Prediction of process-induced void formation in anisotropic Fiber-reinforced autoclave composite parts

  • Bamdad BarariEmail author
  • Pavel Simacek
  • Shridhar Yarlagadda
  • Roger M. Crane
  • Suresh G Advani
Original Research
  • 25 Downloads

Abstract

A numerical methodology is proposed to predict void content and evolution during autoclave processing of thermoset prepregs. Starting with the initial prepreg void content, the void evolution model implements mechanisms for void compaction under the effect of the applied pressure, including Ideal Gas law compaction, and squeeze flow for single curvature geometries. Pressure variability in the prepreg stack due to interactions between applied autoclave pressure and anisotropic material response are considered and implemented. A parametric study is conducted to investigate the role of material anisotropy, initial void content, and applied autoclave pressure on void evolution during consolidation of prepregs on a tool with single curvatures. The ability of the model to predict pressure gradient through the thickness of the laminate and its impact on void evolution is discussed.

Keywords

Void prediction Prepreg Anisotropic prepreg Laminate Autoclave process 

Notes

Acknowledgements

This work is supported by Composites Automation, LLC and the United States Naval Air and Warfare Center under Prime Contract No. N68335-17-C-0093 administrated by Dr. Suresh G. Advani. The views, opinions and/or findings contained in this report are those of the author(s) and should not be construed as an official US Naval Air Warfare Center position, policy or decision unless so designated by other documentation. The authors also declare that they have no conflict of interest.

References

  1. 1.
    Chandrakala K, Vanaja A, Rao R (2009) Storage life studies on RT cure glass—epoxy prepregs. J Reinf Plast Compos 28(16):1987–1997CrossRefGoogle Scholar
  2. 2.
    Herrmann A, Zahlen P, Zuardy I (2005) Sandwich structures technology in commercial aviation. In: Thomsen OT, Bozhevolnaya E, Lyckegaard A (eds) Sandwich structures 7: advancing with sandwich structures and materials. Springer Netherlands, pp 13–26CrossRefGoogle Scholar
  3. 3.
    Kardos J. L., Duduković M. P., Dave R. (2005) Void growth and resin transport during processing of thermosetting — Matrix composites. Epoxy resins and composites IV. Advances in polymer science, vol 80. SpringerGoogle Scholar
  4. 4.
    Lightfoot SC, Wisnom MR, Potter K (2013) A new mechanism for the formation of ply wrinkles due to sheer between plies. Composites Part A 49:139–147CrossRefGoogle Scholar
  5. 5.
    Potter K, Khan B, Wisnom MR, Bell T, Stevens J (2008) Variability, fiber waviness and misalignment in the determination of the properties of composite materials and structures. Composites Part A 39(9):1343–1354CrossRefGoogle Scholar
  6. 6.
    Bloom LD, Wang J, Potter KD (2013) Damage progression and defect sensitivity: an experimental study of representative wrinkles in tension. Composites Part B 45(1):449–458CrossRefGoogle Scholar
  7. 7.
    Hsiao HM, Daniel IM (1996) Effect of fiber waviness on stiffness and strength reduction of unidirectional composites under compressive loading. Compos Sci Technol 56(5):581–593CrossRefGoogle Scholar
  8. 8.
    Garnich MR, Karami G (2004) Finite element for stiffness and strength of wavy fiber composites. J Compos Mater 38(4):273–292CrossRefGoogle Scholar
  9. 9.
    Karami G, Garnich MR (2005) Effective moduli and failure consideration for composites with periodic fiber waviness. Compos Struct 67(4):461–475CrossRefGoogle Scholar
  10. 10.
    Hubert P, Poursartip A (1998) A review of flow and compaction modelling relevant to thermoset matrix laminate processing. J Reinf Plast Compos 17(4):286–318CrossRefGoogle Scholar
  11. 11.
    Fernlund G, Griffith J, Courdji R, Poursartip A (2002) Experimental and numerical study of the effect of caul-sheets on corner thinning of composite laminates. Composites Part A 33(3):411–426CrossRefGoogle Scholar
  12. 12.
    Naji MI, Hoa SV (2000) Curing of thick angle-bend thermoset composite part: curing process modification for uniform thickness and uniform fiber volume fraction distribution. J Compos Mater 34(20):1710–1755CrossRefGoogle Scholar
  13. 13.
    Li Y, Li M, Gu Y, Zhang Z (2009) Numerical and experimental study on the effect of lay-up type and structural elements on thickness uniformity of L-shaped laminates. Appl Compos Mater 16(2):101–115CrossRefGoogle Scholar
  14. 14.
    Wang X, Zhang Z, Xie F, Li M, Dai D, Wang F (2009) Correlated rules between complex structure of composite components and manufacturing defects in autoclave molding technology. J Reinf Plast Compos 28(22):2791–2803CrossRefGoogle Scholar
  15. 15.
    Li M (2001) Optimal curing of thermoset composites: thermochemical and consolidation considerations. PhD thesis, University of Illinois at Urbana-ChampaignGoogle Scholar
  16. 16.
    Mélanie B (2010) Out-of-autoclave manufacturing of complex shape composite laminates. McGill University, Montreal, ManufacturingGoogle Scholar
  17. 17.
    Xin CB, Gu YZ, Li M, Luo J, Li YX, Zhang ZG (2011) Experimental and numerical study on the effect of rubber mold configuration on the compaction of composite angle laminates during autoclave processing. Composites Part A 42(10):1353–1360CrossRefGoogle Scholar
  18. 18.
    Johnston A (1997) An integrated model of the development of process-induced deformation in autoclave processing of composite structures. Ph.D. thesis, The University of British ColumbiaGoogle Scholar
  19. 19.
    Hubert P, Vaziri R, Poursartip A (1999) A two-dimensional flow model for the process simulation of complex shape composite laminates. Int J Numer Meth Eng 44(1):1–26 86CrossRefzbMATHGoogle Scholar
  20. 20.
    Min L, Yanxia L, Yizhuo G (2008) Numerical simulation flow and compaction during the consolidation of laminated composites. Wiley Intersci Soc Plast Eng 29(5):560–568 87Google Scholar
  21. 21.
    Dave R, Kardos JL, Dudukovic MP (1987) A model for resin flow during composite processing: part 1-general mathematical development. Polym Compos 8(1):29–38 88CrossRefGoogle Scholar
  22. 22.
    Gutowski TG, Cai Z, Bauer S, Boucher D (1987) Consolidation experiments for laminate composites. J Compos Mater 21(7):650–669 89CrossRefGoogle Scholar
  23. 23.
    Li M, Li Y, Zhang Z, Gu Y (2008) Numerical simulation flow and compaction during the consolidation of laminated composites. Polym Compos 29(5):560–568 90CrossRefGoogle Scholar
  24. 24.
    Li M, Charles L, Tucker III (2002) Modelling and simulation of two-dimensional consolidation for thermoset matrix composites. Compos A 33(6):877–892 91CrossRefGoogle Scholar
  25. 25.
    Dong C (2011) Model development for the formation of resin-rich zones in composites processing. Compos A 42(4):419–424CrossRefGoogle Scholar
  26. 26.
    Simacek P, Advani SG, Gruber M, Jensen B (2013) A non-local void filling model to describe its dynamics during processing thermoplastic composites. Composites Part A 46(1):154–165CrossRefGoogle Scholar

Copyright information

© Springer-Verlag France SAS, part of Springer Nature 2019

Authors and Affiliations

  • Bamdad Barari
    • 1
    Email author
  • Pavel Simacek
    • 2
    • 3
  • Shridhar Yarlagadda
    • 3
    • 4
  • Roger M. Crane
    • 3
    • 4
  • Suresh G Advani
    • 2
    • 3
  1. 1.Massachusetts Institute of TechnologyBostonUSA
  2. 2.Department of Mechanical EngineeringUniversity of DelawareNewarkUSA
  3. 3.Center for Composite MaterialsUniversity of DelawareNewarkUSA
  4. 4.Composites Automation LLCNewarkUSA

Personalised recommendations