative, positive and slightly negative) were synthesized and characterized using transmission electron microscopy, FT-IR, dynamic light scattering and ζ-potential. Negatively charged nanoparticles (Neg-SNPs; − 33.45 ± 2.75) were obtained by following the Stöber process. The silanol groups present on the surface of the Neg-SNPs are responsible for the negative surface charge. Positively charged nanoparticles (AP-SNPs; + 42.25 ± 1.9) and slightly negatively charged nanoparticles (MeO-PEG-SNPs; − 12.20 ± 0.42) were obtained by grafting (3-aminopropyl) triethoxysilane and methoxy polyethylene glycol (MeO-PEG2K) onto the surface of Neg-SNPs, respectively. The impact of silica materials with different charge profiles on wettability alteration and oil displacement at different concentrations (100 or 200 mg/L) was evaluated by contact angle estimation and spontaneous imbibition experiments. The results demonstrated that the surface charge of SNPs transformed the wettability of the sandstone cores and impacted oil recovery in a different extent. While MeO-PEG-SNPs showed the best performance at a low concentration, Neg-SNPs were the most effective in changing the rock wettability and removing oil from sandstone cores at a higher concentration. Overall, our results not only allowed to identify the impact of surface charge on oil recovery but also the effect of SNPs concentration on the suitability of the treatment for enhancing the oil recovery process.
KeywordsSilica nanoparticles Rock wettability Oil recovery and contact angle
Because wettability is one of the most important properties controlling oil recovery [2, 7, 26], the efficiency of this process has been improved using wettability modifiers such as surfactants and polymers [6, 29]. The utilization of these agents can induce changes in the wettability of the rock surface from an oil-wet to a water-wet state, which affects the flow behavior of water and oil in porous media . Nevertheless, the use of polymers and surfactants is limited because their mechanical and shear properties are significantly affected at the high temperatures and salinity present in oil reservoirs [6, 17]. Therefore, it is critical to find novel approaches to enhance the oil recovery process. For decades, nanomaterials have attracted considerable interest due to their novel properties in a wide variety of scientific areas [5, 12, 28, 34]. Recently, the utilization of nanoparticles (NPs) for oil recovery has been proposed and evaluated [19, 24, 25, 34].
Different studies have reported that NPs can improve the wettability of the reservoir rock and they are more stable than surfactants and polymers at the conditions found in porous media [6, 34]. Emerging inorganic nanoparticles such as iron oxide, titanium oxide, aluminum oxide and silica have been used for this application [9, 14, 16, 21]. A comparative study using different types of nanofluids demonstrated that silica nanoparticles (SNPs) had one of the best performances for enhancing oil recovery . This is one of the reasons why this type of nanoparticles has attracted wide spread interest for oil displacement from porous media. Additionally, SNPs involve low cost of fabrication, stable structure and their surface can be easily modified by known chemical methods [23, 27]. There are several studies demonstrating their effectiveness in the wettability alteration of reservoir rocks [1, 10, 18, 25]. For example, Ju et al. studied the change in the wettability of the sandstone surface using lipophobic and hydrophilic polysilicon nanoparticles . The authors claimed that polysilicon nanoparticles are suitable agents for enhancing oil recovery. They also suggested that the concentration of the nanoparticles plays an important role during the oil recovery process. Similarly, Roustaei et al. demonstrated that SNPs are effective enhanced oil recovery agents for light and intermediate oil reservoirs . The results showed that the utilization of SNPs transformed the rock wettability and efficiently increased the oil recovery from light oil reservoirs.
Two classic mechanisms involved in oil recovery using nanofluids have been reported: (1) nanofluids decrease the interfacial tension between the water and the oil phase and (2) nanofluids can alter the rock wettability [3, 20, 26, 34]. Recently, a new mechanism of oil displacement from a solid substrate using nanoparticles has been proposed [15, 33]. It is based on the ability of the nanoparticles to form two-dimensional layered structures in the confines of the three-phase (solid–oil–aqueous phase) contact line. This phenomenon induces a pressure gradient within the nanofluid, which is responsible for spreading the nanofluid over the solid surface, detaching the oil.
The three mechanisms mentioned above highly depend on the interaction between the NPs and porous media [32, 34]. It has been reported that the interaction between these two systems is affected by some parameters such as, shape and size of nanoparticles, nanoparticle concentration, particle charge, polydispersity and colloidal stability [15, 32, 33, 34]. There are several studies reporting the influence of size and concentration of SNPs, colloidal stability of SNPs, types of silica nanoparticles and temperature on oil recovery [30, 31, 32]. For example, Onyekonwu et al. used three different polysilicon nanoparticles (lipohydrophilic, hydrolipophobic and medium-wet nanoparticles) to evaluate their impact on oil recovery . They concluded that these three types of nanoparticles are suitable oil recovery agents. Similarly, Ju et al. conducted a study using untreated polysilicon nanoparticle, lipophobic and hydrophilic polysilicon nanoparticle to evaluate the wettability alteration due to the adsorption of NPs on porous walls of sandstone . Their results revealed that the nanoparticles were able to improve the relative permeability of water in porous media, thus, enhancing oil recovery. The effect of the size of SNPs on oil recovery was reported by Hendraningrat et al. . The results indicated that oil recovery is inversely proportional to SNP size. On the other hand, Miranda et al. reported that high temperature and salinity affected the diffusion coefficient of SNPs and the interfacial tension between the SNPs and the bulk .
Other groups have studied the effect of concentration and colloidal stability of SNPs [11, 25]. These studies confirmed that these parameters are critical for an effective oil recovery. Despite all these reported results, to our knowledge, no study has been undertaken experimentally to investigate the effect of surface charge of SNPs on oil recovery. We hypothesize that the surface charge of SNPs could impact oil recovery, since this parameter could significantly alter the wettability of the reservoir rocks. To prove this hypothesis, SNPs with different charge profiles: negative (Neg-SNPs; − 33.45 ± 2.75), positive (AP-SNPs; + 42.25 ± 1.90) and slightly negative (MeO-PEG-SNPs; − 12.20 ± 0.42) were synthesized and characterized using transmission electron microscopy (TEM), FT-IR, dynamic light scattering (DLS) and ζ-potential. In addition, the effect of the surface charge of SNPs on wettability alteration and oil recovery was evaluated by contact angle estimation and spontaneous imbibition experiments. The results demonstrated that SNPs with different surface charge profiles were able to influence the rock wettability and increased the oil recovery. At a concentration of 100 mg/L, MeO-PEG-SNPs had the best performance in changing the rock wettability from an oil wet to a water wet state as determined by contact angle estimation. These results are in agreement with imbibition experiments which demonstrated that these NPs showed the higher oil displacement. However, at a higher concentration (200 mg/L), the effectiveness of Neg-SNPs and AP-SNPs increased as demonstrated by contact angle and imbibition experiments, with Neg-SNPs showing the best performance. These results offer an understanding of the influence of surface charge on oil recovery, which may provide valuable information to maximize oil recovery using nanofluids.
Tetraethyl orthosilicate (TEOS 98%), ammonium hydroxide solution (31.5%), methoxy polyethylene glycol (MeO-PEG, 2K), 3-aminopropyl (AP) triethoxysilane (APTES), 3-(triethoxysilyl)propyl isocyanate and absolute ethanol (95%) were obtained from Sigma-Aldrich (St Louis, MO, USA). Crude oil was obtained from Texas Raw Crude (Midland, TX, USA). Berea sandstone core plugs were purchased from Berea Sandstone Petroleum Cores (Vermilion, OH, USA). All the reagents and solvents were used as received without further purification.
Synthesis and characterization of silica nanoparticles with different charge profiles
For the synthesis of silica nanoparticles with different charge profiles, a multistep procedure was carried out by following the Stöber process using TEOS as a silica source and aqueous ammonium hydroxide as a catalyst . First, 50 mL of a solution containing ammonium hydroxide (12 mmol), and deionized water (60 mmol) in ethanol was stirred for 5 min. Then, 10 mL of a mixture of TEOS (24 mmol) and ethanol was added to the previous solution and stirred overnight at room temperature. Afterward, SNPs were recovered by centrifugation at high speed, washed twice with ethanol, resuspended in ethanol and stored in the same solvent. The silanol groups present on the surface of the SNPs after this synthetic pathway provided negatively charged nanoparticles (Neg-SNPs; − 33.45 ± 2.75). The second step was the functionalization of the Neg-SNPs with various functional groups to render slightly negative and positive surface charges. Methoxy polyethylene glycol (MeO-PEG2K) was used to modify the surface of the Neg-SNPs to a slightly negatively charged surface (MeO-PEG-SNPs; − 12.20 ± 0.42). MeO-PEG2K has a near neutral ζ-potential and has the ability to neutralize the negative charged surface provided by silanol groups. This functionalization step involved the modification of one end of the MeO-PEG2K chain to obtain a MeO-PEG2K silane derivative for binding on the surface of silica nanoparticles. To synthesize the MeO-PEG2K-silane, 302.2 mg (0.15 mmol) of dehydrated MeO-PEG2K were dissolved in 10 mL of dichloromethane. Then, 40.4 μL of 3-(triethoxysilyl)propyl isocyanate was added and the final solution was stirred overnight at 0 °C. After this period of time, the final product was concentrated by rotary evaporation, dried in a vacuum and characterized using 1H-NMR and 13C-NMR. Next, 100 mg of Neg-SNPs were redispersed in 30 ml of ethanol followed by the addition of 160 mg of the MeO-PEG2K-silane derivative. The final solution was refluxed overnight at 90 °C. MeO-PEG-SNPs were washed three times with ethanol and stored in the same solvent.
The positively charged nanoparticles (AP-SNPs; + 42.25 ± 1.9) were obtained grafting (3-aminopropyl) triethoxysilane (APTES) onto the surface of Neg-SNPs by ethanolic refluxing. To this, 100 mg of Neg-SNPs were redispersed in 30 mL of ethanol. Then, 0.6 mmol of APTES was added to the nanoparticle solution and stirred overnight at 90 °C under refluxing conditions. AP-SNPs were washed three times with ethanol, resuspended in ethanol and stored in the same solvent.
The particle size and morphology of the negatively, slightly negatively and positively charged nanoparticles were determined using a JEOL JEM 2100 LaB6 Transmission Electron Microscope (TEM). The hydrodynamic diameter and the ζ-potential of the nanoparticles in water were determined using a particle-size analyzer (Zetasizer Nano; Malvern Instruments, Malvern, UK). FT-IR analysis were performed to further confirm the successful surface modification of the silica materials (Perkin-Elmer 100 IR spectrophotometer).
Contact angle estimation
Berea sandstone core plugs were cut into small pieces and aged in crude oil for 7 days at 55 °C to alter the wetting tendency of their surface to an oily-wet . After this period of time, sandstone cores were removed from the crude oil and placed in an oven until dried. The aged sandstone core pieces were immersed into an aqueous solution of 0.3% NaCl containing different concentrations of silica materials (100 or 200 mg/L) for 24 h. Afterward, the samples were removed and placed in an oven until dried. Then, a droplet of water was added onto the surface of silica materials-treated sandstone and the angle between the solid surface and the tangent to the drop profile at the drop edge (contact angle) was measured by visual estimation . As a control, contact angle estimation in untreated aged sandstone was also performed.
For spontaneous imbibition experiments, Berea sandstone core plugs were cut into adequate pieces and aged in crude oil to alter the wetting tendency of their surface to an oily-wet as established previously . After this process, the mass of oil adsorbed by the sandstone core was determined by the difference between the mass of the dry core and the mass of the oil-treated core (Moil = Moil treated core − Mdry core). The volume of the oil present in the sandstone cores was calculated using the density of the crude oil (0.7 g/mL). Then, the aged sandstone core pieces were immersed into a glass jar containing a 0.3% NaCl aqueous solution and different concentrations of silica materials (100 or 200 mg/L). The oil that was expelled from the Berea sandstone as the nanoparticle solution imbibed was removed from the top of the glass jar using a glass pipette. The samples were centrifuged at high speed to remove the test solution and the amount of oil displaced by the solution of silica materials (expressed as a percentage of the original amount of oil in the sandstone cores) was estimated as a function of time. The imbibition studies were performed also in untreated cores.
Results and discussion
Characterization of silica nanoparticles with different charge profiles
The surface charge of nanoparticles may play an important role in oil recovery. To evaluate the effect of the surface charge of SNPs on oil recovery, SNPs with different charges (negative, positive and slightly negative) were prepared following a multistep procedure. First, the Stöber process was used to synthesize SNPs using TEOS as the silica source and ammonium hydroxide as a catalyst. The final material obtained from this synthetic pathway exhibited a negative surface charge due to the silanol groups present on its surface (Neg-SNPs). Next, the slightly negatively and positively charged nanoparticles were obtained by modifying the surface of Neg-SNPs with MeO-PEG2K silane and APTES, respectively. Before grafting the MeO-PEG2K silane onto the surface of Neg-SNPs, its successful synthesis in situ was confirmed by NMR (supplementary material, Fig. S1): 1H-NMR (300 MHz): δ (t, 2H, 0.63), (t, 9H, 1.20), (m, 2H, 1.68), (t, 2H, 3.37), (s, 3H, 3.49), (m, 164H, 3.50–3.65), (q, 6H, 3.76); 13C-NMR (300 MHz): δ 7.76 (CH2), 18.26 (CH3), 25.14 (CH2), 45.45 (CH2), 58.46 (O–CH2), 61.67 (O–CH3), 70.4–72.6 (O–CH2 PEG), 156.48 (C=O).
Structural properties of the synthesized nanoparticles
Hydrodynamic diameter (nm)
78.8 ± 19.0
− 33.45 ± 2.75
114.0 ± 16.6
+ 42.25 ± 1.90
254.6 ± 181.0
− 12.20 ± 0.42
Effect of silica nanoparticles with different charge profiles on the wettability of Berea sandstone cores and oil displacement
Wettability alteration of rock reservoirs plays an important role in oil recovery and it is used to determine the efficacy of nanomaterials during the oil recovery process . To investigate the effect of the surface charge of SNPs on oil recovery, two techniques were performed: contact angle estimation and spontaneous imbibition experiments.
For contact angle estimation, the sandstone cores were submerged in crude oil for 7 days to change the wettability of the rock to an oil-wet. Then, the crude oil-treated sandstone cores were exposed to variant concentrations of nanoparticles for 24 h and the contact angle was determined by visual estimation after adding a droplet of water on the surface of the treated sandstone cores.
Our work demonstrated that silica nanoparticles with different surface charges were capable of altering the wettability of sandstone cores as determined by contact angle estimation. Additionally, these materials impacted the oil recovery process in different extents. While MeO-PEG-SNPs (slightly negatively charged nanoparticles) showed the highest oil recovery at a low concentration (100 mg/L), at a higher concentration (200 mg/L), Neg-SNPs demonstrated to be the most effective in recovering oil from sandstone cores. Moreover, the concentration plays an important role in evaluating the impact of the surface charge on oil recovery. As the concentration increased, Neg-SNPs and AP-SNPs improved the wettability and the oil recovery process. On the other hand, the effectiveness of MeO-PEG-SNPs decreased as the concentration increased. Overall, the results obtained from this study could not only give a deeper insight of the interaction between nanofluids and porous media, but could also provide additional information about the optimal structural characteristics that SNPs should meet to maximize oil recovery.
We thank the Inter American University of Puerto Rico (Seed Grant funding) for supporting this research work.
Compliance with ethical standards
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
- 13.Ju, B., Dai, S., Luan, Z., Zhu, T., Su, X., Qiu, X.: A study of wettability and permeability change caused by adsorption of nanometer structured polysilicon on the surface of porous media. In: Paper presented at the SPE Asia Pacific Oil and Gas Conference and Exhibition, Melbourne, Australia, 2002/1/1 (2002)Google Scholar
- 17.Levitt, D., Pope, G.A.: Selection and screening of polymers for enhanced-oil recovery. In: Paper presented at the SPE Symposium on Improved Oil Recovery, Tulsa, Oklahoma, USA, 20–23 April (2008)Google Scholar
- 18.Miranda, C.R., Lara, L.S.D., Tonetto, B.C.: Stability and mobility of functionalized silica nanoparticles for enhanced oil recovery applications. In: Paper presented at the SPE International Oilfield Nanotechnology Conference and Exhibition, Noordwijk, The Netherlands, 12–14 June (2012)Google Scholar
- 20.Onyekonwu, M.O., Ogolo, N.A.: Investigating the use of nanoparticles in enhancing oil recovery. In: Paper presented at the Nigeria Annual International Conference and Exhibition, Tinapa—Calabar, Nigeria, 31 July–7 August (2010)Google Scholar
- 21.Ponnapati, R., Karazincir, O., Dao, E., Ng, R., Mohanty, K.K., Krishnamoorti, R.: Polymer-functionalized nanoparticles for improving waterflood sweep efficiency: characterization and transport properties. Ind. Eng. Chem. Res. 50, 13030–13036 (2011). https://doi.org/10.1021/ie2019257 CrossRefGoogle Scholar
- 26.Shahrabadi, A., Bagherzadeh, H., Roostaie, A., Golghanddashti, H.: Experimental investigation of HLP nanofluid potential to enhance oil recovery: a mechanistic approach. In: Paper presented at the SPE International Oilfield Nanotechnology Conference and Exhibition, 12–14 June, Noordwijk, Netherlands, June 12 − 14 (2012)Google Scholar
- 28.Singh, S.K., Kulkarni, P.P., Dash, D.: Biomedical applications of nanomaterials: an overview. In: Bio-nanotechnology. Blackwell Publishing Ltd., pp. 1–32. (2013). https://doi.org/10.1002/9781118451915.ch1
- 29.Tabary, R., Bazin, B., Douarche, F., Moreau, P., Oukhemanou-Destremaut, F.: Surfactant flooding in challenging conditions: towards hard brines and high temperatures. In: Paper presented at the SPE Middle East Oil and Gas Show and Conference, Manama, Bahrain, 10–13 March (2010)Google Scholar
- 30.Torsaeter, O., Li, S., Hendraningrat, L.: Enhancing oil recovery of low-permeability berea sandstone through optimised nanofluids concentration. In: Paper presented at the SPE Enhanced Oil Recovery Conference, Kuala Lumpur, Malaysia, 2013/7/2 (2013)Google Scholar
- 31.Torsater, O., Li, S., Hendraningrat, L.: A coreflood investigation of nanofluid enhanced oil recovery in low-medium permeability berea sandstone. In: Paper presented at the SPE International Symposium on Oilfield Chemistry, The Woodlands, Texas, USA, 2013/4/8 (2013a)Google Scholar
- 32.Torsater, O., Li, S., Hendraningrat, L.: Effect of some parameters influencing enhanced oil recovery process using silica nanoparticles: an experimental investigation. In: Paper presented at the SPE Reservoir Characterization and Simulation Conference and Exhibition, Abu Dhabi, UAE, 16–18 September (2013b)Google Scholar
- 33.Wasan, D.T., Nikolov, A.D.: Spreading of nanofluids on solids. Nature 423, 156–159 (2003). http://www.nature.com/nature/journal/v423/n6936/suppinfo/nature01591_S1.html
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.