Relationship between granulometric distribution and compressive strength of heat-treated Toarcian-Bajocian gypsum, Tunisia: implications for casting teeth in molds

  • Fatma Hassaïri-Krid
  • Mongi Felhi
  • Nabil Fattah
  • Ali TliliEmail author
Original Paper
  • 2 Downloads

Abstract

Toarcian-Bajocian gypsum deposits of the Mestaoua formation (southern part of Tunisia) correspond to very thick gypsum layers. The natural gypsum and their heat-treated products were investigated to assess their utilization in dental field (cast plaster into molds for dental prosthesis). XRD data show that the Mestaoua sample (GMes) constituted of gypsum. However, the commercial product (PXETD) is made up of bassanite. Powder X-ray diffraction combined with chemical and infrared analyses reveals that heat-treated GMes samples at different temperatures (200 °C, 220 °C, 240 °C, 260 °C) are dominantly bassanite with minor amounts of anhydrite, particularly, in the samples heated at 240 °C and 260 °C. The data obtained revealed that the sample heated at 220 °C and 240 °C are distinguished by satisfactory values of compressive strength, which are close to the value observed for a commercial product, and are suitable for use in dentistry. The slight decrease in the compressive strength is commonly due to the less abundant water molecules and the two divergent modes of particle distribution, which enhance pore space. Bulk properties of the sample heated at 240 °C are generally appropriate for use as a material to prepare molds in dental fields, as confirmed by the casting of plaster into mold teeth, where teeth revealed clearly steaks and showed even small details.

Keywords

Gypsum Bassanite Mold teeth Compressive strength Particle distributions 

Notes

Acknowledgments

The authors are thankful to the Engineers of Research Center of Métlaoui for XRD analysis. We thank Abdelfattah Affes for compressive strength measurement and Hafedh Gargouri for laser granulometry analysis. We are very thankful to Mr. Ridha Krid (head of dental prosthesis laboratory) for making autoclave and casting teeth in molds.

Funding information

This work was supported by the “Laboratoire Géoressources, Matériaux, Environnement et Changements Globaux, Département des Sciences de la Terre, Faculté des Sciences, Université de Sfax Tunisie.”

References

  1. Al-Hadad NS, Al-Mandilawi LR, AlDoori DI (2001) Compressive strength of several gypsum products dried by microwave oven with different programs. Iraqi Dent J 28:219–231Google Scholar
  2. Béji-Sassi A (1999) Les phosphates dans les bassins paléogènes de la partie méridionale de l’Axe Nord-Sud (Tunisie). Thèse Doctorat. Etat, Université, Tunisie.Google Scholar
  3. Ben Ali F, Iucolano F, Liguori B, Piscopo D, Marino O, Caputo D (2014) Physical and mechanical characterization of sun-dried bricks. A case history: the galeb of Kebili. Mater Struct 49:159–165CrossRefGoogle Scholar
  4. Ben Ismail M.H (1991) Les bassins mésozoïques (Trias a Aptien) du sud de la Tunisie: Stratigraphie intégrée, caractéristiques géophysiques et évolution géodynamique. Thése 3 2me cycle, p.149-160Google Scholar
  5. Ben Mansour M, Soukaina CA, Benhamou B, Jabrallah SB (2013) Thermal characterization of a Tunisian gypsum plaster as construction material. Energy Procedia 42(68042):6Google Scholar
  6. Bishop JL, Lane M, Dyar MD, King SJ, Brown AJ, Swayze GA (2014) What lurks in the martian rocks and soil investigations of sulfates, phosphates, and perchlorates. Spectral properties of Ca-sulfates: gypsum, bassanite, and anhydrite. Am Mineral 99:2105–2115CrossRefGoogle Scholar
  7. Bouaziz S, Barrier E, Soussi M, Turki MM, Zouari H (2002) Tectonic evolution of the northern African margin in Tunisia from paleostress data and sedimentary record. Tectonophysics. 357:227–253CrossRefGoogle Scholar
  8. Bouaziz S (1995) Etude de la tectonique cassante dans la plateforme et l’atlas saharien (Tunisie Méridionale): évolution des paléochamps de contraintes et implications géodynamiques, thèse 3 éme cycleGoogle Scholar
  9. Bouaziz S (2005) Les matières premières naturelles du gouvernorat de Tataouine: caracterisation et utilisations. ODS, Tunisia, p 285Google Scholar
  10. Bouaziz. S, Sghari. A, Benzina. M, Sdiri. A and Chaabouni. R .,2007. Les matieres premieres naturelles du gouvernorat de Gabes: caracterisation et utilisations. ODS, Tunisia, pp 380Google Scholar
  11. Brindley GW, Brown G (1980) Crystal structures of clay minerals and their X-ray identification. Monograph 5, Mineralogical Society, London, pp197–248Google Scholar
  12. Burollet PF (1956) Contribution à l’étude stratigraphique de la Tunisie centrale. Ann Mines Geol (Tunis) 18 Tunisia, 345 ppGoogle Scholar
  13. Busson G (1967) Le mésozozoiqueque saharien, 1e `re partie: l’extre ˆme Sud tunisien. Edition du C.N.R.S. France. Ser. Geol. 8, 194 ppGoogle Scholar
  14. Camarini G, Pinheiro SMM (2014) Microstructure of recycled gypsum plaster by SEM. Adv Mater Res 912-914:243–246CrossRefGoogle Scholar
  15. Chaffee NR, Bailey JH, Sherrard DJ (1997) Dimensional accuracy of improved dental stone and epoxy resin die materials Part II: complete arch. J Prosthet Dent 77(2):235–238CrossRefGoogle Scholar
  16. Freyer D, Voigt W (2003) Crystallization and phase stability of CaSO4 and CaSO4-based salts. Monatsh Chem/Chem Mon 134:693–719CrossRefGoogle Scholar
  17. Graig RG, Power JM (2002) Restorative dental materials, 11th edn. Mosby Co., Missouri, pp 635–670 392-404Google Scholar
  18. Guan B, Yang L, Wu Z, Shen Z, Ma X, Ye Q (2009) Preparation of a-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl2 solution under mild conditions. Fuel J.7:1286–1293CrossRefGoogle Scholar
  19. Hatim NA, Al-Khayat IK, Abdullah MA (2009) Modification of gypsum products (Part II). The effect of drying methods on the compressive strength and surface hardness of modified gypsum products. Al–Rafidain Dent J 9(2):162–167Google Scholar
  20. Jaoudi M (2004) Les évènements tectoniques du crétacé supérieur dans le secteur méridional de l'Axe Nord–Sud (Tunisie). p 49, 84, 101Google Scholar
  21. Kammoun F, Peybernés B, Ben Youssef M (1987) Analyse biostratigraphie et sédimentologique du jurassique de l’extrême sud-Tunisien (Plateforme saharienne et abords de la chaîne permienne). Revue des sciences de la terre, vol 6. INRST, TunisGoogle Scholar
  22. Karni J, Karni E (1995) Gypsum in construction: origin and properties. Mater Struct 28:92–100CrossRefGoogle Scholar
  23. Kraiem N (2004) Etude comparative du gypse dans les formations évaporitiques Eocène et Jurassique du centre et du Sud de la Tunisie : Essais de fabrication des plâtres. Mastère, F.S.Safx, 85pagesGoogle Scholar
  24. Lewry AJ, Williamson J (1994) The setting of gypsum plaster: part I the hydration of calcium sulphate hemihydrate. J Mater Sci 29:5524–5528CrossRefGoogle Scholar
  25. Macedo Portela da Silva N, Rong Y, Espitalier F, Baillon F, Gaunand A (2017) Solvothermal recrystallization of α-calcium sulfate hemihydrate: batch reactor experiments and kinetic modelling. J Cryst Growth 472:46–53CrossRefGoogle Scholar
  26. Mahmoudi S, Bennour A, Chalwati Y, Souidi K, Thabet M, Srasra E, Zargouni F (2016) Tunisian gypsums: Characteristics and use in cement. J Afr Earth Sci 6(121):267–273CrossRefGoogle Scholar
  27. Pansu M, Gautheyrou J (2006) Handbook of soil analysis mineralogical, organic and inorganic methods. XIX, 993p 183 illus Hardcover. ISBN: 978-3-540-31210-9Google Scholar
  28. Philips RW (1984) Elements of dental materials, 4th edn. W.B.Saunder Co., Philadephia, p 62Google Scholar
  29. Pinheiro S.M.M, Camarini G (2015) Characteristics of gypsum recycling in different cycles IACSIT. International Journal of Engineering and Technology 7:215–216CrossRefGoogle Scholar
  30. Rabizadeh T, Peacock CL, Benning LG (2014) Carboxylic acids: effective inhibitors for calcium sulfate precipitation. Mineral Mag 78(6):1465–1472CrossRefGoogle Scholar
  31. Rejab LT, Al-Hamdani FS, Mohammed Y (2012) Evaluation of some physical properties of die stone made from local raw gypsum material. Al–Rafidain Dent J 12(2):309–315Google Scholar
  32. Schwedhelm ER, Lepe X (1997) Fracture strength of type IV and type V die stone as a function of time. J Prosthet Dent 78(6):554–559CrossRefGoogle Scholar
  33. Sdiri A, Bouaziz S, Sekrafi A (2016) Properties of Mestaoua evaporites (southern Tunisia)for plaster industry. Carbonates Evaporites 32: 195–204CrossRefGoogle Scholar
  34. Siadat A, Shahrokhi R (2007) Gypsum products used in dentistry field. J Prosthet Dent 4:24–50Google Scholar
  35. Skinner EW, Phillip RW (1960) The science of dental materials, 5th edn. W.B.Saunder Co., Philadephia, pp 31–57Google Scholar
  36. Triollier M (1979) Hydratation du sulfate de calcium hémihydraté. Thèse. L’institut National Polytechnique de Grenoble. pp.130Google Scholar
  37. Walter GS (1997) Strength and durability of the cast upon its rate of setting and the subsequent plaster of Paris. J Bone Joint Surg Am 2(4):352–363Google Scholar
  38. Yang L, Wu Z, Guan B, Fu H, Ye Q (2009) Growth rate of a-calcium sulfate hemihydrate in K–Ca–Mg–Cl–H2O systems at elevated temperature. J Cryst Growth 311:4518–4524CrossRefGoogle Scholar

Copyright information

© Saudi Society for Geosciences 2019

Authors and Affiliations

  • Fatma Hassaïri-Krid
    • 1
  • Mongi Felhi
    • 2
  • Nabil Fattah
    • 3
  • Ali Tlili
    • 1
    Email author
  1. 1.Department of Earth Science, Faculty of Science of SfaxSfax UniversitySfaxTunisia
  2. 2.Department of Geological Engineering, National School of Engineers of SfaxUniversity of SfaxSfaxTunisia
  3. 3.Gafsa Phosphate Company, Research Center Metlaoui 2130GafsaTunisia

Personalised recommendations