Research on Nitrogen Solubility of Fe–Cr–Mn–V–N System Alloys in Liquid and Solid Phases

  • Jian Cheng
  • Houfa Shen
Technical Paper
  • 16 Downloads

Abstract

In this paper, the thermodynamic model of nitrogen solubility in vanadium nitrogen microalloyed high strength weathering steels of Fe–Cr–Mn–V–N system, according to Hillert’s model for Gibbs energy of its various phases, was established and validated. In the model, the effect of the nitrogen partial pressure on the activity coefficient and the lattice structure characteristics of the vanadium nitrogen precipitated phase were considered. It would be of guiding significance for the design and smelting of Fe–Cr–Mn–V–N system alloys. Based on the established model, the nitrogen contents in \(\delta\), \(\gamma\), \(\alpha\) phase and liquid were calculated as a function of the temperature for Fe–Cr–Mn–V–N system alloys. The results show that: first, the maximum solubility of nitrogen in the solidification process is obviously affected by the phase transition when there is a sudden change in the solubility of nitrogen at the phase transition point. The maximum nitrogen solubility of the molten steel in the delta phase region determines whether nitrogen bubbles are formed during the solidification process. The nitrogen solubility is lowest in the solid–liquid region (about 1673 K). Secondly, the increase of Cr and Mn content is beneficial to improve nitrogen solubility in liquid and solid phases. However, the increase of V content mainly affects the nitrogen solubility in the solid phase because the nitrogen in this temperature range is precipitated in the form of vanadium nitride, as the second phase plays a role in strengthening. In addition, the alloying element Mn has a significant effect on nitrogen solubility since the Mn element is the promoting element of austenitic formation. During the solidification process, the delta ferrite region gradually reduces and may disappear with increasing Mn content. Therefore, increasing the Mn content of the alloy system in the design of alloy composition, can reduce the precipitation trend of the nitrogen during the solidification process, which can effectively avoid bubble formation in high nitrogen weathering steels. Lastly, with the increase in the nitrogen partial pressure, the solubility of nitrogen increases during the liquid and solid phases.

Keywords

Thermodynamic model Nitrogen solubility Vanadium nitrogen precipitated phase Fe–Cr–Mn–V–N system alloys 

Notes

Acknowledgements

This work was financially supported by the project of green manufacturing system integration of MIIT China (2016-64).

References

  1. 1.
    Andrew J, Iron and Nitrogen, The Iron and Steel Institute, London, VII (1912).Google Scholar
  2. 2.
    Adcock F, J Iron Steel Inst 114 (1926) 117.Google Scholar
  3. 3.
    Perez N, Electrochemistry and Corrosion Science, Springer, Berlin (2004).Google Scholar
  4. 4.
    Li H B, Jiang Z H, Shen M H, and You X M, J Iron Steel Res Int 14 (2007) 64.CrossRefGoogle Scholar
  5. 5.
    Makaya A, and Fredriksson H, Sci Eng A 413 (2007) 533.Google Scholar
  6. 6.
    Adrian H, Mater Sci Technol 8 (1992) 406.CrossRefGoogle Scholar
  7. 7.
    Kowanda C, Stickstofflöslichkeit in nickel und nickel basis legierungen im schmelzflüssigen zustand unter erhöhtem stickstoffpartialdruck, Zürich (2000).Google Scholar
  8. 8.
    Wang W E, Kim Y S, and Hong H S, J Alloys Compd 308 (2000) 147.CrossRefGoogle Scholar
  9. 9.
    Mancha H, Herrera-Trejo M, García G, Méndez M, and Ablitzer D, Mater Des 17 (1996) 103.CrossRefGoogle Scholar
  10. 10.
    Kunze J, and Rothe I, Steel Res Int 65 (1994) 331.CrossRefGoogle Scholar
  11. 11.
    Qiu C A, Metall Trans A 24 (1993) 629.CrossRefGoogle Scholar
  12. 12.
    Ishii F, Banya S, and Fuwa T, Tetsu- to- Hagane 68 (1982) 81.CrossRefGoogle Scholar
  13. 13.
    Pomarin Y M, Grigorenko G M, and Lakomskiy V I, Russ Metall (1975) 61.Google Scholar
  14. 14.
    Kirchner G, Nishizawa T, and Uhrenius B, Metall. Trans. 4 (1973) 167.CrossRefGoogle Scholar
  15. 15.
    Kobayashi T, Kuwana T, and Kiguchi R, J. Jpn. Weld. Soc. 41 (1972) 308.CrossRefGoogle Scholar
  16. 16.
    Schürmann E, and Kunze H D, Steel Res Int 38 (1967) 585.Google Scholar
  17. 17.
    Dodd R A, and Gokcen N A, Trans. Metall. Soc. Aime 221 (1961) 233.Google Scholar
  18. 18.
    Jiang Z H, Zhu H C, and Li H B, Int Symp Liq Met Process Cast 2015 143 (2016) 12038.Google Scholar
  19. 19.
    Li G Q, Zhang F, and Zhu C Y, J Wuhan Univ Sci Technol Nat Sci Ed 28 (2005) 115.Google Scholar
  20. 20.
    Fast J D, and Verrijp M B, Acta Metall 3 (1955) 203.CrossRefGoogle Scholar
  21. 21.
    Åatröm HU, and Borelius G, Acta Metall 2 (1954) 547.CrossRefGoogle Scholar
  22. 22.
    Qiu C A, Metall Trans A 24 (1993) 2393.CrossRefGoogle Scholar
  23. 23.
    Zheng X H, Nitrogen solubility in iron-base alloys and powder metallurgy of high nitrogen stainless steels (1991).Google Scholar
  24. 24.
    Kunze J, Brož P, Sopoušek J, and Gruner W, Steel Res Int 67 (1996) 26.CrossRefGoogle Scholar
  25. 25.
    Coutsouradis D, Materials for advanced power engineering 1994: proceedings of a conference held in Liège, Belgium, 3–6 October 1994, Springer (1994).Google Scholar
  26. 26.
    Ghali S, J Metall 2014 (2014).Google Scholar
  27. 27.
    Pehlke R D, and Elliott JF, Trans Am Inst Min Metall Eng 218 (1960) 1088.Google Scholar
  28. 28.
    Feichtinger H, Zheng X H, and Rennhard C, Steel Res Int 61 (1990) 26.CrossRefGoogle Scholar
  29. 29.
    Grigorenko G M, and Pomarin Y M, Nitrogen and Hydrogen in Molten Metals and Alloys, CRC Press, Boca Raton (1990).Google Scholar
  30. 30.
    Chen J X, Handbook of Diagram and Data of Steelmaking, Metallurgical Industry Press, Beijing (1984).Google Scholar
  31. 31.
    Satirkolorz A H, and Feichtinger H K, Zeitschrift Fur Metallkunde 82 (1991) 689.Google Scholar
  32. 32.
    Chipman J, and Corrigan D A, Trans Metall Soc AIME 233 (1965) 1249.Google Scholar
  33. 33.
    Hillert M, and Staffansson L I, Acta Chem Scand 24 (1970) 3618.Google Scholar
  34. 34.
    Balachandran G, High Nitrogen Steels and Stainless Steelsmanuf Acturing, Properties and Applications, Alpha Science International Ltd, Pangbourne (2004) p 40.Google Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  1. 1.The State Key Laboratory of Refractories and MetallurgyWuhan University of Science and TechnologyWuhanChina
  2. 2.Key Laboratory for Advanced Materials Processing Technology, Ministry of Education, School of Materials Science and EngineeringTsinghua UniversityBeijingChina

Personalised recommendations