Optimization of the controllable crystal size of iron/zeolite nanocomposites using a Box–Behnken design and their catalytic activity
- 6 Downloads
Experimental conditions for the synthesis of an iron nanoparticle (NPs)–zeolite composite (hereinafter denoted as Fe/zeolite NPs) via sol–gel method were optimized using a Box–Behnken design to produce a high formic acid yield. The effects of various parameters, including weight ratio of starting materials (Fe and zeolite), volume of polyethylene glycol (PEG) as a surfactant, and calcination temperature, on controllable crystallite size, and the relationship between crystallite size and formic acid yield were studied. The crystal size, as the main parameter indicating formic acid yield, of Fe NPs was evaluated through polynomial regression. Results revealed that the optimum conditions for producing small Fe NPs based on the model were obtained at a weight ratio of Fe to zeolite of 62.5%, a PEG volume of 2 mL, and a calcination temperature of 500 °C. The experimental results (52.02 nm) versus the predicted results (58.30 nm) of the crystal size of Fe NPs under the optimum synthesis conditions were similar. Furthermore, 62.5% Fe/zeolite NPs with a crystal size of 52.02 nm produced the highest formic acid concentration from CO2 hydrogenation. Conversely, 100% Fe/zeolite NPs had a smaller crystal size but exhibited a remarkably lower reaction performance. This high ratio of Fe and zeolite contributed to the increased agglomeration of Fe particles. The zeolite surface became fully covered and subsequently reduced the reactant interaction on catalyst surfaces.
Fe–zeolite nanocomposite was optimized using a Box–Behnken design.
The polynomial regression model showed the optimum nanoparticle (NP) crystal size of 52.02 nm.
Synthesis parameters significantly affected catalyst morphology and crystal.
The effect of calcination plays an important role on crystal and particle size.
The influence of NP crystallite size was evaluated in terms of formic acid production.
KeywordsBox–Behnken design Fe/zeolite nanoparticles Optimization Carbon dioxide Formic acid
The authors wish to thank Universiti Kebangsaan Malaysia (UKM) and Ministry of Higher Education for funding this project under Research Grant, DIP-2016-010, and GUP-2016-057, respectively, and the Centre of Research and Innovation Management (CRIM) UKM for the use of the instruments.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- Abdul Rahman NA, Mustaffa NA, Abdul Aziz ND, Badar N, Kamarulzaman N (2012) Synthesis and characterization of Fe2O3 prepared via sol–gel method. Adv Mater Res 545:410–413. https://doi.org/10.4028/www.scientific.net/AMR.545.410 CrossRefGoogle Scholar
- Chowdhury ZZ, Zain SM, Khan RA, Ahmad AA, Khalid K (2012) Application of response surface methodology (RSM) for optimizing production condition for removal of Pb (II) and Cu (II) onto Kenaf fiber based activated carbon. Appl Sci Eng Technol 4:458–465Google Scholar
- Danbaba N, Nkama I, Badau MH (2015) Application of response surface methodology (rsm) and central composite design (CCD) to optimize minerals composition of rice-cowpea composite blends during extrusion cooking. Int J Food Sci Nutr Eng 5:40–52. https://doi.org/10.5923/j.food.20150501.06 CrossRefGoogle Scholar
- Ferreira SLC, Bruns RE, Ferreira HS, Matos GD, David JM, Brandão GC, da Silva EGP, Portugal LA, dos Reis PS, Souza AS, dos Santos WNL (2007) Box–Behnken design: an alternative for the optimization of analytical methods. Anal Chim Acta 597:179–186. https://doi.org/10.1016/j.aca.2007.07.011 CrossRefGoogle Scholar
- Gupta AK, Gupta M (2005) Synthesis and surface engineering of iron oxide nanoparticles for biomedical applications. Biomaterials 26:3995–4021. https://doi.org/10.1016/j.biomaterials.2004.10.012 CrossRefGoogle Scholar
- Hakim A, Marliza TS, Abu Tahari NM, Wan Isahak RWN, Yusop RM, Mohamed Hisham WM, Yarmo AM (2016) Studies on CO2 adsorption and desorption properties from various types of iron oxides (FeO, Fe2O3, and Fe3O4). Ind Eng Chem Res 55:7888–7897. https://doi.org/10.1021/acs.iecr.5b04091 CrossRefGoogle Scholar
- Latempa TJ, Feng X, Paulose M, Grimes CA (2009) Temperature-dependent growth of self-assembled hematite (α-Fe2O3) nanotube arrays: rapid electrochemical synthesis and photoelectrochemical properties. J Phys Chem 113:16293–16298Google Scholar
- Li X, Liu Y, Zhang C, Wen T, Zhuang L, Wang X, Song G, Chen D, Ai Y, Hayat T, Wang X (2017) Porous Fe2O3 microcubes derived from metal organic frameworks for efficient elimination of organic pollutants and heavy metal ions. Chem Eng J. https://doi.org/10.1016/j.cej.2017.11.188 CrossRefGoogle Scholar
- Palimi MJ, Rostami M, Mahdavian M, Ramezanzadeh B (2015) A study on the corrosion inhibition properties of silane-modified Fe2O3 nanoparticle on mild steel and its effect on the anticorrosion properties of the polyurethane coating. J Coat Technol Res 12:277–292. https://doi.org/10.1007/s11998-014-9631-6 CrossRefGoogle Scholar
- Razavian M, Fatemi S, Komasi M (2014) Investigation the role of polyethylene glycol (PEG) as a co-template in synthesis of SAPO-34 catalyst. In: Proceedings of the the 8th international chemical engineering congress & exhibition, Kish, Iran, 24–27 February 2017Google Scholar
- Srikanth DV, Sridhar DC, Chennupati D, Rao MS (2016) Application of RSM for optimal response of process parameters on machining of CFRP composites by using AJM. Int Conf Electr Electron Optim Tech ICEEOT 1677–1681. https://doi.org/10.1109/ICEEOT.2016.7754970
- Wang GH, Li WC, Jia KM, Spliethoff B, Schüth F, Lu AH (2009) Shape and size controlled α-Fe2O3 nanoparticles as supports for gold-catalysts: synthesis and influence of support shape and size on catalytic performance. Appl Catal A Gen 364:42–47. https://doi.org/10.1016/j.apcata.2009.05.030 CrossRefGoogle Scholar
- Xu H, Sun M, Liu S, Li Y, Wang J, Chen Y (2017) Effect of the calcination temperature of cerium-zirconium mixed oxides on the structure and catalytic performance of WO3/CeZrO2 monolithic catalyst for selective catalytic reduction of NOx with NH3. RSC Adv 7:24177–24187. https://doi.org/10.1039/c7ra03054a CrossRefGoogle Scholar
- Zhang GY, Feng Y, Xu YY, Gao DZ, Sun YQ (2012) Controlled synthesis of mesoporous α-Fe2O3 nanorods and visible light photocatalytic property. Mater Res Bull 47:625–630. https://doi.org/10.1016/j.materresbull.2011.12.032 CrossRefGoogle Scholar