Variation of Nano Ce Content in Austempered Ductile Iron (ADI) Weld Metal and Its Effects on Microstructure

  • Tapan Sarkar
  • Tapan Kumar Pal
  • Akshay Kumar Pramanick
Technical Paper
  • 61 Downloads

Abstract

In the present study, four numbers of coated electrode were developed with and without addition of nano Ce content for welding ductile iron and convert to austempered ductile iron after isothermal heat treatment. Ce contents were varied with three different levels, i.e. 0.05, 0.1, 0.2 wt% to understand the effect of Ce content in the weld metal with respect to microstructural properties. Defect-free welds were established by applying preheat and then post weld heat treatment immediately after welding. Austenitization was done at 900 °C for 2 h and austempering at 300 and 350 °C for three different holding time. Microstructural constituents were varied by varying the Ce content in weld metals. The optimum amount of Ce content to refine the microstructure before and after austempering shows a significant effect in the austempering kinetics. Among all three levels of Ce content, 0.1 wt% was considered as the optimum level with respect to microstructural constituents and hardness.

Keywords

Electrode development Cerium oxide Isothermal heat treatment Microstructure XRD analysis Microhardness 

Notes

Acknowledgement

The cooperation received from Dr. Goutam Das, Senior Principal Scientist, National Metallurgical Laboratory (SEM analysis) is gratefully acknowledged.

References

  1. 1.
    Putatunda S K, Mater Sci and Eng A 315 (2001) 70.CrossRefGoogle Scholar
  2. 2.
    Bartosiewicz L, Krause A R, Alberts F A, Iqbal Singh, Putatunda S K, Mater Charact 30 (1993) 22l.Google Scholar
  3. 3.
    Putatunda S K, Rao P P, Metall Mater Trans 28 (1997) 1457.CrossRefGoogle Scholar
  4. 4.
    Eric O, Sidjanin L, Miskovic Z, Zec S, Jovanovic M T, Mater Lett 58 (2004) 2707.CrossRefGoogle Scholar
  5. 5.
    Kovacs B V, Mod Cast., 80 (1990) 38.Google Scholar
  6. 6.
    El-Kashif E, Morsy M A, N Y Sci J 4 (2011) 21.Google Scholar
  7. 7.
    Putatunda S K, Gadicherla P K, Mater Sci Eng A 268 (1999) 15.CrossRefGoogle Scholar
  8. 8.
    Thomson R C, James J S, Putman D C, Mater Sci Technol 16 (2000) 1412.CrossRefGoogle Scholar
  9. 9.
    Borrajo J M, Martinez R A, Boeri R E, Sikora J A, ISIJ Int 42 (2002) 257.CrossRefGoogle Scholar
  10. 10.
    Ramadana M, Nofal A A, Elmahalawi I, Abdel-Karim R, Mater Sci Eng A 435–436 (2006) 564.CrossRefGoogle Scholar
  11. 11.
    El-Banna E M, Nageda M M, El-Saadat Abo, Mater Lett 42 (2000) 311.CrossRefGoogle Scholar
  12. 12.
    Pascual M, Ferrer C, Rayon E, Revista de Metal 45 (2009) 334.CrossRefGoogle Scholar
  13. 13.
    Veselko J, Mesko J, Pleva J, Racz G, Weld Int 7 (1993) 914.CrossRefGoogle Scholar
  14. 14.
    Sytnik N M Avt Svarka 5 (1982) 74.Google Scholar
  15. 15.
    Sun D Q, Gu X Y, Lui W H, Xuan Z Z, Mater Sci Eng A 402 (2015) 402.Google Scholar
  16. 16.
    McLuhan T K, Mode Cast 52 (1967) 80.Google Scholar
  17. 17.
    Liu H, Zheng D H, Xu Z Y, Journal of Rare Earth, 10 (1992) 189.Google Scholar
  18. 18.
    Liang Y, Yi Y, Long S, Tan Q, JMEPEG 23 (2014) 4251.CrossRefGoogle Scholar
  19. 19.
    El-Banna E M, Mater Lett 41 (1999) 20.CrossRefGoogle Scholar
  20. 20.
    Gonzalez R C, Richard E W, Digital Image Processing Second Edition, Beijing publishing house of Electronics Industry (2005) p 208.Google Scholar
  21. 21.
    Cullity B D, Elements of X-ray Diffraction, Addison-Wesley Publishing Company Reading MA (1978) p 411.Google Scholar
  22. 22.
    Roberts C S, Trans AIME 197 (1982) 203.Google Scholar
  23. 23.
    Lu A L, Yoo S Y, Pense A W, Weld J 67 (1988) 178.Google Scholar
  24. 24.
    Ruizhen G, Hangi H, Zueyoy Z, Proceedings of the International Conference on Rare Earth Developments and Applications, Beijing (1985) 1277.Google Scholar
  25. 25.
    Diao X, Ning Z, Cao F, Sun J, Int J Mod Phys B 23 (2009) 1853.Google Scholar
  26. 26.
    Rees G I, Bhadeshia H K D H, Mater Sci Technol 8 (1992) 985.CrossRefGoogle Scholar
  27. 27.
    Rao P P, Putatunda S K, Metall Mater Trans A 28 (1997)1457.CrossRefGoogle Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  • Tapan Sarkar
    • 1
  • Tapan Kumar Pal
    • 1
  • Akshay Kumar Pramanick
    • 1
  1. 1.Metallurgical and Material Engineering Department, Welding Technology CentreJadavpur UniversityKolkataIndia

Personalised recommendations