Graphene oxide selenium nanorod composite as a stable electrode material for energy storage devices

  • Aftab AhmadEmail author
  • Sadeeq Ullah
  • Abrar Khan
  • Waqas Ahmad
  • Arif Ullah Khan
  • Usman Ali Khan
  • Aziz Ur Rahman
  • Qipeng YuanEmail author
Original Article
  • 47 Downloads

Abstract

Selenium (Se), a member of the sulfur family, is considered as a potential alternative cathode material due to its high electronic conductivity and comparable volumetric capacity density to sulfur. Herein, we report on a simple one-step procedure to prepare trigonal selenium nanorods (t-Se) on graphene oxide (GO) without using any surfactant. The developed method does not utilize any harmful chemicals or harsh experimental conditions, and is, therefore, friendly from the environmental and economic point of views. We discovered that well-dispersed Se nanorods can be prepared at 20 mM Se under heating at 85 °C for 3 h. The successful growth of t-Se rods on GO sheets was confirmed by X-ray diffraction (crystalline structure), transmission electron microscopy (morphology), Raman spectroscopy (crystalline form and defects), and XPS technique (elemental composition). The Se nanorod-loaded GO composite (GO–Se) displayed a promising specific capacity of 405.5 mAh g−1 at a high current density (10 A g−1) and high cycling stability with a negligible capacity decay over 1000 cycles. Importantly, the GO–Se electrode delivered a high reversible capacity of 471.5 mAh g−1 at 0.5 A g−1. The improved electrical performance of the GO–Se composite could be attributed to the electrical conductivity and unique architecture of reduced graphene, which effectively enhances the utilization of active Se rods and significantly augment the electronic conductivity of the GO–Se electrode. The present study demonstrates that a hybrid system of 1D t-Se impregnated GO composite could be a promising cathode material for long-life batteries and other storage devices.

Keywords

Graphene oxide Selenium rods Cathode material Electrochemical properties 

Notes

Acknowledgement

We sincerely acknowledge the financial support from the Fundamental Research Funds for the Central Universities (ylkxj03), the Program of Introducing Talents of Discipline to Universities (“111” Project, B13005), and National Natural Science Foundation of China (21636001, 21776008, 21606012).

Compliance with ethical standards

Conflict of interest

The authors declare no conflict of interest.

References

  1. Abouimrane A, Dambournet D, Chapman KW, Chupas PJ, Weng W, Amine K (2012) A new class of lithium and sodium rechargeable batteries based on selenium and selenium–sulfur as a positive electrode. J Am Chem Soc 134:4505–4508CrossRefGoogle Scholar
  2. Ahmad A, Syed F, Shah A, Khan Z, Tahir K, Khan AU et al (2015) Silver and gold nanoparticles from Sargentodoxa cuneata: synthesis, characterization and antileishmanial activity. RSC Adv 5:73793–73806CrossRefGoogle Scholar
  3. Bernabò N, Machado-Simoes J, Valbonetti L, Ramal-Sanchez M, Capacchietti G, Fontana A et al (2019) Graphene oxide increases mammalian spermatozoa fertilizing ability by extracting cholesterol from their membranes and promoting capacitation. Sci Rep 9:8155CrossRefGoogle Scholar
  4. Bhunia SK, Jana NR (2014) Reduced graphene oxide-silver nanoparticle composite as visible light photocatalyst for degradation of colorless endocrine disruptors. ACS Appl Mater Interfaces 6:20085–20092CrossRefGoogle Scholar
  5. Cai FS, Zhang GY, Chen J, Gou XL, Liu HK, Dou SX (2004) Ni (OH) 2 tubes with mesoscale dimensions as positive-electrode materials of alkaline rechargeable batteries. Angew Chem Int Ed 43:4212–4216CrossRefGoogle Scholar
  6. Cai Q, Li Y, Li Q, Xu J, Gao B, Zhang X et al (2017) Freestanding hollow double-shell Se@ CNx nanobelts as large-capacity and high-rate cathodes for Li–Se batteries. Nano Energy 32:1–9CrossRefGoogle Scholar
  7. Chen Z, Shen Y, Xie A, Zhu J, Wu Z, Huang F (2009) L-Cysteine-assisted controlled synthesis of selenium nanospheres and nanorods. Cryst Growth Des 9:1327–1333CrossRefGoogle Scholar
  8. Chen X, Wu G, Chen J, Chen X, Xie Z, Wang X (2011) Synthesis of “clean” and well-dispersive Pd nanoparticles with excellent electrocatalytic property on graphene oxide. J Am Chem Soc 133:3693–3695CrossRefGoogle Scholar
  9. Ding J, Zhou H, Zhang H, Stephenson T, Li Z, Karpuzov D et al (2017) Exceptional energy and new insight with a sodium–selenium battery based on a carbon nanosheet cathode and a pseudographite anode. Energy Environ Sci 10:153–165CrossRefGoogle Scholar
  10. Du H, Jiao L, Wang Q, Huan Q, Peng W, Song D et al (2011) Selenium: another metalloid beneficial for the electrochemical performance of Co electrode in alkaline rechargeable batteries. J Power Sources 196:10748–10752CrossRefGoogle Scholar
  11. Eftekhari A (2017) The rise of lithium–selenium batteries. Sustain Energy Fuels 1:14–29CrossRefGoogle Scholar
  12. Ferrari AC (2007) Raman spectroscopy of graphene and graphite: disorder, electron–phonon coupling, doping and nonadiabatic effects. Solid State Commun 143:47–57CrossRefGoogle Scholar
  13. Filippo E, Manno D, Serra A (2010) Characterization and growth mechanism of selenium microtubes synthesized by a vapor phase deposition route. Cryst Growth Des 10:4890–4897CrossRefGoogle Scholar
  14. Fu G, Chang K, Shangguan E, Tang H, Li B, Chang Z et al (2015) Synthesis of CoO/reduced graphene oxide composite as an alternative additive for the nickel electrode in alkaline secondary batteries. Electrochim Acta 180:373–381CrossRefGoogle Scholar
  15. Gao X-P, Yang H-X (2010) Multi-electron reaction materials for high energy density batteries. Energy Environ Sci 3:174–189CrossRefGoogle Scholar
  16. Gates B, Mayers B, Cattle B, Xia Y (2002a) Synthesis and characterization of uniform nanowires of trigonal selenium. Adv Func Mater 12:219–227CrossRefGoogle Scholar
  17. Gates B, Mayers B, Grossman A, Xia Y (2002b) A sonochemical approach to the synthesis of crystalline selenium nanowires in solutions and on solid supports. Adv Mater 14:1749–1752CrossRefGoogle Scholar
  18. Govindhan M, Chen A (2015) Simultaneous synthesis of gold nanoparticle/graphene nanocomposite for enhanced oxygen reduction reaction. J Power Sources 274:928–936CrossRefGoogle Scholar
  19. Han K, Liu Z, Shen J, Lin Y, Dai F, Ye H (2015) A free-standing and ultralong-life lithium-selenium battery cathode enabled by 3D mesoporous carbon/graphene hierarchical architecture. Adv Func Mater 25:455–463CrossRefGoogle Scholar
  20. He G, Jiao L, Yuan H, Zhang Y, Zhang Y, Wang Y (2007) Effect of synthesis method on the structure and electrochemical behaviour of Co–Si particles. Int J Hydrogen Energy 32:3416–3419CrossRefGoogle Scholar
  21. Hochbaum AI, Chen R, Delgado RD, Liang W, Garnett EC, Najarian M et al (2008) Enhanced thermoelectric performance of rough silicon nanowires. Nature 451:163CrossRefGoogle Scholar
  22. Hong YJ, Kang YC (2017) Selenium-impregnated hollow carbon microspheres as efficient cathode materials for lithium–selenium batteries. Carbon 111:198–206CrossRefGoogle Scholar
  23. Hu K, Teng F, Zheng L, Yu P, Zhang Z, Chen H et al (2017) Binary response Se/ZnO p-n heterojunction UV photodetector with high on/off ratio and fast speed. Laser Photonics Rev 11:1600257CrossRefGoogle Scholar
  24. Huang J-Q, Zhuang T-Z, Zhang Q, Peng H-J, Chen C-M, Wei F (2015) Permselective graphene oxide membrane for highly stable and anti-self-discharge lithium–sulfur batteries. ACS Nano 9:3002–3011CrossRefGoogle Scholar
  25. Huang Y, Wang Z, Jiang Y, Li S, Li Z, Zhang H et al (2018) Hierarchical porous Co0. 85Se@ reduced graphene oxide ultrathin nanosheets with vacancy-enhanced kinetics as superior anodes for sodium-ion batteries. Nano Energy 53:524–535CrossRefGoogle Scholar
  26. Ju S, Facchetti A, Xuan Y, Liu J, Ishikawa F, Ye P et al (2007) Fabrication of fully transparent nanowire transistors for transparent and flexible electronics. Nat Nanotechnol 2:378CrossRefGoogle Scholar
  27. Kavitha M, John H, Gopinath P, Philip R (2013) Synthesis of reduced graphene oxide–ZnO hybrid with enhanced optical limiting properties. J Mater Chem C 1:3669–3676CrossRefGoogle Scholar
  28. Koltypin M, Aurbach D, Nazar L, Ellis B (2007) More on the performance of LiFePO4 electrodes—the effect of synthesis route, solution composition, aging, and temperature. J Power Sources 174:1241–1250CrossRefGoogle Scholar
  29. Li Y, Gao W, Ci L, Wang C, Ajayan PM (2010) Catalytic performance of Pt nanoparticles on reduced graphene oxide for methanol electro-oxidation. Carbon 48:1124–1130CrossRefGoogle Scholar
  30. Li Z, Yuan L, Yi Z, Liu Y, Huang Y (2014) Confined selenium within porous carbon nanospheres as cathode for advanced Li–Se batteries. Nano Energy 9:229–236CrossRefGoogle Scholar
  31. Li J, Guo L, Shangguan E, Yue M, Xu M, Wang D et al (2017) Synthesis of novel spherical Fe3O4@ Ni3S2 composite as improved anode material for rechargeable nickel–iron batteries. Electrochim Acta 240:456–465CrossRefGoogle Scholar
  32. Lin Y, Zhang K, Chen W, Liu Y, Geng Z, Zeng J et al (2010) Dramatically enhanced photoresponse of reduced graphene oxide with linker-free anchored CdSe nanoparticles. ACS Nano 4:3033–3038CrossRefGoogle Scholar
  33. Liu L, Hou Y, Wu X, Xiao S, Chang Z, Yang Y et al (2013) Nanoporous selenium as a cathode material for rechargeable lithium–selenium batteries. Chem Commun 49:11515–11517CrossRefGoogle Scholar
  34. Liu C-H, Chang Y-C, Norris TB, Zhong Z (2014) Graphene photodetectors with ultra-broadband and high responsivity at room temperature. Nat Nanotechnol 9:273–278CrossRefGoogle Scholar
  35. Liu M-H, Liu Y-T, Wang CC (2015) Symmetry-breaking segmented selenium nanorods and nanowires: synthesis via coupling of nanorods. Chem Mater 27:2832–2838CrossRefGoogle Scholar
  36. Luo C, Xu Y, Zhu Y, Liu Y, Zheng S, Liu Y et al (2013) Selenium@ mesoporous carbon composite with superior lithium and sodium storage capacity. ACS Nano 7:8003–8010CrossRefGoogle Scholar
  37. Ma G, Hua F, Sun K, Fenga E, Peng H, Zhang Z et al (2018) Nanostructure selenium compounds as pseudocapacitive electrodes for high-performance asymmetric supercapacitor. R Soc Open Sci 5:171186CrossRefGoogle Scholar
  38. Marlinda A, Huang N, Muhamad M, An’Amt M, Chang B, Yusoff N et al (2012) Highly efficient preparation of ZnO nanorods decorated reduced graphene oxide nanocomposites. Mater Lett 80:9–12CrossRefGoogle Scholar
  39. Mukkabla R, Deshagani S, Meduri P, Deepa M, Ghosal P (2017) Selenium/graphite platelet nanofiber composite for durable Li–Se batteries. ACS Energy Lett 2:1288–1295CrossRefGoogle Scholar
  40. Rong J, Ge M, Fang X, Zhou C (2013) Solution ionic strength engineering as a generic strategy to coat graphene oxide (GO) on various functional particles and its application in high-performance lithium–sulfur (Li–S) batteries. Nano Lett 14:473–479CrossRefGoogle Scholar
  41. Schedin F, Geim A, Morozov S, Hill E, Blake P, Katsnelson M et al (2007) Detection of individual gas molecules adsorbed on graphene. Nat Mater 6:652CrossRefGoogle Scholar
  42. Shangguan E, Wang Q, Wu C, Wu S, Ji M, Li J et al (2018) Novel application of repaired LiFePO4 as a candidate anode material for advanced alkaline rechargeable batteries. ACS Sustain Chem Eng 6:13312–13323CrossRefGoogle Scholar
  43. Shao W, Liu X, Min H, Dong G, Feng Q, Zuo S (2015) Preparation, characterization, and antibacterial activity of silver nanoparticle-decorated graphene oxide nanocomposite. ACS Appl Mater Interfaces 7:6966–6973CrossRefGoogle Scholar
  44. Singh G, Choudhary A, Haranath D, Joshi AG, Singh N, Singh S et al (2012) ZnO decorated luminescent graphene as a potential gas sensor at room temperature. Carbon 50:385–394CrossRefGoogle Scholar
  45. Song Z, Wei Z, Wang B, Luo Z, Xu S, Zhang W et al (2016) Sensitive room-temperature H2S gas sensors employing SnO2 quantum wire/reduced graphene oxide nanocomposites. Chem Mater 28:1205–1212CrossRefGoogle Scholar
  46. Song J, Kang SW, Lee YW, Park Y, Kim J-H, Han SW (2017) Regulating the catalytic function of reduced graphene oxides using capping agents for metal-free catalysis. ACS Appl Mater Interfaces 9:1692–1701CrossRefGoogle Scholar
  47. Sridharan K, Ollakkan MS, Philip R, Park TJ (2013) Non-hydrothermal synthesis and optical limiting properties of one-dimensional Se/C, Te/C and Se–Te/C core–shell nanostructures. Carbon 63:263–273CrossRefGoogle Scholar
  48. Steichen M, Dale P (2011) Synthesis of trigonal selenium nanorods by electrodeposition from an ionic liquid at high temperature. Electrochem Commun 13:865–868CrossRefGoogle Scholar
  49. Tang K, Yu D, Wang F, Wang Z (2006) Controlled growth of hexagonal trigonal selenium microtubes. Cryst Growth Des 6:2159–2162CrossRefGoogle Scholar
  50. Wan J, Hao Y, Shi Y, Song Y-X, Yan H-J, Zheng J et al (2019) Ultra-thin solid electrolyte interphase evolution and wrinkling processes in molybdenum disulfide-based lithium-ion batteries. Nat Commun 10:3265CrossRefGoogle Scholar
  51. Wang MC, Gates BD (2013) Surface-initiated atom transfer radical polymerization-induced transformation of selenium nanowires into copper selenide@ polystyrene core–shell nanowires. ACS Appl Mater Interfaces 5:9546–9553CrossRefGoogle Scholar
  52. Wang R, Xu C, Lee J-M (2016) High performance asymmetric supercapacitors: new NiOOH nanosheet/graphene hydrogels and pure graphene hydrogels. Nano Energy 19:210–221CrossRefGoogle Scholar
  53. Wang T, Pan J, Achille KG, Sun Y (2017) A green dual complexation precipitation synthesis of hierarchical α-Ni (OH) 2 microspheres and their electrochemical performance. Int J Hydrogen Energy 42:19139–19147CrossRefGoogle Scholar
  54. Wu Y, Ni Y (2012) Low temperature rapid preparation of selenium nanostructures in the presence of food surfactants. Chem Eng J 187:328–333CrossRefGoogle Scholar
  55. Xie Q, Dai Z, Huang W, Zhang W, Ma D, Hu X et al (2006) Large-scale synthesis and growth mechanism of single-crystal Se nanobelts. Cryst Growth Des 6:1514–1517CrossRefGoogle Scholar
  56. Xu Q, Liu T, Li Y, Hu L, Dai C, Zhang Y et al (2017) Selenium encapsulated into metal-organic frameworks derived N-doped porous carbon polyhedrons as cathode for Na–Se batteries. ACS Appl Mater Interfaces 9:41339–41346CrossRefGoogle Scholar
  57. Yang CP, Xin S, Yin YX, Ye H, Zhang J, Guo YG (2013) An advanced selenium–carbon cathode for rechargeable lithium–selenium batteries. Angew Chem 125:8521–8525CrossRefGoogle Scholar
  58. Yang X, Wang H, Yu DY, Rogach AL (2018a) Vacuum calcination induced conversion of selenium/carbon wires to tubes for high-performance sodium–selenium batteries. Adv Func Mater 28:1706609CrossRefGoogle Scholar
  59. Yang X, Wang J, Wang S, Wang H, Tomanec O, Zhi C et al (2018b) Vapor-infiltration approach toward selenium/reduced graphene oxide composites enabling stable and high-capacity sodium storage. ACS Nano 12:7397–7405CrossRefGoogle Scholar
  60. Youn H-C, Jeong JH, Roh KC, Kim K-B (2016) Graphene–selenium hybrid microballs as cathode materials for high-performance lithium–selenium secondary battery applications. Sci Rep 6:30865CrossRefGoogle Scholar
  61. Zhang B, Dai W, Ye X, Zuo F, Xie Y (2006) Photothermally assisted solution-phase synthesis of microscale tubes, rods, shuttles, and an urchin-like assembly of single-crystalline trigonal selenium. Angew Chem Int Ed 45:2571–2574CrossRefGoogle Scholar
  62. Zhang J, Xu Y, Fan L, Zhu Y, Liang J, Qian Y (2015) Graphene–encapsulated selenium/polyaniline core–shell nanowires with enhanced electrochemical performance for Li–Se batteries. Nano Energy 13:592–600CrossRefGoogle Scholar
  63. Zhang Y, Zheng J, Zhao Y, Hu T, Gao Z, Meng C (2016) Fabrication of V2O5 with various morphologies for high-performance electrochemical capacitor. Appl Surf Sci 377:385–393CrossRefGoogle Scholar
  64. Zhang S-F, Wang W-P, Xin S, Ye H, Yin Y-X, Guo Y-G (2017) Graphitic nanocarbon-selenium cathode with favorable rate capability for Li–Se batteries. ACS Appl Mater Interfaces 9:8759–8765CrossRefGoogle Scholar
  65. Zhou X, Gao P, Sun S, Bao D, Wang Y, Li X et al (2015) Amorphous, crystalline and crystalline/amorphous selenium nanowires and their different (De) lithiation mechanisms. Chem Mater 27:6730–6736CrossRefGoogle Scholar

Copyright information

© King Abdulaziz City for Science and Technology 2019

Authors and Affiliations

  1. 1.State Key Laboratory of Chemical Resource EngineeringBeijing University of Chemical TechnologyBeijingPeople’s Republic of China

Personalised recommendations