Abstract
Transparent conductive Al2O3-doped zinc oxide (in AZO, Al2O3 content is ~ 2 wt%) thin films are deposited on flexible polyethylene terephthalate (PET) substrates, using radio frequency (rf) magnetron sputtering. The Taguchi method with an L 9 (34) orthogonal array, a signal-to-noise ratio and analysis of variance (ANOVA) was used to determine the performance characteristics of the coating operations. Using grey relational analysis, the optimization of these deposition process parameters for AZO thin films with multiple characteristics was performed. The electrical resistivity of AZO/PET films is reduced from 2.6 × 10−2 to 5.5 × 10−3 Ω-cm and the visible range transmittance is > 83%, using the grey relational analysis. ANOVA results for the grey relational grade indicate that rf power and working pressure are the two most influential factors. The effect of the rf power (in the range from 30 to 70 W) and the argon working pressure (in the range from 0.90 to 1.1 Pa) on the morphology and optoelectronic performance of AZO films are also investigated. An analysis of the influence of the dominant parameters in the optimal design region is helpful for adjustment of the coating parameters.
Similar content being viewed by others
References
Agashe C, Kluth O, Hüpkes J, Zastrow U, Rech B and Wuttig M 2004 J. Appl. Phys. 95 1911
Chen D Y and Hsu C Y 2008 Superlattice Microst. 44 742
Chen Y I and Duh J G 1991 Mater. Chem. Phys. 27 427
Chung Y M, Moon C S, Jung M J and Han J G 2005 Surf. Coat. Technol. 200 936
Deng J L 1989 J. Grey Syst. 1 1
Fernández S, Martínez-Steele A, Gandía J J and Naranjo F B 2009 Thin Solid Films 517 3152
Fortunato E, Gonçalves A, Assunção V, Marques A, Águas H, Pereira L, Ferreira I and Martins R 2003 Thin Solid Films 442 121
Hsu C Y and Tsang C H 2008 Sol. Energ. Mater. Sol. Cells 92 530
Jeong S H and Boo J H 2004 Thin Solid Films 105 447
Jin B J, Bae S H, Lee S Y and Im S 2000 Mater. Sci. Eng. B71 301
Kao J Y, Tsao C C, Wang S S and Hsu C Y 2010 Int. J. Adv. Manuf. Technol. 47 395
Kassis A and Saad M 2003 Sol. Energ. Mater. Sol. Cells 80 491
Kuo H H, Wu J H and Chin J 1998 J. Grey Syst. 1 47
Lee J, Jung H, Lee J, Lim D, Yang K, Yi J and Song W C 2008 Thin Solid Films 516 1634
Lin Y C, Chen M Z, Kuo C C and Yen W T 2009 Colloids Surf. A: Physicochem. Eng. Aspects 337 52
Lv M, Xiu X, Pang Z, Dai Y and Han S 2006 Appl. Surf. Sci. 252 5687
Miyazaki M, Sato K, Mitsui A and Nishimura H 1997 J. Non-Cryst. Solids 218 323
Moon C S, Chung Y M, Jung W S and Han J G 2007 Surf. Coat. Technol. 210 5035
Osama S M, Haitham R S and Hussam L A 2009 Eng. Tech. J. 27 1143
Paraguay D F, Morales J, Estrada L W, Andrade E and Miki-Yoshida M 2000 Thin Solid Films 366 16
Pei Z L, Zhang X B, Zhang G P, Gong J, Sun C, Huang R F and Wen L S 2006 Thin Solid Films 497 20
Phillip J R 1989 Taguchi techniques for quality engineering (New York: McGraw-Hill)
Rim Y S, Kim S M, Choi H W, Park S J and Kim K H 2008 Colloid. Surf. A313 461
Szyszka B 1999 Thin Solid Films 351 164
Tarng Y S, Juang S C and Chang C H 2002 J. Mater. Process Technol. 128 1
Tseng C H, Huang C H, Chang H C, Chen D Y, Chou C P and Hsu C Y 2011 Thin Solid Films 519 7959
Yu X, Ma J, Ji F, Wang Y, Zhang X, Cheng C and Ma H 2005a Appl. Surf. Sci. 239 222
Yu X, Ma J, Ji F, Wang Y, Zhang X, Cheng C and Ma H 2005b J. Cryst. Growth 274 474
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hu, C.C., Lu, T.W., Chou, C.Y. et al. Optimization of AZO films prepared on flexible substrates. Bull Mater Sci 37, 1275–1282 (2014). https://doi.org/10.1007/s12034-014-0072-8
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-014-0072-8