Experimental Study on Oxidizing Roasting Process of Black Dross
- 4 Downloads
The oxidizing roasting process of the black dross was investigated by X-ray diffraction, thermogravimetry–differential thermal analysis and thermodynamic calculation, and the effects of roasting conditions on the removal rate of AlN and salt flux in black dross were studied. The results show that the best roast conditions for oxidation of AlN are as follows: the roast temperature is about 800 °C, and the roast time is about 60 min. The removal rate of AlN is up to 93.8%. Salt flux in black dross can be removed in the form of flue gas, but it needs a higher temperature than AlN oxidation reaction. The removal rate of salt flux can reach 80% when it is roasted at 1200 °C for 60 min.
KeywordsAluminum dross Oxidation roasting Thermodynamics Salt flux
Financial support to this project is provided by the National Key R&D Program of China (Grant No. 2017YFC0703105) and the National Natural Science Foundation of China (Grant No. 51304216).
- 3.Schilesinger M E, Aluminium Recycle, 2nd edn. Taylor&Francis, Boka Raton (2013).Google Scholar
- 5.Magyar M J, Kaplan R S, and Makar H V (1980) Experimental processing of salt slags from an aluminum dross furnace (No. BM-RI-8446). Bureau of Mines, Washington, DC (USA).Google Scholar
- 6.Skoch J T, and Collins R L, in Third International Symposium on Recycling of Metals and Engineered Materials, Light Metals: Proceedings of Sessions, TMS Annual Meeting, Warren dale (1995) p 937.Google Scholar
- 9.Beheshti R, Sustainable Aluminum and Iron Production (Doctoral dissertation, KTH Royal Institute of Technology) (2017).Google Scholar
- 10.Yaws C L, The Yaws handbook of vapor pressure: Antoine coefficients. Gulf Professional Publishing (2015).Google Scholar
- 11.Ishaque M, Bull Soc Chim France 1 (1952) 127.Google Scholar