Advertisement

Transition metal-substituted Keggin-type polyoxometalates as catalysts for adipic acid production

  • Sihem Mouanni
  • Dahbia Amitouche
  • Tassadit MazariEmail author
  • Cherifa Rabia
Open Access
Original Article
  • 75 Downloads

Abstract

The adipic acid (AA) production was carried out in two stages: oxidation of cyclohexanone (-one) by Keggin-type polyoxometalate (POM), followed by oxidation of this latter by hydrogen peroxide. The process lasts 20 h and the temperature is maintained at 90 °C. AA is then recovered by cold crystallization (4 °C). The POMs have as formula HMPMo12O40 (M:Co, Ni, Mn, Cu or Zn). The materials were characterized by FT-IR and UV–Vis spectroscopies and by thermogravimetric analysis. The purity of adipic acid was confirmed by FT-IR and 13C and 1H NMR analysis. The effects of POM composition, catalyst/-one molar ratio and the cyclohexanol addition to -one on adipic acid yield were examined. The whole catalysts were found to be effective toward cyclohexanone oxidation and the highest yield (53%) was obtained with HZnPMo12O40 system for a catalyst/-one molar ratio of 1.89 × 10−3. The alcohol addition to -one has a negative effect on adipic acid formation.

Keywords

Keggin-type heteropoly salts Oxidation Hydrogen peroxide Cyclohexanone Adipic acid 

Introduction

Adipic acid (AA) is a raw material for the production of polyamides, particularly nylon 6-6, polyesters and polyurethanes and food additives [7, 17]. AA is obtained industrially from oxidation of a mixture of cyclohexanone and cyclohexanol (noted KA oil) by nitric acid. This process has several disadvantages such as the corrosion phenomenon and release of nitrogen oxides coming from nitric acid reduction. Among these gases, N2O that represents 300 kg N2O/ton of AA, is the most dangerous. In addition to its strong greenhouse effect and long residence time in the atmosphere, it participates in ozone layer destruction [22, 34]. The development of an environmentally friendly process is one of the most difficult research tasks to achieve.

Among used green oxidants, hydrogen peroxide (H2O2) seems to be the most attractive compared to oxygen molecules and air [5, 8, 33, 35]. Effectively, in addition to being easy to handle, it is known for its clean environment because of its reduction that leads only to water formation.

In organic synthesis, H2O2 is widely used in alkene epoxidation reactions [12, 13, 18] and Baeyer–Villiger oxidation reactions of cyclic ketones and aldehydes [37, 38, 40, 41]. In the case of AA synthesis, H2O2 was used in the presence of different catalysts such as µ3-oxo-bridged Co/Mn cluster complexes CoMn2(O) [9], [MnIIIT(p-Cl)PP]Cl [23], N-hydroxyphthalimide combined with Mn(acac)2 or Co(OAc)2 [19], β-{[H3NC(CH2O)3]2MnMo6O18} [24], [CoPM11O39]5− and [NiPM11O39]5− [1]. In these processes, H2O2 was added to the reaction mixture at the same time as the substrate (cyclohexene, cyclohexanone or cyclohexanol) and catalyst.

In our previous works, AA synthesis was carried out in two stages, using the Nomiya process [32], in the presence of Keggin or Dawson polyoxometalate of formulas MxPMo12O40 (M:Fe, Ni, Co and x:1 or 1.5) [26], H3–2xCox PMo12O40 (x:0–1.5) [4] (NH4)3–2xNixPMo12O40 (x:0.25–1.5) [39] and (NH4)xAyPMo12O40 (An+ = Sb3+, Bi3+ or Sn2+) [31]. In the first step, the reaction mixture consists of a substrate (cyclohexanone or cyclohexanol) and POM. The role of the POM is to oxidize the substrate, which results in a color change from yellow (characteristic color of the oxidized POM) to blue (characteristic color of the reduced POM). Then, hydrogen peroxide is added in the second step. In the latter case, H2O2 reacts as an oxidant to restore the POM and as a peroxide to form peroxo species with the POM. These peroxo species were reported by several authors as the active species in the formation of oxygenated compounds. They were evidenced by multinuclear NMR spectroscopies in the cases of H3PW12O40 as {PO4[WO(O2)2]4}3− and {PO4[WO(O2)2]2}2− [14, 16] and H3PMo12O40 as {PO4[MoO(O2)2]4}3−, {PMo3Om}n and {PO4[MoO(O2)2]2}2− [2, 21].

In these different series of POMs, it was observed that those which contain metal (M) counter-ions having several oxidation states such as Co, Mn, Sn and Sb led to better AA yields. This has been attributed to the presence of several redox couples as Co(III)/Co(II), Mn(IV)/Mn(II), Sn(IV)/Sn(II) and Sb(V)/Sb(III), formed during the POM. A redox reaction occurs in situ between Mo(VI) and M(II). On the other hand, in recent work, it has been shown that the proton presence in the POM allows the activation of cyclohexanone by keto-enolic tautomerization, before its oxidation into more oxygenated compounds [2].

In this context and to understand the influence of the metal nature on adipic acid formation, we tested a series of substituted POMs by introducing both single metal atom with an oxidation state of 2 and single proton as counter-ion of the [PMo12O40]3− Keggin anion. The choice was made on Co and Mn that have several oxidation states, Ni that has only one oxidation state (II) and Cu that has several oxidation states, but it cannot be reduced from Cu(II) to Cu(I) and Zn as a non-transition metal with one oxidation state (II). Their formula is HMPMo12O40. They were characterized by FT-IR and UV–Vis spectroscopies. The catalytic cyclohexanone oxidation to adipic acid was carried out in the homogenous phase at 90 °C using H2O2 (30%). The effects of the catalyst/-one molar ratio and that of the alcohol addition (ratio -one/-ol) on adipic acid yield were studied. The purity of adipic acid was verified by FT-IR, 13C and 1H NMR analysis.

Experimental

Material synthesis

HMPMo12O40 heteropoly salts were prepared using a cationic exchange method [4, 26, 39]. In the first step, H3–2xBaxPMo12O40, substituted salt was prepared by Ba(OH)2 addition to an aqueous solution of H3PMo12O40 in stoichiometric ratios, according to the RXN. (1) To avoid the Keggin anion decomposition, it is necessary to maintain pH < 2, by gradual addition of Ba(OH)2. The second step consists in the substitution of Ba2+ ions by the transition metal M2+ (M:Co, Ni, Mn, Cu or Zn) using MSO4 according to the RXN. (2) After total BaSO4 precipitation, the filtrate was dried at 50 °C under vacuum and HMPMo12O40 recovered in the form of a powder:
$${\text{H}}_{3} {\text{PMo}}_{{12}} {\text{O}}_{{40}} + {\text{Ba(OH)}}_{2} \to {\text{HBaPMo}}_{{12}} {\text{O}}_{{40}} + 2{\text{H}}_{2} {\text{O RXN}}(1)$$
$${\text{HBaPMo}}_{12} {\text{O}}_{40} + {\text{MSO}}_{4} \to {\text{HMPMo}}_{12} {\text{O}}_{40} + {\text{BaSO}}_{4} \downarrow {\text{RXN}}(2)$$

The M presence confirmation was realized using the complexation tests shown in Table 1.

Table 1

Complexation tests

Cations

Reagents

Initial color

Products

Final color

Cu2+

CH3COOH (5 ml, 6 M) + K4Fe(CN)6 (1 ml, 0.5 M)

Blue

Cu2Fe(CN)6

Red brown

Mn2+

H2O2 (3 ml, 30%) + HNO3 (4 ml, 0.5 M) + KIO4

Purple

MnO2, nH2O

Black

Zn2+

HCl (1 ml, 3 M) + K4Fe(CN)6 (3 ml, 1 M)

White

/

Transparent

Co2+

NH4SCN (0.5 g) + amyl alcohol (3 ml) + acetic acid (solvent)

Blue

[Co(SCN)4]2−

Blue

Ni2+

Dimethylglyoxime (3 ml)

Red

/

Red brown

Characterization

The FT-IR spectra recording of salts was carried out on a Fourier Transform Nicolet-Magna 550 IR spectrometer. The samples are ground in the KBr (2 mg of sample per 200 mg of KBr) and then pressed in the form of pellets. The spectra were treated by Omnic 8.1 software.

UV–Vis spectra of samples were recorded between 100 and 1000 nm on a Shimadzu UV-1601 PC spectrometer.

Thermal analysis was performed between room temperature and 600 °C, under air flow with a heating rate of 5 °C/min on a TGA 2050 apparatus.

Solid-phase 13C and 1H NMR spectroscopies were performed on a BioSpin GmbH, Bruker spectrometer. H3PO4 (85%) was used as an external reference.

Catalytic reaction

Cyclohexanone oxidation was performed according to the literature [32]. A mixture constituting the substrate (-one) and catalyst was introduced into a flask under stirring (1000 rpm) and heated at 90 °C under a reflux condenser. After few minutes, the reaction mixture yellow in color turns blue, the characteristic color of reduced POM (MoV). Then, hydrogen peroxide was added to restore the initial color, the characteristic color of oxidized POM (MoVI). This operation is repeated after each catalyst reduction. The end of the reaction is reached when the POM is no longer reduced, thus indicating the total substrate consumption. After 20 h of reaction time, the mixture was cooled to 4 °C and then the white crystals of adipic acid were recovered after almost two nights and weighed (w (AA)exp). The AA purity was verified by melting point (152 °C) and FT-IR and NMR spectroscopies (13C and 1H). Hydrogen peroxide concentration was verified by potassium permanganate dosage before performing the catalytic test. The adipic acid yield was calculated by following formula:
$${\text{AA}}\,{\text{yield}}\, ( {\text{\% )}} = 100 \times {\text{w}}\, ( {\text{AA)}}_{\exp } / {\text{w}}\, ( {\text{AA)}}_{\text{the}}$$

Results and discussion

Characterization results

FT-IR spectra of HMPMo12O40 (Fig. 1) showed the characteristic vibration bands of the Keggin structure in the spectral range of 1200–400 cm−1 [36]. The vibration band corresponding to phosphorus–oxygen, vas P–Oa, was observed at 1062 cm−1 and those assigned to metal–oxygen, vas Mo–Od, vas Mo–Ob–Mo and vas Mo–Oc–Mo at 960, 860 and 780 cm−1, respectively. The proton partial substitution of H3PMo12O40 by transition metal (Co, Ni, Mn, Cu or Zn) does not reveal a significant variation in frequency values of different IR vibration bands, confirming thus that the introduction of a metal atom in cationic position does not disturb the Keggin anion symmetry as already reported in other studies [4, 26].
Fig. 1

FT-IR spectra of HMPMo12O40

The UV–visible spectra of different solids (Fig. 2) show a large charge transfer band oxygen–molybdenum(VI) in 200–480 nm range, consisting of two components located at 200–300 and 300–450 nm [11, 27]. The latter are associated with the different types of oxygen atoms of the Keggin anion, inter-anion charge transfer transitions and counter-ion nature. In the case of HZnPMo12O40, the second component is slightly shifted to higher wavelength. This difference can be attributed to a non-transition metal character and/or saturated d atomic orbital (d10) of Zn.
Fig. 2

UV–visible spectra of HMPMo12O40

The TG curves of the samples (not represented here) show different mass losses. The first loss was observed in the temperature range 50–180 °C, corresponding to the departure of 8–13 hydration water molecules. The second one, observed in the range 180–380 °C, was attributed to the departure of half constitution water molecule (1/2 H2O) that results from the combination of proton with an oxygen atom of the Keggin anion. Above 400 °C, the POM decomposition to P2O5, MoO3 and MO occurred. The TG analysis results are reported in the Table 2. A good correlation between the experimental and theoretical formulas was observed, confirming also the reliability of the cationic exchange synthesis method.
Table 2

Thermal analysis results of HMPMo12O40 salts

Theoretical formula

Experimental formula

H1.00Co1.00PMo12O40

H0.87Co1.07PMo12O40

H1.00Zn1.00PMo12O40

H1.04 Zn0.98PMo12O40

H1.00Mn1.00PMo12O40

H0.94 Mn1.03PMo12O40

H1.00Cu1.00PMo12O40

H0.97Co1.01PMo12O40

H1.00Ni1.00PMo12O40

H0.94Ni1.03PMo12O40

Catalytic performances of HMPMo12O40 for adipic acid synthesis

The reaction products are adipic, glutaric and succinic acids. In this work, only adipic acid (AA) was considered. It was isolated by crystallization at 4 °C and characterized by FT-IR and NMR spectroscopies (13C and 1H). The IR spectrum of adipic acid (Fig. 3) shows an intense vibration band located at 1700 cm−1 and another more broad at 3000 cm−1, characteristic of the C=O and O–H bonds of the carboxylic acid, respectively.
Fig. 3

FT-IR spectrum of adipic acid

The 1H NMR spectrum shows two signals at 1.65 and 2.33 ppm corresponding to methyl groups –CH2– and a peak associated with the proton of the –COOH group at 10.48 ppm (Fig. 4). The 13C NMR spectrum shows two peaks at 25.11 and 38.83 ppm, assigned to carbon atoms of methyl groups –CH2– and a signal at 174.39 ppm characteristic of the carbon atom of the carboxylic group (Fig. 5). The peaks observed at 2.06 ppm in 1H NMR (Fig. 4) and at around 29.84 and 206.23 ppm in 13C NMR (Fig. 5) are associated with the acetone solvent.
Fig. 4

1HNMR spectra of adipic acid

Fig. 5

13CNMR spectra of adipic acid

Adipic acid synthesis from cyclohexanone oxidation

In the preliminary tests carried out with H3PMo12O40 for the cyclohexanone oxidation at 90 °C during 20 h, no crystal, corresponding to the adipic acid formation, was observed after cold conditions (4 °C) overnight, when the reaction mixture constituted of: (1) cyclohexanone and catalyst, (2) substrate, catalyst and hydrogen peroxide and (3) substrate and hydrogen peroxide. In the first case (1), the POM oxidizes the substrate that is visualized by the change in color from blue to yellow. In the second case (2), the reaction mixture turns to blue, attesting to the reduction of POM. The latter can oxidize both cyclohexanone and hydrogen peroxide (H2O2 being amphoteric). POM has a higher oxidizing power than H2O2. In case (3), the substrate has probably reacted with hydrogen peroxide. From these observations, it is necessary to apply the procedure mentioned in the experimental part.

The catalytic performances of HMPMo12O40 are summarized in Table 3. The proton partial substitution by cobalt or copper seems to have no effect on the catalytic behavior of H3PMo12O40 (25 and 29, respectively, against 28% of AA yield). The introduction of manganese or nickel strongly decreases the AA yield from 28 to 16 and 2%, respectively, whereas the presence of zinc leads to a strong AA yield increase (41 against 2–29%). The difference in catalytic behavior can be attributed to several parameters: (1) its non-transition metal character, (2) presence of a saturated d atomic orbital (d10), Zn(II) behaves like a Lewis acid that would promote substrate activation, (3) a non-reducible character that would more easily give peroxo entities (ZnO2). These properties seem to create a moderate oxidative power that can favor AA formation to the detriment of those of other oxygenated products. This observation has already been signaled in the case of the vanadium substituted molybdenum in the Dawson type POMs [30].
Table 3

AA yields as a function of POM composition

Catalyst

AA yield (%)

H3PMo12O40

28

HCoPMo12O40

25

HNiPMo12O40

2

HMnPMo12O40

16

HCuPMo12O40

29

HZnPMo12O40

41

Conditions Treact = 90 °C, agitation rate: 1000 rpm, reaction time = 20 h, mcatalyst = 0.03 g, n-one = 30 mmol, H2O2 addition mode: 0.5–0.1 ml

Figure 6 presents the AA yield variation, with an error bar of 3%, as a function of catalyst/-one molar ratio. The -one oxidation was carried out in the presence of HZnPMo12O40. The AA yield decreases from 41 to 7% when catalyst/-one molar ratio increases from 0.47 × 10−3 to 1.41 × 10−3. The maximum AA yield (53%) was reached with a catalyst/-one molar ratio of 1.89 × 10−3 (catalyst: 0.12 g, cyclohexanone: 30 mmol). At higher ratios, AA yield drop from 53 to 2% was observed.
Fig. 6

AA yields as a function of catalyst/-one molar ratio, (catalyst: HZnPMo12O40, Treact = 90 °C, agitation rate: 1000 rpm, reaction time = 20 h, H2O2 addition mode: 0.5–0.1 ml)

Adipic acid synthesis from cyclohexanone/cyclohexanol oxidation

The AA synthesis was also performed via -one/-ol mixture oxidation in the presence of HZnPMo12O40, with a catalyst/-one molar ratio of 1.89 × 10−3. Different -one/-ol ratios were examined (100/0, 75/25, 50/50, 25/75, 100/0). The obtained results (Fig. 7) showed that ketone oxidation alone led to 53% of AA yield and that of alcohol alone to 9%, whereas similar AA yields (4–5%) were obtained with -one/-ol ratios of 75/25 and 25/75. With an equimolar mixture (50/50%), AA formation was not observed, contrarily to the industrial process. The negative effect of alcohol presence in the reaction mixture has already been mentioned [4, 8, 20, 26, 28, 39]. It was attributed to the formation of hydrogen bonds between the C=O group of the ketone and the hydrogen of the C–OH group of cyclohexanol, which makes the -one oxidation of the mixture difficult.
Fig. 7

AA yields as a function of -one/-ol mixture composition (catalyst: HZnPMo12O40, Treact = 90 °C, agitation rate: 1000 rpm, reaction time = 20 h, mcatalyst = 0.12 g, n-one = 30 mmol, H2O2 addition mode: 0.5–0.1 ml)

Comparative study

Table 4 shows the adipic acid yields obtained by oxidation of cyclohexanone over various catalysts reported in literature. The use of various organic and inorganic solvents and Mn/Co-based materials as catalyst leads to AA yields slightly higher compared to those obtained with Dawson or Keggin POMs as catalysts, in free solvent (75–91% against 57–75%). It is noted that the AA yields (57–75%) are higher than those obtained with vanadium based POMs, in the presence of CH3COOH, CH3CN, CH3OH as solvent (50–54%). These latter’s are similar to that obtained with HZnPMo12O40 (53%) used in this study. In conclusion, the comparison between these different processes shows well that the use of POMs in the absence of the solvent leads to a process that is much cleaner and with appreciable AA yields.
Table 4

Comparison between several processes of adipic acid synthesis from cyclohexanone oxidation

Catalyst

Solvent

T (°C)

AA yield (%)

Refs.

Mn(OAc)2

CH3COOH/CF3COOH

65

75

[10]

Mn(NO3)2/Co(NO3)2

CH3COOH + HNO3

40

91

[15]

Co/Mn cluster

CH3COOH/H2O

100

85

[6]

H7PMo8V4O40

CH3COOH/H2O

70

50

[3]

H5PMo10V2O40

CH3CN/CH3OH

60

54

[9]

H1Mn0.25Co0.75PMo12O40 75 [28]

Free

90

75

[29] (in press)

K6P2Mo6W12O62

Free

90

58

[30]

(NH4)0,5Sn1.25PMo12O40

Free

90

57

[31]

HZnPMo12O40

Free

90

53

This work

Reaction pathway

The catalytic process of cyclohexanone oxidation by hydrogen peroxide in the presence of POM is composed of three steps. The first step corresponds to the substrate oxidation by the POM. The latter changes color from yellow, the characteristic color of POM at the oxidized state (noted POMox), to blue, the characteristic color of POM at the reduced state (noted POMred). It was reported that the POMox, corresponding to [PMo12O40]3−, Keggin anion (noted α (0)), undergoes successive reductions from α (0) to α(II) and β(II) [PMo12O40]5− and to α(IV) and β(IV) [PMo12O40]7−, in the presence of the reducing agent [2]. In addition, a Mars and Van Krevelen mechanism can be assumed, in which POMox oxygen atoms participate in the oxidation process by giving lacunary POMs (noted POM lac) as [PMo11O39]7− and [PMo9O34]9− [25]. In these latter species, there is a departure of both molybdenum and oxygen atoms (Eq. 1). On the other hand, during this first step, a keto–enol tautomeric equilibrium catalyzed by the Brønsted acidity of the POM (HMPMo12O40) is attained, a necessary step for substrate activation (Eq. 2).

This step can be explained by the following reactions shown in the equations (Eqs. 1 and 2) that take place simultaneously:
$${\text{Substrate}} + {\text{POMox}} \to {\text{products}} + {\text{POMred}} + {\text{POMlac}}.$$
(1.)
In the second step, the addition of hydrogen peroxide led to a POM color change from blue to yellow that is attributed to the POMred oxidation. It was reported that in the presence of hydrogen peroxide, peroxo species such as {PO4[MoO(O2)2]4}3−, {PMo3Om}n and {PO4[MoO(O2)2]2}2− (noted peroxo-POM) are formed, as evidenced by multinuclear NMR spectroscopy [2, 21]. This step can be explained by the following equation:
$${\text{POMred}} + {\text{H}}_{2} {\text{O}}_{2} \to {\text{peroxo-species}}$$
(3)
During the 20 h of reaction, the peroxo-POM species will react with some products from the Eq. (1) to form final products including adipic acid according with Eq. (4). In this last step, we can also assume another similar mechanism to that of Mars and Van Krevelen, where the oxygen atoms of the peroxo-POM would intervene in the intermediate products’ oxidation:
$${\text{Peroxo}} - {\text{POM}}_{\text{ox}} + {\text{intermediate species}} \to {\text{reaction products}} + {\text{POMox}}$$
(4)

Conclusion

The oxidation of cyclohexanone and that of cyclohexanol/cyclohexanone mixture was carried out in the homogenous phase at 90 °C using H2O2 (30%) in the presence of a series of Keggin-type POMs of formula HMPMo12O40 (M:Co, Ni, Mn, Cu or Zn).

The formulation, HMPMo12O40, was evidenced by TG analysis for proton amount and complexation characteristic test of each metal in the cationic position. FT-IR and UV–Vis spectroscopies have evidenced the Keggin anion structure.

The catalytic results showed that HZnPMo12O40 exhibits the highest adipic acid yield (53%), evidencing the efficiency of the presence of a metal compared to that of a transition metal as a counter-ion of the [PMo12O40]3− system.

A reaction pathway was proposed showing different steps of the oxidation process.

The use of both hydrogen peroxide, green oxidant and HMPMo12O40, non-polluting catalyst can be an attractive route for developing a clean adipic acid industrial process compared to the HNO3 method.

Notes

References

  1. 1.
    Alcaniz-Monge J, Trautwein G, Garcia-Garcia A (2014) Influence of peroxometallic intermediaries present on polyoxometalates nanoparticles surface on the adipic acid synthesis. J Mol Catal A Chem 394:211–216.  https://doi.org/10.1016/j.molcata.2014.07.023 CrossRefGoogle Scholar
  2. 2.
    Amitouche D, Haouas M, Mazari T, Mouanni S, Canioni R, Rabia C, Cadot E, Marchal-Roch C (2018) The primary stages of polyoxomolybdate catalyzed cyclohexanone oxidation by hydrogen peroxide as investigated by in situ NMR. Substrate activation and evolution of the working catalyst. Appl Catal A Gen 561:104–116.  https://doi.org/10.1016/j.apcata.2018.05.017 CrossRefGoogle Scholar
  3. 3.
    Atlamsani A, Brégeault JM, Ziyad M (1993) Oxidation of 2-methylcyclohexanone and cyclohexanone by dioxygen catalyzed by vanadium-containing heteropolyanions. J Org Chem 58:5663–5665.  https://doi.org/10.1021/jo00073a026 CrossRefGoogle Scholar
  4. 4.
    Benadji S, Mazari T, Dermeche L, Salhi N, Cadot E, Rabia C (2013) Clean alternative for adipic acid synthesis via liquid-phase oxidation of cyclohexanone and cyclohexanol over H3−2xCoxPMo12O40 catalysts with hydrogen peroxide. Catal Lett 143:749–755.  https://doi.org/10.1007/s10562-013-1025-3 CrossRefGoogle Scholar
  5. 5.
    Blach P, Böstrom Z, Franceschi-Messant S, Lattes A, Perez E, Rico-Lattes I (2010) Recyclable process for sustainable adipic acid production in microemulsions. Tetrahedron 66:7124–7128.  https://doi.org/10.1016/j.tet.2010.06.093 CrossRefGoogle Scholar
  6. 6.
    Brégeault JM, Bassam EA, Martin J (1991) US Patent 4: 983, 767Google Scholar
  7. 7.
    Cavallaro A, Bart JCJ, Cavallaro S (1991) Industrial production and use of adipic acid. Catal Today 9:237–254.  https://doi.org/10.1016/0920-5861(91)80049-F CrossRefGoogle Scholar
  8. 8.
    Cavani F, Ferronia L, Frattini A, Lucarelli C, Mazzinia A, Raabova K, Alini S, Accorinti P, Babini P (2011) Evidence for the presence of alternative mechanisms in the oxidation of cyclohexanone to adipic acid with oxygen, catalysed by Keggin polyoxometalates. Appl Catal A Gen 391:118–124.  https://doi.org/10.1016/j.apcata.2010.04.032 CrossRefGoogle Scholar
  9. 9.
    Chavan SA, Srinivas D, Ratnasamy P (2002) Oxidation of cyclohexane, cyclohexanone, and cyclohexanol to adipic acid by a non-HNO3 route over Co/Mn cluster complexes. J Catal 212:39–45.  https://doi.org/10.1006/jcat.2002.3756 CrossRefGoogle Scholar
  10. 10.
    Constantini M, Krumenacker L (1983) FR Patent 2: 541, 993Google Scholar
  11. 11.
    Dermeche L, Thouvenot R, Hocine S, Rabia C (2009) Preparation and characterization of mixed ammonium salts of Keggin phosphomolybdate. Inorg Chem Acta 362:3896–3900.  https://doi.org/10.1016/j.ica.2009.04.049 CrossRefGoogle Scholar
  12. 12.
    Ding Y, Gao Q, Li G, Zhang H, Wang J, Yan L, Suo J (2004) Selective epoxidation of cyclohexene to cyclohexene oxide catalyzed by Keggin-type heteropoly compounds using anhydrous urea–hydrogen peroxide as oxidizing reagent and acetonitrile as the solvent. J Mol Catal A Chem 218:161–170.  https://doi.org/10.1016/j.molcata.2004.04.019 CrossRefGoogle Scholar
  13. 13.
    Ding Y, Ma B, Gao Q, Li G, Yan L, Suo J (2005) A spectroscopic study on the 12-heteropolyacids of molybdenum and tungsten (H3PMo12-nWnO40) combined with cetylpyridinium bromide in the epoxidation of cyclopentene. J Mol Catal A Chem 230:121–128.  https://doi.org/10.1016/j.molcata.2004.12.017 CrossRefGoogle Scholar
  14. 14.
    Duncan DC, Chambers RC, Hecht E, Hill CL (1995) Mechanism and dynamics in the H3[PW12O40] catalyzed selective epoxidation of terminal olefins by H2O2. Formation, reactivity, and stability of {PO4[WO(O2)2]4}3−. J Am Chem Soc 117:681–691.  https://doi.org/10.1021/ja00107a012 CrossRefGoogle Scholar
  15. 15.
    Fumagalli C, Minisci F, Pirola R (2001) WO Patent 01/87, 815Google Scholar
  16. 16.
    Frenzel R, Sathicq ÁG, Blanco MN, Romanelli GP, Pizzio LR (2015) Carbon-supported metal-modified lacunary tungstosilicic polyoxometallates used as catalysts in the selective oxidation of sulphides. Mol Catal A Chem 403:27–36.  https://doi.org/10.1016/j.molcata.2015.02.021 CrossRefGoogle Scholar
  17. 17.
    Ghosh S, Acharyya SS, Adak S, Konathala LS (2014) Selective oxidation of cyclohexene to adipic acid over silver supported tungsten oxide nanostructured catalysts. Green Chem 16:2826–2834.  https://doi.org/10.1039/c4gc00130c CrossRefGoogle Scholar
  18. 18.
    Ishii Y, Yamawaki K, Ura T, Yamada H, Yoshida T, Ogawa M (1988) Hydrogen peroxide oxidation catalyzed by heteropoly acids combined with cetylpyridinium chloride: epoxidation of olefins and allylic alcohols, ketonization of alcohols and diols, and oxidative cleavage of 1,2-diols and olefins. Org Chem 53:3581–3593.  https://doi.org/10.1021/jo00250a032 CrossRefGoogle Scholar
  19. 19.
    Iwahama T, Syojyo K, Sakaguchi S, Ishii Y (1998) Direct conversion of cyclohexane into adipic acid with molecular oxygen catalyzed by n-hydroxyphthalimide combined with Mn(acac)2 and Co(OAc)2. Org Process Res Dev 2:255–260.  https://doi.org/10.1021/op980016y CrossRefGoogle Scholar
  20. 20.
    Katsoulis DE (1998) A survey of applications of polyoxometalates. Chem Rev 98:359.  https://doi.org/10.1021/cr960398a CrossRefPubMedGoogle Scholar
  21. 21.
    Kuznetsova LI, Kuznetsova NI, Maksimovskaya RI, Koshcheeva OS, Utkin VA (2013) Catalytic properties of heteropoly compounds in 1,3-butadiene oxidation with hydrogen peroxide. Kinet Catal 54:420–430.  https://doi.org/10.1134/S0023158413040071 CrossRefGoogle Scholar
  22. 22.
    Leont’ev AV, Fomicheva OA, Proskurnina MV, Zefirov NS (2001) Modern chemistry of nitrous oxide. Russ Chem Rev 70:91–104.  https://doi.org/10.1070/RC2001v070n02ABEH000631 CrossRefGoogle Scholar
  23. 23.
    Li H, She Y, Fu H, Cao M, Wang J, Wang T (2015) Synergistic effect of co-reactant promotes one-step oxidation of cyclohexane into adipic acid catalyzed by manganese porphyrins. Can J Chem 93:696–701.  https://doi.org/10.1139/cjc-2014-0515 CrossRefGoogle Scholar
  24. 24.
    Luo J, Huang Y, Ding B, Wang P, Geng X, Zhang J, Wei Y (2018) Single-atom Mn active site in a triol-stabilized β-Anderson manganohexamolybdate for enhanced catalytic activity towards adipic acid production. Catalysts 8:121.  https://doi.org/10.3390/catal8030121 CrossRefGoogle Scholar
  25. 25.
    Maksimovskaya RI (2013) Molybdophosphate heteropoly blues: electron-transfer reactions in aqueous solutions as studied by NMR. Polyhedron 65:54–59.  https://doi.org/10.1016/j.poly.2013.08.014 CrossRefGoogle Scholar
  26. 26.
    Mazari T, Benadji S, Tahar A, Dermeche L, Rabia C (2013) Simple and green liquid-phase synthesis of adipic acid using Keggin-type phosphomolybdates catalysts. J Mat Sci Eng B 3:146–152.  https://doi.org/10.1016/j.molcata.2014.07.023 CrossRefGoogle Scholar
  27. 27.
    Mazari T, Marchal-Roch C, Hocine S, Salhi N, Rabia C (2009) Oxidation of propane over substituted Keggin phosphomolybdate salts. J Nat Gas Chem 18:319–324.  https://doi.org/10.1016/S1003-9953(08)60111-5 CrossRefGoogle Scholar
  28. 28.
    Mouanni S, Mazari T, Benadji S, Dermeche L, Marchal-Roch C, Rabia C (2018) Simple and green adipic acid synthesis from cyclohexanone and/or cyclohexanol oxidation with efficient (NH4)xHyMzPMo12O40 (M: Fe Co, Ni) catalysts. BREC 13:386–391Google Scholar
  29. 29.
    Mouanni S, Mazari T, Amitouche D, Benadji S, Dermeche L, Roch-Marchal C, Rabia C (2019) Preparation and characterization of H3−2 (x+y)MnxCoyPMo12O40 heteropolysalts. Application to adipic acid green synthesis from cyclohexanone oxidation with hydrogen peroxide. C R Chim.  https://doi.org/10.1016/j.crci.2019.01.003 CrossRefGoogle Scholar
  30. 30.
    Moudjahed M, Dermeche L, Benadji S, Mazari T, Rabia C (2016) Dawson-type polyoxometalates as green catalysts for adipic acid synthesis. Mol Catal A Chem 414:72–77.  https://doi.org/10.1016/j.molcata.2015.12.014 CrossRefGoogle Scholar
  31. 31.
    Mouheb L, Dermeche L, Mazari T, Benadji S, Essayem N, Rabia C (2018) Clean adipic acid synthesis from liquid-phase oxidation of cyclohexanone and cyclohexanol using (NH4)xAyPMo12O40 (A: Sb, Sn, Bi) mixed heteropolysalts and hydrogen peroxide in free solvent. J Catal Lett 148:612–620.  https://doi.org/10.1007/s10562-017-2263-6 CrossRefGoogle Scholar
  32. 32.
    Nomiya K, Miwa M, Sugaya Y (1984) Catalysis by heteropolyacid-VII. Catalytic oxidation of cyclohexanol by dodecamolybdate. Polyhedron 3:607–610.  https://doi.org/10.1016/S0277-5387(00)88096-1 CrossRefGoogle Scholar
  33. 33.
    Penate IQ, Lesage G, Cognet P, Poux M (2012) Clean synthesis of adipic acid from cyclohexene in microemulsions with stearyl dimethyl benzyl ammonium chloride as surfactant: from the laboratory to bench scale. Chem Eng J 200–202:357–364CrossRefGoogle Scholar
  34. 34.
    Pérez-Ramıırez J, Kapteijn F, Schöffel K, Moulijn JA (2003) Formation and control of N2O in nitric acid production: where do we stand today? Appl Catal B Environ 44:117–151.  https://doi.org/10.1016/S0926-3373(03)00026-2 CrossRefGoogle Scholar
  35. 35.
    Piyali B, Kajari G, Safikul I, Astam KP, Manirul I, Asim B (2016) New hybrid iron phosphonate material as an efficient catalyst for the synthesis of adipic acid in air and water. ACS Sustain 4:7147–7157.  https://doi.org/10.1021/acssuschemeng.6b02023 CrossRefGoogle Scholar
  36. 36.
    Rocchiccioli-Deltcheff C, Fournier M, Franck R, Thouvenot R (1984) Vibrational investigations of polyxometalates. 4. Valence force fields of anions related to the lindqvist structure. J Mol Struct 114:49–56.  https://doi.org/10.1016/S0022-2860(84)87202-6 CrossRefGoogle Scholar
  37. 37.
    Renz M, Blasco T, Corma A, Fornes V, Jensen R, Nemeth L (2002) Selective and shape-selective Baeyer–Villiger oxidations of aromatic aldehydes and cyclic ketones with Sn-beta zeolites and H2O2. Chem Eur J 8:20CrossRefGoogle Scholar
  38. 38.
    Strukul G, Varagnolo A, Pinna F (1997) New (old) hydroxo complexes of platinum(II) as catalysts for the Baeyer–Villiger oxidation of ketones with hydrogen peroxide. J Mol Catal A Chem 17:413–423.  https://doi.org/10.1016/S1381-1169(96)00246-4 CrossRefGoogle Scholar
  39. 39.
    Tahar A, Benadji S, Mazari T, Dermeche L, Marchal-Roch C, Rabia C (2015) Preparation, characterization and reactivity of Keggin type phosphomolybdates, H3−2xNixPMo12O40 and (NH4)3−2xNixPMo12O40, for adipic acid synthesis. Catal Lett 145:569–575.  https://doi.org/10.1007/s10562-014-1373-7 CrossRefGoogle Scholar
  40. 40.
    Terent’ev AO, Platonov MM, Kashin AS, INikishin GI (2008) Oxidation of cycloalkanones with hydrogen peroxide: an alternative route to the Baeyer–Villiger reaction. Synthesis of dicarboxylic acid esters. Tetrahedron 64:7944–7948.  https://doi.org/10.1016/j.tet.2008.06.027 CrossRefGoogle Scholar
  41. 41.
    Xu S, Wang Z, Zhang X, Zhang X, Ding K (2008) Chiral Brønsted acid catalyzed asymmetric Baeyer–Villiger reaction of 3-substituted cyclobutanones by using aqueous H2O2. J Angew Chem 120:2882–2885.  https://doi.org/10.1002/ange.200705932 CrossRefGoogle Scholar

Copyright information

© The Author(s) 2019

Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Authors and Affiliations

  • Sihem Mouanni
    • 1
  • Dahbia Amitouche
    • 1
    • 2
  • Tassadit Mazari
    • 1
    • 2
    Email author
  • Cherifa Rabia
    • 1
  1. 1.Laboratoire de Chimie du Gaz NaturelFaculté de Chimie, USTHBAlgierAlgeria
  2. 2.Laboratoire de Chimie Appliquée et Génie ChimiqueUniversité Mouloud Mammeri, Tizi-Ouzou (UMMTO)AlgierAlgeria

Personalised recommendations