Effect of Carbon on the Microstructure and Mechanical Properties in Wire Rods Used for the Manufacture of Cold Heading Quality Steels

  • V. Madhuri
  • R. Gobinath
  • G. BalachandranEmail author
Technical Paper

Abstract

Wire rod is an intermediate product, used in the manufacture of cold head quality steel. The quality of the wire rod in the as-hot-rolled condition, was evaluated in a series of carbon steels with and without boron content and at two different wire rod thicknesses. While the effect of boron on hardenability in the hardened and tempered condition is well studied, the effect of boron on the quality in the ferrite–pearlite condition is not well analysed. Hence the present study established that the addition of boron improved strength and ductility in carbon steels compared to steels without boron. The increased strength was attributed to the increased pearlite content and fineness of interlamellar spacing, and the strength was compared with Gladman’s equation and a theoretical equation. The room-temperature flow curve evaluation showed a higher strain hardening exponent in boron-containing steel compared to the steel without it. The upset ratio, which measured the ability of the wire rod for the subsequent wire drawing operation, was found to decrease with carbon content for steels without boron, while it was found to marginally increase in boron-containing steels. The evaluations were substantiated with microstructures evaluated in different grades and thicknesses.

Keywords

Cold head quality Wire rod Boron alloyed Strengthening Flow curve Upset ratio 

References

  1. 1.
    Turner A F, Betteridge C S, and Avery J, Development of Steels for the Fastener and Cold Forging Markets by Testing Under Fastener Production Conditions British Steel Report, Commission of the European Communities EUR 8998 EN. (1984) p 1.Google Scholar
  2. 2.
    Crawford J D, Dunn R G, and Humphrey J H, The Influence of Alloying Elements on the Cold Deformation of Steel, Source Book on Cold Forming, ASM (1964) p 140.Google Scholar
  3. 3.
    Xiaoyu M A, Alan O H, Jim N, Michel H, Nick N, and John J J, ISIJ Int 44 (2004) 905.Google Scholar
  4. 4.
    Maheshwari M D, Dutta B, and Mukherjee T, Quality Requirements for Cold Heading Grades of Steel, Tool & Alloy Steels. (1978) p 247.Google Scholar
  5. 5.
    Antonio A G, Steel Forming and Heat Treating Handbook, McGraw Hill, Sao Paulo (2002).Google Scholar
  6. 6.
    Jennarong T, Vitoon U, and Wolfgang B, J Met Mater Miner 19 (2009) p 29.Google Scholar
  7. 7.
    Yong L G, Xiang X X, and He Y, ISIJ Int 56 (2016) p 619.CrossRefGoogle Scholar
  8. 8.
    Gao Y, Xue X, and Yang H, Crystal 5 (2015) p 592.CrossRefGoogle Scholar
  9. 9.
    Anelli E, Folgarait P, Merigo A, Lianos J M, Zufia A, Kawalla R, and Goldhahn G, New thermomechanically processed wire rod for drawing and cold heading applications (Thermorod), European Comission EUR 21633EN (2005) p 1.Google Scholar
  10. 10.
    Gladman T, The physical metallurgy of microalloyed steels, The Institute of Mater, London (1997).Google Scholar
  11. 11.
    Janusz D, Třinec Z, Tomáš K, Denisa K, and Petra H, Počít Simulace, Výpočet Metody 4 (2009) p 67.Google Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  1. 1.JSW Steel Ltd, Salem WorksMecheri, SalemIndia

Personalised recommendations