A Study on the Formation Mechanism of the Interfacial Layer Between Solid CaO and Molten Iron Alloys

  • Sunghee Lee
  • Dong Joon MinEmail author
Article

Abstract

The present study aims to clarify the formation mechanism of the interfacial layer between solid CaO and molten iron through SEM–EDS analysis. The interfacial layer formed between CaO and molten iron is observed by SEM–EDS for different compositions of molten iron (CaO/Fe–C–S interface: CaS layer; CaO/Fe–C–Si–S interface: CaS and Ca2SiO4 layers; CaO/Fe–C–Si interface: no interfacial layer; CaO/Fe–S–Si interface: Ca2SiO4 and CaS layers). The effect of S and Si concentrations on layer formation is discussed using the following proposed mechanism.
$$ {\text{CaO}}\left( s \right) + \underline{\text{S}} = {\text{CaS}}\left( s \right) + \frac{1}{2}{\text{O}}_{2} $$
$$ 2{\text{CaO}}\left( s \right) + \underline{\text{Si}} + {\text{O}}_{2} = {\text{Ca}}_{2} {\text{SiO}}_{4} \left( s \right) $$
In the case of the Fe–C–Si–Al–S/CaO interface, CaS and Ca3Al2O6 layers are observed. The formation mechanism of a reaction layer for Al-containing iron melts is also proposed as below.
$$ {\text{CaO}}\left( s \right) + \underline{\text{S}} = {\text{CaS}}\left( s \right) + \frac{1}{2}{\text{O}}_{2} $$
$$ 3{\text{CaO}}\left( s \right) + \underline{{2{\text{Al}}}} + \frac{3}{2}{\text{O}}_{2} = {\text{Ca}}_{3} {\text{Al}}_{2} {\text{O}}_{6} \left( {\text{s}} \right) $$

Keywords

Calcia Dicalcium silicate Calcium sulfide Desulfurization 

Notes

Acknowledgements

The study was supported by the Korea Evaluation Institute of Industrial Technology project no. 10076604.

References

  1. 1.
    J. Niedringhaus, R. Fruehan, Metall. Mater. Trans. B 19, 261 (1988)CrossRefGoogle Scholar
  2. 2.
    F. Oeters, Metallurgie der Stahlherstellung (Springer, Berlin, 2012)Google Scholar
  3. 3.
    D. Boyd, W. Phelps, M. Hepworth, Metall. Mater. Trans. B 6, 87 (1975)CrossRefGoogle Scholar
  4. 4.
    E. Turkdogan, L. Msartonik, Trans. Iron Steel Inst. Jpn. 23, 1038 (1983)CrossRefGoogle Scholar
  5. 5.
    Y. Kawai, K. Mori, Y. San-nomiya, Tetsu-to-Hagané 61, 29 (1975)CrossRefGoogle Scholar
  6. 6.
    T. Mitsuo, T. Shoji, Y. Hatta, H. Ono, H. Mori, T. Kai, Trans. Jpn. Inst. Met. 23, 768 (1982)CrossRefGoogle Scholar
  7. 7.
    H.-J. Visser, R. Boom, ISIJ Int. 46, 1771 (2006)CrossRefGoogle Scholar
  8. 8.
    D. Lindström, P. Nortier, D. Sichen, Steel Res. Int. 85, 76 (2014)CrossRefGoogle Scholar
  9. 9.
    E.T. Turkdogan, Physical Chemistry of High Temperature Technology (Academic Press, New York, NY, 1980)Google Scholar
  10. 10.
    Q. Han, X. Zhang, D. Chen, P. Wang, MTB 19, 617 (1988)CrossRefGoogle Scholar
  11. 11.
    S.R. Simeonov, I.N. Ivanchev, A.V. Hainadjiev, ISIJ Int. 31, 1396 (1991)CrossRefGoogle Scholar
  12. 12.
    N.G.S.S.D. Iinkai, Steelmaking Data Sourcebook (Gordon and Breach Science Publishers, New York, 1998)Google Scholar

Copyright information

© The Korean Institute of Metals and Materials 2018

Authors and Affiliations

  1. 1.Department of Material Science and EngineeringYonsei UniversitySeoulRepublic of Korea

Personalised recommendations