Aging behavior of a copper-bearing high-strength low-carbon steel
- 11 Downloads
The effects of aging temperature and time on the hardness and impact toughness of a copper-bearing high-strength low-carbon steel were investigated. The hardness of the aged samples reached maxima after 1 h and 5 h of aging at 500 and 450°C, respectively; this increase in hardness was followed by a decrease in hardness until a temperature of 700°C, at which secondary hardening was observed. The impact toughness of the aged steel was found to be higher for 5 h of aging. Transmission electron microscopy confirmed the presence of carbide and copper precipitates; also, the secondary hardening could be the result of the transformation of austenite (formed in the aging treatment) to martensite. Differential scanning calorimetry of the steel was performed to better understand the precipitation behavior. The results revealed that the precipitation of the steel exhibited two significant stages of copper precipitate nucleation and coarsening of the precipitates, with corresponding activation energies of 49 and 238 kJ·mol−1, respectively.
Keywordsaging treatment BA-160 steel differential scanning calorimetry precipitation
Unable to display preview. Download preview PDF.
- N. Maruyama, M. Sugiyama, T. Hara, and H. Tamehiro, Precipitation and phase transformation of copper particles in low alloy ferritic and martensitic steels, Mater. Trans., JIM, 40(1999), No. 4, p. 268.Google Scholar
- A.N. Bhagat, S.K. Pabi, S. Ranganathan, and O.N. Mohanty, Aging behaviour in copper bearing high strength low alloy steels, ISIJ Int., 44(2004), No. 1, p. 115.Google Scholar
- NAVSEA Thechnical Publication, Base Materials for Critical Applications: Requirements for Low Aalloy Steel Plate, Forgings, Castings, Shapes, Bars, and Heads of HY-80/100/130 and HSLA-80/100, T9074-BD-GIB-010/0300 (REV. 2), 2012.Google Scholar
- W.S. Li, H.Y. Gao, Z.Y. Li, H. Nakashima, S. Hata, and W.H. Tian, Effect of lower bainite/martensite/retained austenite triplex microstructure on the mechanical properties of a low-carbon steel with quenching and partitioning process, Int. J. Miner. Metall. Mater., 23(2016), No. 3, p. 303.CrossRefGoogle Scholar