, Volume 27, Issue 9, pp 701–708 | Cite as

A disentangled state using TiCl4/MgCl2 catalyst: a case study of polyethylene

  • Amin Heidari
  • Hamid Zarghami
  • Saeid Talebi
  • Mostafa Rezaei
Original Research
  • 34 Downloads

Abstract

Fully entangled morphology which is usually expected for polyethylene produced using Ziegler–Natta (ZN) catalyst is due to the presence of active sites crowded on catalyst’s support surface as well as within its volume. In this research, the feasibility of producing disentangled, more precisely less entangled, polyethylene using a heterogeneous ZN catalyst supported on magnesium chloride, TiCl4/MgCl2, is introduced. Polymerization was carried out at rather low temperature and pressure, and the nascent polymer was characterized to investigate its entanglement state. The rheological measurements, at small amplitude oscillating in the time sweep mode, exhibited a rather good modulus build-up, demonstrating the nascent polymer in its dis(less)-entangled state. Tape and film samples were prepared from the synthesized polyethylene below its melting point to keep the morphology untapped. The solid-state drawability test was performed on the samples at 100 °C showing its improved drawability. Thus, it could be concluded that the polyethylene synthesized at rather low temperature of 0 °C and longer polymerization time was in disentangled state. Furthermore, a rheometrical analysis in frequency mode was used to estimate the molecular weight and molecular weight distribution of the synthesized polyethylene qualitatively. From X-ray diffraction patterns the existence of a small amount of hexagonal phase in the nascent polymer could be detected, which may be due to the formation of extended chains during polymerization.

Keywords

UHMWPE Disentangled state Solid-state drawability Ziegler–Natta catalyst Mechanical properties 

Supplementary material

13726_2018_648_MOESM1_ESM.docx (551 kb)
Supplementary material 1 (DOCX 551 KB)

References

  1. 1.
    Gupta S, Riyad MF (2016) Synthesis and tribological behavior of novel UHMWPE-Ti3SiC2 composites. Polym Compos 39:254–262CrossRefGoogle Scholar
  2. 2.
    Vadivel HS, Golchin A, Emami N (2018) Tribological behaviour of carbon filled hybrid UHMWPE composites in water. Tribol Int 124:169–177CrossRefGoogle Scholar
  3. 3.
    Wang Q, Wang H, Wang Y, Yan F (2016) Modification effects of short carbon fibers on mechanical properties and fretting wear behavior of UHMWPE composites. Surf Interface Anal 48:139–145CrossRefGoogle Scholar
  4. 4.
    Ravanbakhsh S, Rezaei M, Sheikh N, Heidari A (2010) Irradiation grafting of methyl methacrylate monomer onto ultra-high-molecular-weight polyethylene: an experimental design approach for improving adhesion to bone cement. J Appl Polym Sci 116:886–894Google Scholar
  5. 5.
    SM Kurtz (2009) Ultra high molecular weight polyethylene in total joint replacement and medical devices, in: UHMWPE biomaterials handbook.8:98. Academic Press, USAGoogle Scholar
  6. 6.
    Rastogi S, Lippits DR, Peters GWM, Graf R, Yao Y, Spiess HW (2005) Heterogeneity in polymer melts from melting of polymer crystals. Nat Mater 4:635–641CrossRefPubMedGoogle Scholar
  7. 7.
    Smith P, Lemstra PJ (1980) Ultra-drawing of high molecular weight polyethylene cast from solution. Colloid Polym Sci 258:891–894CrossRefGoogle Scholar
  8. 8.
    Talebi S(2008) Technische Universiteit Eindhoven, Eindhoven, The NetherlandsGoogle Scholar
  9. 9.
    Kurelec L, Rastogi S, Meier RJ, Lemstra PJ (2000) Chain mobility in polymer systems: on the borderline between solid and melt. 3. Phase transformations in nascent ultrahigh molecular weight polyethylene reactor powder at elevated pressure as revealed by in situ Raman spectroscopy. Macromolecules 33:5593–5601CrossRefGoogle Scholar
  10. 10.
    Pandey A, Champouret Y, Rastogi S (2011) Heterogeneity in the distribution of entanglement density during polymerization in disentangled ultrahigh molecular weight polyethylene. Macromolecules 44:4952–4960CrossRefGoogle Scholar
  11. 11.
    Rastogi S, Yao Y, Lippits DR, Hhne GWH, Graf R, Spiess HW, Lemstra PJ (2009) Segmental mobility in the non-crystalline regions of semicrystalline polymers and its implications on melting. Macromol Rapid Commun 30:826–839CrossRefPubMedGoogle Scholar
  12. 12.
    Romano D, Ronca S, Rastogi S (2015) A hemi-metallocene chromium catalyst with trimethylaluminum-free methylaluminoxane for the synthesis of disentangled ultra-high molecular weight polyethylene. Macromol Rapid Commun 36:327–331CrossRefPubMedGoogle Scholar
  13. 13.
    Talebi S, Duchateau R, Rastogi S, Kaschta J, Peters GWM, Lemstra PJ (2010) Molar mass and molecular weight distribution determination of UHMWPE synthesized using a living homogeneous catalyst. Macromolecules 43:2780–2788CrossRefGoogle Scholar
  14. 14.
    Lippits DR, Rastogi S, Talebi S, Bailly C (2006) Formation of entanglements in initially disentangled polymer melts. Macromolecules 39:8882–8885CrossRefGoogle Scholar
  15. 15.
    Ronca S, Forte G, Tjaden H, Yao Y, Rastogi S (2012) Tailoring molecular structure via nanoparticles for solvent-free processing of ultra-high molecular weight polyethylene composites. Polymer 53:2897–2907CrossRefGoogle Scholar
  16. 16.
    Kaminsky W, Funck A, Klinke C (2008) In-situ polymerization of olefins on nanoparticles or fibers by metallocene catalysts. Top Catal 48:84CrossRefGoogle Scholar
  17. 17.
    .Heidari A, Talebi S, Rezaei M, Keshavarz-Mirzamohamadi H, Jafariyeh-Yazdi E (2018) In situ synthesis of ultrahigh molecular weight polyethylene/graphene oxide nanocomposite using the immobilized single-site catalyst. Polym Plast Technol Eng 17:1313–1324CrossRefGoogle Scholar
  18. 18.
    Li W, Yang H, Zhang J, Mu J, Gong D, Wang X (2016) Immobilization of isolated FI catalyst on polyhedral oligomeric silsesquioxane-functionalized silica for the synthesis of weakly entangled polyethylene. Chem Commun 52:11092–11095CrossRefGoogle Scholar
  19. 19.
    Entezami A, Najafi Moghadam P (2005) Supported zirconocene catalyst for preventing reactor fouling in ethylene polymerization. Polym Int 54:1326–1329CrossRefGoogle Scholar
  20. 20.
    Alexandre M, Martin E, Dubois P, Marti MG, Jerome R (2000) Use of metallocenes in the polymerization-filling technique with production of polyolefin-based composites. Macromol Rapid Commun 21:931–936CrossRefGoogle Scholar
  21. 21.
    Redzic E, Garoff T, Mardare CC, List M, Hesser G, Mayrhofer L, Hassel AW, Paulik C (2016) Heterogeneous Ziegler–Natta catalysts with various sizes of MgCl2 crystallites: synthesis and characterization. Iran Polym J 25:321–337CrossRefGoogle Scholar
  22. 22.
    Kissin YV, Mink R, Nowlin T (1999) Ethylene polymerization reactions with Ziegler–Natta catalysts. I. Ethylene polymerization kinetics and kinetic mechanism. J Polym Sci A Polym Chem 37:4255–4272CrossRefGoogle Scholar
  23. 23.
    Kissin YV, Mirabella FM, Meverden CC (2005) Multi-center nature of heterogeneous Ziegler–Natta catalysts: TREF confirmation. J Polym Sci A Polym Chem 43:4351–4362CrossRefGoogle Scholar
  24. 24.
    Ferry JD (1980) Viscoelastic properties of polymers 10:243. Wiley, USAGoogle Scholar
  25. 25.
    Dealy JM, Larson RG (2006) Structure and rheology of molten polymers, 5. Hanser, Munich, p 152CrossRefGoogle Scholar
  26. 26.
    Li W, Guan C, Xu J, Mu J, Gong D, Chen Z, Zhou Q (2014) Disentangled UHMWPE/POSS nanocomposites prepared by ethylene in situ polymerization. Polymer 55:1792–1798CrossRefGoogle Scholar
  27. 27.
    Suzuki Y, Terao H, Fujita T (2003) Recent advances in phenoxy-based catalysts for olefin polymerization. Bull Chem Soc Jpn 76:1493–1517CrossRefGoogle Scholar
  28. 28.
    Furuyama R, Saito J, Ishii S, Makio H, Mitani M, Tanaka H, Fujita T (2005) Fluorinated bis (phenoxy-imine) Ti complexes with MAO: remarkable catalysts for living ethylene and syndioselective living propylene polymerization. J Organomet Chem 690:4398–4413CrossRefGoogle Scholar
  29. 29.
    Shirkavand MJ, Azizi H, Ghasemi I, Karrabi M, Rashedi R (2015) A correlation between microstructure and rheological properties of broad MWD high-density polyethylene. Iran Polym J 24:953–963CrossRefGoogle Scholar
  30. 30.
    Men Y, Rieger J, Endeler HF, Lilge D (2003) Mechanical α-process in polyethylene. Macromolecules 36:4689–4691CrossRefGoogle Scholar
  31. 31.
    Ward IM, Hadley DW (1993) An introduction to the mechanical properties of solid polymers.10:280. Wiley, USAGoogle Scholar
  32. 32.
    Hu WG, Schmidt-Rohr K (1999) Polymer ultradrawability: the crucial role of α-relaxation chain mobility in the crystallites. Acta Polym 50:271–285CrossRefGoogle Scholar
  33. 33.
    Ronca S, Romano D, Forte G, Andabloâ Reyes E, Rastogi S (2012) Improving the performance of a catalytic system for the synthesis of ultra high molecular weight polyethylene with a reduced number of entanglements. Adv Polym Tech 31:193–204CrossRefGoogle Scholar
  34. 34.
    Capaccio G, Ward I (1974) Preparation of ultra-high modulus linear polyethylenes; effect of molecular weight and molecular weight distribution on drawing behaviour and mechanical properties. Polymer 15:233–238CrossRefGoogle Scholar
  35. 35.
    Yamamoto T, Miyaji H, Asai K (1977) Structure and properties of high pressure phase of polyethylene. Jpn J Appl Phys 16:1891CrossRefGoogle Scholar
  36. 36.
    Kakiage M, Yamanobe T, Komoto T, Murakami S, Uehara H (2006) Transient crystallization during drawing from ultra-high molecular weight polyethylene melts having different entanglement characteristics. Polymer 47:8053–8060CrossRefGoogle Scholar
  37. 37.
    Uehara H, Kanamoto T, Kawaguchi A, Murakami S (1996) Real-time X-ray diffraction study on two-stage drawing of ultra-high molecular weight polyethylene reactor powder above the static melting temperature. Macromolecules 29:1540–1547CrossRefGoogle Scholar
  38. 38.
    Hosseinnezhad R, Talebi S, Rezaei M (2016) The unique effect of chain entanglements and particle morphology on the sintering of ultrahigh molecular weight polyethylene. J Elastomers Plast 49:609–629CrossRefGoogle Scholar
  39. 39.
    Pereira RA, Dias ML, Mano EB (2000) Orthorhombic-hexagonal phase transition in high density polyethylene crystals. Intern J Polym Mater 45:69–78CrossRefGoogle Scholar
  40. 40.
    Rastogi S, Odell JA (1993) Stress stabilization of the orthorhombic and hexagonal phases of UHM PE gel-spun fibres. Polymer 34:1523–1527CrossRefGoogle Scholar
  41. 41.
    Gedde ULF (2013) Polymer physics. Springer, GermanyGoogle Scholar
  42. 42.
    Zachariades AE, Kanamoto T (1986) The effect of initial morphology on the mechanical properties of ultra-high molecular weight polyethylene. Polym Eng Sci 26:658–661CrossRefGoogle Scholar
  43. 43.
    Ivan’kova EM, Myasnikova LP, Marikhin VA, Baulin AA, Volchek BZ (2001) On the memory effect in UHMWPE nascent powders. J Macromol Sci Ph 40:813–832CrossRefGoogle Scholar

Copyright information

© Iran Polymer and Petrochemical Institute 2018

Authors and Affiliations

  • Amin Heidari
    • 1
  • Hamid Zarghami
    • 1
  • Saeid Talebi
    • 1
  • Mostafa Rezaei
    • 1
  1. 1.Polymer Engineering Department, Institute of Polymeric MaterialsSahand University of TechnologyTabrizIran

Personalised recommendations