Development of functionalized carrageenan, chitosan and alginate as polymeric chelating ligands for water softening

  • K. A. AliEmail author
  • M. E. Hassan
  • M. M. M. Elnashar
Original Paper

Abstract

Chitosan, carrageenan and alginate are among the most abundant biopolymers in nature. They were prepared in uniform beads shape with a diameter of 2 mm ± 10%, using the encapsulator for removal of calcium, magnesium and iron cations from hard water. Solutions of 100–500 mg/L were prepared from each cation, and the detection of cations was carried out using atomic absorption spectrometer. Carrageenan and chitosan were able to chelate the three cations without further modification. However, alginate beads succeeded to chelate iron and magnesium and failed to chelate any calcium ions; in contrast, it increased the initial calcium concentration! That could be due to the pre-cross-linking of alginate beads using calcium chloride solution, which may be leaked back to the solution. However, grafting the alginate beads with polyethyleneimine and bromoacetic acid rectified this problem and the new functional group, –COOH, has been proved using the FT-IR. Optimization of the results in terms of beads weight (0.25–3.0 g) and cations concentrations (100–500 mg/L) has shown that most biopolymeric beads can chelate 85–100% of the cations in concentrations up to 500 mg/L. According to our finding, we came up with the recommendation to use chitosan for chelation of calcium and iron as it showed 100% chelation efficiency of both cations, whereas carrageenan is highly recommended for chelation of iron and magnesium, as it showed 100 and 98% chelation efficiency, respectively. Further work can be done on the reusability of the beads and scale up for the industrial use.

Keywords

Biopolymers Metal ions Chelation Water purification Grafting 

Notes

Acknowledgements

This work was supported by the National Research Centre-Egypt under the 10th project Grant (Project No. 10080101).

Supplementary material

13762_2017_1298_MOESM1_ESM.pdf (476 kb)
Supplementary material 1 (PDF 476 kb)

References

  1. Ali KA, Haroun AA, Abd El-Moez SI (2013) Synthesis and antimicrobial activity of gelatin-thiazolidine derivative based nanohybrids. In: CIMDD conference at Algeria: May 6th to 9th, 2013. UniversitéM’HamedBougaraBoumerdesGoogle Scholar
  2. Chaturvedi S, Dave PN (2012) Removal of iron for safe drinking water. Desalination 313:1–11CrossRefGoogle Scholar
  3. Deans JR, Dixon BG (1992) Uptake of Pb2+ and Cu2+ by novel biopolymers. Water Res 26:469–472CrossRefGoogle Scholar
  4. Elnashar MM (2010) Immobilized molecules using biomaterials and nanobiotechnology. J Biomater Nanobiotechnol 1:61–76CrossRefGoogle Scholar
  5. Elnashar MM (2011) The art of immobilization using biopolymers, biomaterials and nanobiotechnology, biotechnology of biopolymers, Chap 1, pp 1–32. ISBN:978-953-307-179-4Google Scholar
  6. Elnashar MM, Hassan ME (2014) Novel epoxy activated hydrogels for solving lactose intolerance. Biomed Res Int 2014:817985Google Scholar
  7. Elnashar MM, Danial EN, Awad EA (2009) Novel carrier of grafted alginate for covalent immobilization of inulinase. Ind Eng Chem Res 48:9781–9785CrossRefGoogle Scholar
  8. El-Sayed MH, Hani HA, Sorour MH (2014) Polymeric ion exchangers for the recovery of ions from brine and seawater. Chem Eng Process Tech 2:1020Google Scholar
  9. Jang LK, Lopez SL, Eastman SL, Prygogle P (1991) Recovery of copper and cobalt by biopolymer gels. Biotechnol Bioeng 37:266–273CrossRefGoogle Scholar
  10. Muraviev D, Noguerol J, Valiente M (1996) Separation and concentration of calcium and magnesium from sea water by carboxylic resins with temperature induced selectivity. React Funct Polym 28:111–126CrossRefGoogle Scholar
  11. Nah CJ, Hwang K (2007) Adsorption of heavy metals using magnetically modified alginic acid. Hydrometallurgy 86:140–146CrossRefGoogle Scholar
  12. Nazarudin MF, Shamsuri AA, Shamsudin MN (2011) Preparation and physicochemical evaluation of biodegradable magnetic κ-carrageenan beads and application for chromium ions pre-concentration. J Chil Chem Soc 56:891–894CrossRefGoogle Scholar
  13. Ohya H, Suzuki T, Nakao S (2001) Integrated system for complete usage of components in seawater. Desalination 134:29–36CrossRefGoogle Scholar
  14. Seki H, Suzuki A (1995) Adsorption of heavymetal ions on insolubilized humic acid. J Colloid Interface Sci 171:490–494CrossRefGoogle Scholar
  15. Zhao L, Shi L, Zhang Z, Chen J, Shi D, Yang J, Tang Z (2011) Preparation and application of chitosan nanoparticles and nanofibers. Braz J Chem Eng 28:353–362CrossRefGoogle Scholar

Copyright information

© Islamic Azad University (IAU) 2017

Authors and Affiliations

  • K. A. Ali
    • 1
    • 2
    Email author
  • M. E. Hassan
    • 1
    • 3
  • M. M. M. Elnashar
    • 1
    • 4
  1. 1.Center of Excellence, Advanced Materials and Nanobiotechnology GroupNational Research CentreDokki, GizaEgypt
  2. 2.Applied Organic Chemistry DepartmentNational Research CentreDokki, GizaEgypt
  3. 3.Chemistry of Natural and Microbial Products DepartmentNational Research CentreDokki, GizaEgypt
  4. 4.Biomedical Sciences Department, Health Sciences SchoolCurtin UniversityPerthAustralia

Personalised recommendations