Soldering of Zr-based bulk metallic glass and copper by Au–12Ge eutectic alloy

  • Jun WangEmail author
  • Jing Cui
  • Hong-Chao Kou
  • Heng Guan
  • Jin-Shan Li
Article
  • 141 Downloads

Abstract

Zr-based bulk metallic glass and copper with different surface roughness were soldered using low temperature eutectic Au–12Ge (wt%) solder on a thermomechanical simulator. The cross-sectional microstructures of the brazed joints were analyzed by scanning electron microscopy (SEM) and transmission electron microscope (TEM) in detail, and the compositional distribution along the interface was analyzed by energy-dispersive spectrometer (EDS). Results show that the surface roughness of base metals plays an important role in the quality of the brazed joint because the surface roughness can enlarge the effective contact area, which can improve the brazing surface quality between two materials. A moderate roughness of treated Zr-based metallic glass of 18 μm is shown to be the best for the soldering, while the surface roughness has a weak effect on the soldering behavior of Au–12Ge solder on copper. After soldering, long-range diffusion of atoms occurs between the base metal and solder, and five distinct regions are formed at the joint region.

Keywords

Bulk metallic glass Soldering Au–Ge eutectic alloy Interface 

Notes

Acknowledgments

This work was financially supported by the Natural Science Basic Research Plan in Shaanxi Province of China (No. 2014JM6234), the Specialized Research Fund for Doctoral Program of Higher Education (No. 20136102120007) and the Program of Introducing Talents of Discipline to Universities (No. B08040).

References

  1. [1]
    Trexler MM, Thadhani NN. Mechanical properties of bulk metallic glasses. Prog Mater Sci. 2010;55(8):759.CrossRefGoogle Scholar
  2. [2]
    Schroers J. Processing of bulk metallic glass. Adv Mater. 2010;22(14):1566.CrossRefGoogle Scholar
  3. [3]
    Wang WH, Dong C, Shek CH. Bulk metallic glasses. Mater Sci Eng R. 2004;44(2–3):45.Google Scholar
  4. [4]
    Wu H, Liu Y, Lik Y, Zhao ZW. Casting effect on compressive brittleness of bulk metallic glass. Trans Nonferrous Met Soc China. 2014;24(2):385.CrossRefGoogle Scholar
  5. [5]
    Zhang Y, Zhao DQ, Pan MX, Wang WH. Glass forming properties of Zr-based bulk metallic alloys. J Non-Cryst Solids. 2003;315(1–2):206.CrossRefGoogle Scholar
  6. [6]
    Lou H, Wang X, Xu F, Ding S, Cao Q, Hono K. 73 mm-diameter bulk metallic glass rod by copper mould casting. Appl Phys Lett. 2011;99(5):051910.CrossRefGoogle Scholar
  7. [7]
    Chiba A, Kawamura Y, Nishida M, Yamamuro T. Explosive welding of ZrTiCuNiBe bulk metallic glass to crystalline Cu plate. Mater Sci Forum. 2011;673:119.CrossRefGoogle Scholar
  8. [8]
    Liu WD, Liu KX, Chen QY, Wang JT, Yan HH, Li XJ. Metallic glass coating on metals plate by adjusted explosive welding technique. Appl Surf Sci. 2009;255(23):9343.CrossRefGoogle Scholar
  9. [9]
    Tariq NH, Shakil M, Hasan BA, Akhter JI, Haq MA, Awan NA. Electron beam brazing of Zr62Al13Ni7Cu18 bulk metallic glass with Ti metal. Vacuum. 2014;101:98.CrossRefGoogle Scholar
  10. [10]
    Kim J, Kawamura Y. Electron beam welding of Zr-based BMG/Ni joints: effect of beam irradiation position on mechanical and microstructural properties. J Mater Process Technol. 2008;207(1–3):112.CrossRefGoogle Scholar
  11. [11]
    Kawamura Y. Liquid phase and supercooled liquid phase welding of bulk metallic glasses. Mater Sci Eng A. 2004;375–377:112.CrossRefGoogle Scholar
  12. [12]
    Wang G, Huang YJ, Makhanlall D, Shen J. Friction joining of Ti40Zr25Ni3Cu12Be20 bulk metallic glass. J Mater Process Technol. 2012;212(9):1850.CrossRefGoogle Scholar
  13. [13]
    Shin HS, Park JS, Yokoyama Y. Dissimilar friction welding of tubular Zr-based bulk metallic glasses. J Alloys Compd. 2010;504(S):S275.CrossRefGoogle Scholar
  14. [14]
    Shin HS. Tool geometry effect on the characteristics of dissimilar friction stir spot welded bulk metallic glass to light weight alloys. J Alloys Compd. 2014;586(S):S50.CrossRefGoogle Scholar
  15. [15]
    Li FP, Zhang DC, Luo ZC, Tan CG, Lin JG. Microstructure and mechanical properties of friction stir welded joint of Zr46Cu46Al18 bulk metallic glass with pure aluminum. Mater Sci Eng A. 2013;588:196.CrossRefGoogle Scholar
  16. [16]
    Chen HY, Cao J, Song XG, Si GD, Feng JC. Pre-friction diffusion hybrid bonding of Zr55Cu30Ni5Al10 bulk metallic glass. Intermetallics. 2013;32:30.CrossRefGoogle Scholar
  17. [17]
    Sun LL, Wang J, Kou HC, Tan BG, Li JS, Zhang PX. Interface characteristics of a Zr-based BMG/copper laminated composite. Surf Interface Anal. 2014;46(2):61.CrossRefGoogle Scholar
  18. [18]
    Kuo PH, Wang SH, Liaw PK, Fan GJ, Tsang HT, Qiao D. Bulk-metallic glasses joining in a supercooled-liquid region. Mater Chem Phys. 2010;120(2–3):532.CrossRefGoogle Scholar
  19. [19]
    Li GZ, Tang HP, Zhang WY, Li G, Yu LL, Li YN. Fabrication of multilayer Nb2O5 nanoporous film by anodization of niobium foils. Rare Met. 2015;34(2):77.CrossRefGoogle Scholar
  20. [20]
    Zhang LY, Shen P, Qi Y, Jiang QC. Wettability in reactive Sn-base alloy/Ni-base metallic glass systems. Appl Surf Sci. 2013;276:424.CrossRefGoogle Scholar
  21. [21]
    Shen P, Yang J, Yin Z, Sun J, Jiang Q. Wetting of amorphous and nanocrystalline Ni75B15Si10 substrates by molten Sn. Surf Interface Anal. 2013;45(4):854.CrossRefGoogle Scholar
  22. [22]
    Ma GF, Zhang HF, Li H, Hu ZQ. Influence of structural relaxation on wetting behavior of molten In–Sn alloy on Cu40Zr44Al8Ag8 bulk metallic glass. J Alloys Compd. 2012;513:273.CrossRefGoogle Scholar
  23. [23]
    Jacobson DM, Humpston G. Gold coatings for fluxless soldering. Gold Bull. 1989;22(1):9.CrossRefGoogle Scholar
  24. [24]
    Leinenbach C, Valenza F, Giuranno D, Elsener H, Jin S, Novakovic R. Wetting and soldering behavior of eutectic Au–Ge alloy on Cu and Ni substrates. J Electron Mater. 2011;40(7):1533.CrossRefGoogle Scholar
  25. [25]
    Humpston G, Jaobson DM. Principles of Soldering. Ohio: Materials Park, ASM International; 2004. 118.Google Scholar
  26. [26]
    Rosenblum M, Spaepen F, Turnabull D. Diffusion and structural relaxation in compositionally modulated amorphous metal films. Appl Phys Lett. 1980;37(2):184.CrossRefGoogle Scholar

Copyright information

© The Nonferrous Metals Society of China and Springer-Verlag Berlin Heidelberg 2016

Authors and Affiliations

  1. 1.State Key Laboratory of Solidification ProcessingNorthwestern Polytechnical UniversityXi’anChina

Personalised recommendations