Effect of melting temperature on microstructural evolutions, behavior and corrosion morphology of Hadfield austenitic manganese steel in the casting process
- 5 Downloads
In this study, the effect of melting temperature on the microstructural evolutions, behavior, and corrosion morphology of Hadfield steel in the casting process is investigated. The mold was prepared by the sodium silicate/CO2 method, using a blind riser, and then the desired molten steel was obtained using a coreless induction furnace. The casting was performed at melting temperatures of 1350, 1400, 1450, and 1500°C, and the cast blocks were immediately quenched in water. Optical microscopy was used to analyze the microstructure, and scanning electron microscopy (SEM) and X-ray diffractrometry (XRD) were used to analyze the corrosion morphology and phase formation in the microstructure, respectively. The corrosion behavior of the samples was analyzed using a potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS) in 3.5wt% NaCl. The optical microscopy observations and XRD patterns show that the increase in melting temperature led to a decrease of carbides and an increase in the austenite grain size in the Hadfield steel microstructure. The corrosion tests results show that with increasing melting temperature in the casting process, Hadfield steel shows a higher corrosion resistance. The SEM images of the corrosion morphologies show that the reduction of melting temperature in the Hadfield steel casting process induced micro-galvanic corrosion conditions.
KeywordsHadfield steel casting process melting temperature microstructural evolutions corrosion behavior corrosion morphology
Unable to display preview. Download preview PDF.
- S.F. Gnyusov, V.P. Rotshtein, A.E. Mayer, E.G. Astafurova, V.V. Rostov, A.V. Gunin, and G.G. Maier, Comparative study of shock–wave hardening and substructure evolution of 304L and Hadfield steels irradiated with a nanosecond relativistic high–current electron beam, J. Alloys Compd., 714(2017), p. 232.CrossRefGoogle Scholar
- A.K. Srivastava, K. Das, and S.K. Toor, Corrosion behaviour of TiC–reinforced Hadfield manganese austenitic steel matrix in–situ composites, Open J. Met. 5(2015), No. 2, p. 11.Google Scholar
- S. Hofer, M. Hartl, G. Schestak, R. Schneider, E. Arenholz, and L. Samek, Comparison of austenitic high–Mn–steels with different Mn–and C–contents regarding their processing properties, BHM Berg–Huttenmann. Monatsh., 156(2011), No. 3, p. 99.Google Scholar
- S.M. Anijdan, M. Sabzi, M. Ghobeiti–Hasab, and A. Roshan–Ghiyas, Optimization of spot welding process parameters in dissimilar joint of dual phase steel DP600 and AISI 304 stainless steel to achieve the highest level of shear–tensile strength, Mater. Sci. Eng. A, 726(2018), p. 120.CrossRefGoogle Scholar
- S.H.M. Anijdan and M. Sabzi, The evolution of microstructure of an high Ni HSLA X100 forged steel slab by thermomechanical controlled processing, [in] TMS Annual Meeting & Exhibition, Cham, 2018, p. 145.Google Scholar
- M. Sabzi, A. Obeydavi, and S.H.M. Anijdan, The effect of joint shape geometry on the microstructural evolution, fracture toughness, and corrosion behavior of the welded joints of a Hadfield steel, Mech. Adv. Mater. Struct., (2018), p. 1. https://doi.org/10.1080/15376494.2018.1430268.Google Scholar
- S. Hosseini and M.B. Limooei, Optimization of heat treatment to obtain desired mechanical properties of high carbon Hadfield steels, World Appl. Sci. J., 15(2011), No. 10, p. 1421.Google Scholar
- S. Hosseini, M.B. Limooei, M.H. Zade, E. Askarnia, and Z. Asadi, Optimization of heat treatment due to austenising temperature, time and quenching solution in Hadfield steels, Int. J. Chem. Mol. Nucl. Mater. Metall. Eng., 7(2013), No. 7, p. 582.Google Scholar
- T.R. Tamilarasan, U. Sanjith, M.S. Shankar, and G. Rajagopal, Effect of reduced graphene oxide (rGO) on corrosion and erosion–corrosion behaviour of electroless Ni−P coatings, Wear, 390 (2017), p. 385.Google Scholar
- M.L.C. Lim, R.G. Kelly, and J.R. Scully, Overview of intergranular corrosion mechanisms, phenomenological observations, and modeling of AA5083, Corros. Sci., 72(2016), No. 2, p. 198.Google Scholar