Microstructure Analysis of the Pack Cementation Aluminide Coatings Modified by CeO2 Addition

  • Hamid Zahedi
  • Farhad Shahriari NogoraniEmail author
  • Mahdi Safari
Article
  • 20 Downloads

Abstract

Minor additions of reactive elements (Y, Ce, Hf, etc.) can improve the oxidation behavior of high temperature alloys and coatings such as aluminide coatings. In the current investigation cerium-modified aluminide coatings were developed via additions of CeO2 to the powder mixture of high activity pack cementation aluminizing. Nickel-based substrates were aluminized at 750 °C and then diffusion annealed at 1080 °C. Microstructure of the coatings was studied using scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction. The results were compared with the characterization results of specimens achieved by aluminizing an electrodeposited Ni–CeO2 interlayer at 1030 °C. The coatings modified by CeO2 addition to the pack showed a dense Al-rich NiAl surface layer with cerium distributed in the coating, however, the coatings modified by Ni–CeO2 interlayer revealed a porous Ni-rich aluminide layer containing CeO2 particles. Increasing the CeO2 content of the pack decreased the thickness of the final coating, but the presence of CeO2 particles in the interlayer increased the thickness of the final aluminide coating. The observed microstructural features were explained using thermodynamic analysis of equilibrium concentration of the involved gaseous species.

Graphic Abstract

Keywords

Cerium oxide Aluminide coating Formation mechanism Reactive element Microstructure Thermodynamics 

Notes

Acknowledgements

This research was supported by Iran National Science Foundation (INSF, Grant No. 90007122). The authors appreciate Department of Materials Science and Engineering, Shiraz University of Technology for provision of laboratory equipment.

References

  1. 1.
    S. Hamadi, M.-P. Bacos, M. Poulain, A. Seyeux, V. Maurice, P. Marcus, Oxidation resistance of a Zr-doped NiAl coating thermochemically deposited on a nickel-based superalloy. Surf. Coat. Technol. 204, 756–760 (2009)CrossRefGoogle Scholar
  2. 2.
    X. Peng, Y. Guan, Z. Dong, C. Xu, F. Wang, A fundamental aspect of the growth process of alumina scale on a metal with dispersion of CeO2 nanoparticles. Corros. Sci. 53, 1954–1959 (2011)CrossRefGoogle Scholar
  3. 3.
    Y. Zhou, X. Zhao, C. Zhao, W. Hao, X. Wang, P. Xiao, The oxidation performance for Zr-doped nickel aluminide coating by composite electrodepositing and pack cementation. Corros. Sci. 123, 103–115 (2017)CrossRefGoogle Scholar
  4. 4.
    L. Qian, F. Xu, K.T. Voisey, V. Nekouie, Z. Zhou, V.V. Silberschmidt, X. Hou, Incorporation and evolution of ZrO2 nano-particles in Pt-modified aluminide coating for high temperature applications. Surf. Coat. Technol. 311, 238–247 (2017).  https://doi.org/10.1016/j.surfcoat.2016.12.106 CrossRefGoogle Scholar
  5. 5.
    X. Tan, X. Peng, F. Wang, The mechanism for self-formation of a CeO2 diffusion barrier layer in an aluminide coating at high temperature. Surf. Coat. Technol. 224, 62–70 (2013)CrossRefGoogle Scholar
  6. 6.
    Y.B. Zhou, H.T. Hu, H.J. Zhang, Oxidation behavior of aluminide coatings on carbon steel with and without electrodeposited Ni–CeO2 film by low-temperature pack cementation. Vacuum 86, 210–217 (2011)CrossRefGoogle Scholar
  7. 7.
    J. Wen, L. Yang, L. Zhu, J. Zhang, Q.-A. Li, A study on the growth kinetics of CeO2-modified aluminide coating and its computer fitting. Mater. Sci. Eng., A 499, 123–125 (2009).  https://doi.org/10.1016/j.msea.2007.11.139 CrossRefGoogle Scholar
  8. 8.
    M. Safari, F.S. Nogorani, Formation mechanism of high activity aluminide coating on Ni–CeO2 coated Rene 80 alloy. Surf. Coat. Technol. 329, 218–223 (2017)CrossRefGoogle Scholar
  9. 9.
    B.M. Warnes, Reactive element modified chemical vapor deposition low activity platinum aluminide coatings. Surf. Coat. Technol. 146–147, 7–12 (2001)CrossRefGoogle Scholar
  10. 10.
    C. Metz, G. Wahl, P. Bianchi, M. lnnocenti, D. Baxter, N. Archer, R. Wing, Yttrium containing aluminide layers. J. Phys. 4(11), Pr3-869–Pr3-876 (2001). https://doi.org/10.1051/jp4:20013108
  11. 11.
    J. Romanowska, M. Zagula-Yavorska, J. Sieniawski, J. Markowski, Zirconium modified aluminide coatings obtained by the CVD and PVD methods. Open J. Met. 3, 92–99 (2013).  https://doi.org/10.4236/ojmetal.2013.34014 CrossRefGoogle Scholar
  12. 12.
    Q. Fan, H. Yu, T.-G. Wang, Z. Wu, Y. Liu, Preparation and isothermal oxidation behavior of zr-doped, pt-modified aluminide coating prepared by a hybrid process. Coating 8(1), 1–12 (2018)CrossRefGoogle Scholar
  13. 13.
    Y.-Q. Wang, M. Suneson, G. Sayre, Synthesis of Hf-modified aluminide coatings on Ni-base superalloys. Surf. Coat. Technol. 206, 1218–1228 (2011).  https://doi.org/10.1016/j.surfcoat.2011.08.031 CrossRefGoogle Scholar
  14. 14.
    M. Mobin, H.K. Sharma, S.K. Hasan, High temperature oxidation behaviour of CeO2 and La2O3 modified aluminide coatings on carbon steel. Anti-Corros. Method. Mater. 49, 283–294 (2002)CrossRefGoogle Scholar
  15. 15.
    Z. Haijun, S. Jianfeng, Fabrication and cyclic oxidation of Y2O3/CeO2-modified low temperature aluminide coatings. R. Metal Mater. Eng. 46, 301–306 (2017)CrossRefGoogle Scholar
  16. 16.
    R. Bianco, R.A. Rapp, Pack cementation aluminide coatings on superalloys: codeposition of Cr and reactive elements. J. Electrochem. Soc. 140, 1181–1190 (1993)CrossRefGoogle Scholar
  17. 17.
    X. Zhao, C. Zhou, Effect of Y2O3 content in the pack on microstructure and hot corrosion resistance of Y-Co-modified aluminide coating. Corros. Sci. 86, 223–230 (2014).  https://doi.org/10.1016/j.corsci.2014.05.018 CrossRefGoogle Scholar
  18. 18.
    T. Zhang, Y. Luo, D.Y. Li, Erosion behavior of aluminide coating modified with yttrium addition under different erosion conditions. Surf. Coat. Technol. 126, 102–109 (2000)CrossRefGoogle Scholar
  19. 19.
    H. Ahmadi, D.Y. Li, Mechanical and tribological properties of aluminide coating modified with yttrium. Surf. Coat. Technol. 161, 210–217 (2002)CrossRefGoogle Scholar
  20. 20.
    Z.D. Xiang, P.K. Datta, Formation of Hf- and W-modified aluminide coatings on nickel—base superalloys by the pack cementation process. Mater. Sci. Eng., A 363, 185–192 (2003)CrossRefGoogle Scholar
  21. 21.
    G.N. Angelopoulos, N. Voudouris, N. Maragoudakis, J.K. Kiplagat, D. Tsipas, Modifying Cr–Al coatings by reactive element additions: experimental and theoretical considerations. Mater. Manuf. Process. 15, 605–620 (2000).  https://doi.org/10.1080/10426910008913008 CrossRefGoogle Scholar
  22. 22.
    M. Fukumoto, T. Suzuki, M. Hara, T. Narita, Effect of the electrodeposition temperature on the cyclic-oxidation resistance of Ni aluminide containing Zr formed by molten-salt electrodeposition. Mater. Trans. 50, 335–340 (2009)CrossRefGoogle Scholar
  23. 23.
    J.M. Brossard, B. Panicaud, J. Balmain, G. Bonnet, Modeling of aluminized coating growth on nickel. Acta Mater. 55, 6586–6595 (2007)CrossRefGoogle Scholar
  24. 24.
    D.K. Das, V. Singh, S.V. Joshi, Evolution of aluminide coating microstructure on nickel-base cast superalloy CM-247 in a single-step high-activity aluminizing process. Metall. Mater. Trans. 29A, 2173–2188 (1998)CrossRefGoogle Scholar
  25. 25.
    Z.D. Xiang, J.S. Burnell-Gray, P.K. Datta, Aluminide coating formation on nickel-base superalloys by pack cementation process. J. Mater. Sci. 36, 5673–5682 (2001)CrossRefGoogle Scholar
  26. 26.
    G.W. Goward, D.H. Boone, Mechanisms of formation of diffusion aluminide coatings on nickel-base superalloys. Oxid. Met. 3, 475–495 (1971)CrossRefGoogle Scholar
  27. 27.
    S.R. Levine, R.M. Caves, Thermodynamics and kinetics of pack aluminide coating formation on IN-100. J. Electrochem. Soc. 121, 1051–1064 (1974)CrossRefGoogle Scholar
  28. 28.
    C. Xu, X. Peng, F. Wang, Cyclic oxidation of an ultrafine-grained and CeO2-dispersed and #x03B4;-Ni2Al3 coating. Corros. Sci. 52, 740–747 (2010)CrossRefGoogle Scholar
  29. 29.
    X. Wang, X. Peng, X. Tan, F. Wang, The reactive element effect of ceria particle dispersion on alumina growth: a model based on microstructural observations. Sci Rep-UK 6, 29593 (2016).  https://doi.org/10.1038/srep29593 CrossRefGoogle Scholar
  30. 30.
    R. Sen, S. Das, K. Das, Synthesis and properties of pulse electrodeposited Ni–CeO2 nanocomposite. Metall. Mat. Trans. 43A, 3809–3823 (2012)CrossRefGoogle Scholar
  31. 31.
    X. Zhou, Y. Shen, Beneficial effects of CeO2 addition on microstructure and corrosion behavior of electrodeposited Ni nanocrystalline coatings. Surf. Coat. Technol. 235, 433–446 (2013)CrossRefGoogle Scholar
  32. 32.
    T. Watanabe, Nano Plating-Microstructure Formation Theory of Plated Films and a Database of Plated Films (Elsevier Science, Amsterdam, 2004)Google Scholar
  33. 33.
    A. Paul, A.A. Kodentsov, F.J.J. Van Loo, On diffusion in the and #x03B2;-NiAl phase. J. Alloy. Compd. 403, 147–153 (2005)CrossRefGoogle Scholar

Copyright information

© The Korean Institute of Metals and Materials 2019

Authors and Affiliations

  1. 1.Department of Materials Science and EngineeringShiraz University of TechnologyShirazIran

Personalised recommendations