Evaluation of surface activity of hot-dip galvanized steel after alkaline cleaning

  • Ville SaarimaaEmail author
  • Carl Lange
  • Teemu Paunikallio
  • Aaretti Kaleva
  • Juha-Pekka Nikkanen
  • Erkki Levänen
  • Pasi Väisänen
  • Antti Markkula
Article
  • 41 Downloads

Abstract

The surface activity of hot-dip galvanized steel was evaluated after alkaline cleaning by exposing the cleaned specimens in humid supercritical carbon dioxide, followed by extraction and quantification of the formed corrosion products. Different free alkalinities of the cleaning bath were studied to obtain information on the evolution of zinc surface activity at different levels of surface etching. Surface reactivity of uncleaned galvanized steel is restricted and local, with major contributions from grain boundaries and intermetallic particles. Formation of zinc corrosion products took place in uncleaned samples exclusively on and around these sites. Al2O3 removal by alkaline cleaning gradually increased the surface activity. The major increase in surface activity was achieved when increasing the free alkalinity from 0.5 to 4.0 mEq/L, which was shown by formation of zinc corrosion products within zinc grains. The surface activity was confirmed by applying a titanium hexafluoride pretreatment on the cleaned panels and measuring the lateral microscale uniformity of the formed layer. The uniformity increased when larger areas of galvanized steel became activated by alkaline cleaning. Reactivity of zinc is rather difficult to quantify when setting up an industrial cleaning sequence for galvanized steel. Controlled exposure of cleaned samples in humid supercritical carbon dioxide, followed by quantification of oxidized zinc, provides a straightforward method to evaluate zinc reactivity.

Keywords

Zinc Surface activity Alkaline cleaning Supercritical carbon dioxide Cr-free pretreatment 

Notes

References

  1. 1.
    Markets for prepainted metal, http://prepaintedmetal.eu/874/947
  2. 2.
    Ohlsson, K, Bergman, T, Sundell, P-E, Deltin, T, Tran, I, Svensson, M, Johansson, M, “Novel Coil Coating Systems Using Fatty Acid Based Reactive Diluents.” Prog. Org. Coat., 73 (4) 291–293 (2012)CrossRefGoogle Scholar
  3. 3.
    Gao, Z, Zhang, D, Liu, Z, Li, X, Jiang, S, Zhang, Q, “Formation Mechanisms of Environmentally Acceptable Chemical Conversion Coatings for Zinc: A Review.” J. Coat. Technol. Res.,16 (1) (2019)CrossRefGoogle Scholar
  4. 4.
    Sinko, J, “Challenges of Chromate Inhibitor Pigments Replacement in Organic Coatings.” Prog. Org. Coat., 42 267–282 (2001)CrossRefGoogle Scholar
  5. 5.
    Belov, I, Copeland, D, Fitzwater, B, Knapps, J, Lewis, T, “Developement of Chromium (VI)-Free Coating Systems for Corrosion and Heat Protection.” In: Proc. Coatings Science International, pp 41–45 (2015)Google Scholar
  6. 6.
    Visser, P, Liu, Y, Terryn, H, Mol, JMC, “Lithium Salts as Leachable Corrosion Inhibitors and Potential Replacement for Hexavalent Chromium in Organic Coatings for the Protection of Aluminum Alloys.” J. Coat. Technol. Res., 13 (4) 557–566 (2016)CrossRefGoogle Scholar
  7. 7.
    Montemor, MF, “Functional and Smart Coatings for Corrosion Protection: A Review of Recent Advances.” Surf. Coat. Technol., 258 17–37 (2014)CrossRefGoogle Scholar
  8. 8.
    Kaluzny, K, “Why Some Metals and Alloys Are More Difficult to Pretreat than Others - Part I.” Met. Finish., 100 (9) 9–19 (2002)CrossRefGoogle Scholar
  9. 9.
    Hörnström, SE, Hedlund, EG, Klang, H, Nilsson, J-O, Backlund, M, Tegehall, P-E, “A Surface Study of the Chemical Pretreatment before Coil Coating of Hot Dip Zinc-Coated Steel.” Surf. Interface Anal., 19 (1–12) 121–126 (1992)CrossRefGoogle Scholar
  10. 10.
    Azmat, NS, Ralston, KD, Cole, IS, “Pre-Treatment of Zn Surfaces for Droplet Corrosion Studies.” Surf. Coat. Technol., 205 (3) 928–935 (2010)CrossRefGoogle Scholar
  11. 11.
    Berger, R, Bexell, U, Stavlid, N, Grehk, TM, “The Influence of Alkali-Degreasing on the Chemical Composition of Hot-Dip Galvanized Steel Surfaces.” Surface and Interface Analysis, 1130–1138 (2006)CrossRefGoogle Scholar
  12. 12.
    Maeda, S, “Surface Chemistry of Galvanized Steel Sheets Relevant to Adhesion Performance.” Prog. Org. Coat., 28 (4) 227–238 (1996)CrossRefGoogle Scholar
  13. 13.
    Schoeman, L, Burty, M, “Cleaning Optimization of Hot-Dip Galvanized Steel Surfaces in Preparation for Paint Application.” Mater. Sci. Forum, 941 1772–1777 (2018)CrossRefGoogle Scholar
  14. 14.
    Falk, T, Svensson, J, Johansson, L, “The Role of Carbon Dioxide in the Atmospheric Corrosion of Zinc.” J. Electrochem. Soc., 145 (1) 39–44 (1998)CrossRefGoogle Scholar
  15. 15.
    Bozbaʇ, SE, Erkey, C, “Supercritical Deposition: Current Status and Perspectives for the Preparation of Supported Metal Nanostructures.” J. Supercrit. Fluids, 96 298–312 (2015)CrossRefGoogle Scholar
  16. 16.
    Snoeyink, V, Jenkins, D, Water Chemistry. Wiley, New York (1980)Google Scholar
  17. 17.
    Kaleva, A, Saarimaa, V, Heinonen, S, Nikkanen, J.-P, Markkula, A, Väisänen, P, Levänen, E, “Dissolution-Induced Nanowire Synthesis on Hot-Dip Galvanized Surface in Supercritical Carbon Dioxide.” Nanomaterials, 7 (7) (2017)CrossRefGoogle Scholar
  18. 18.
    Saarimaa, V, Kaleva, A, Paunikallio, T, Nikkanen, J-P, Heinonen, S, Levänen, E, Väisänen, P, Markkula, A, “Convenient Extraction Method for Quantification of Thin Zinc Patina Layers.” Surf. Interface Anal., 50 (5) 564–570 (2018)CrossRefGoogle Scholar
  19. 19.
    Leroy, V, “Metallurgical Applications of Surface Analytical Techniques.” Mater. Sci. Eng., 42 (C) 289–307 (1980)CrossRefGoogle Scholar
  20. 20.
    Feliu, S, Jr, Barranco, V, “XPS Study of the Surface Chemistry of Conventional Hot-Dip Galvanised Pure Zn, Galvanneal and Zn-Al Alloy Coatings on Steel.” Acta Mater., 51 5413–5424 (2003)CrossRefGoogle Scholar
  21. 21.
    Wolpers, M, Angeli, J, “Activation of Galvanized Steel Surfaces before Zinc Phosphating - XPS and GDOES Investigation.” Appl. Surf. Sci., 179 281–291 (2001)CrossRefGoogle Scholar
  22. 22.
    Biber, HE, “Scanning Auger Microprobe Study of Hot-Dipped Regular-Spangle Galvanized Steel: Part I. Surface Composition of as-Produced Steel.” Metall. Trans. A, 19A 1603–1608 (1988)CrossRefGoogle Scholar
  23. 23.
    Marder, AR, “The Metallurgy of Zinc-Coated Steel.” Prog. Mater. Sci., 45 (3) 191–271 (2000)CrossRefGoogle Scholar
  24. 24.
    Strutzenberger, J, Faderl, J, “Solidification and Spangle Formation of Hot-Dip-Galvanized Zinc Coatings.” Met. Mater. Trans. A, 29A 631–645 (1998)CrossRefGoogle Scholar
  25. 25.
    Peng, D, Wu, J, Yan, X, Du, X, Yan, Y, Li, X, “The Formation and Corrosion Behavior of a Zirconium-Based Conversion Coating on the Aluminum Alloy AA6061.” J. Coat. Technol. Res., 13 (5) 837–850 (2016)CrossRefGoogle Scholar
  26. 26.
    Rangel, CM, Paiva, TI, Luz, PP, “Conversion Coating Growth on 2024-T3 Al Alloy The Effect of Pre-Treatments.” Surf. Coat. Technol., 202 3396–3402 (2008)CrossRefGoogle Scholar
  27. 27.
    Lunder, O, Simensen, C, Yu, Y, Nisancioglu, K, “Formation and Characterisation of Ti-Zr Based Conversion Layers on AA6060 Aluminium.” Surf. Coat. Technol., 184 (2–3) 278–290 (2004)CrossRefGoogle Scholar
  28. 28.
    Nordlien, JH, Walmsley, JC, Østerberg, H, Nisancioglu, K, “Formation of a Zirconium-Titanium Based Conversion Layer on AA 6060 Aluminium.” Surf. Coat. Technol., 153 (1) 72–78 (2002)CrossRefGoogle Scholar
  29. 29.
    Saarimaa, V, Markkula, A, Juhanoja, J, Skrifvars, BJ, “Improvement of Barrier Properties of Cr-Free Pretreatments for Coil-Coated Products.” J. Coat. Technol. Res., 12 (4) 721–730 (2015)CrossRefGoogle Scholar
  30. 30.
    Ramezanzadeh, B, Attar, MM, Farzam, M, “Corrosion Performance of a Hot-Dip Galvanized Steel Treated by Different Kinds of Conversion Coatings.” Surf. Coat. Technol., 205 (3) 874–884 (2010)CrossRefGoogle Scholar
  31. 31.
    Saarimaa, V, Kauppinen, E, Markkula, A, Juhanoja, J, Skrifvars, B-J, Steen, P, “Microscale Distribution of Ti-Based Conversion Layer on Hot Dip Galvanized Steel.” Surf. Coat. Technol., 206 19–20 (2012)CrossRefGoogle Scholar
  32. 32.
    Saarimaa, V, Kauppinen, E, Markkula, A, Juhanoja, J, Skrifvars, BJ, Steen, P, “Microscale Distribution of Ti-Based Conversion Layer on Hot Dip Galvanized Steel.” Surf. Coat. Technol., 206 (19–20) 4173–4179 (2012)CrossRefGoogle Scholar
  33. 33.
    Verdier, S, van der Laak, N, Dalard, F, Metson, J, Delalande, S, “An Electrochemical and SEM Study of the Mechanism of Formation, Morphology, and Composition of Titanium or Zirconium Fluoride-Based Coatings.” Surf. Coat. Technol., 200 (9) 2955–2964 (2006)CrossRefGoogle Scholar
  34. 34.
    Verdier, S, Van Der Laak, N, Delalande, S, Metson, J, Dalard, F, “The Surface Reactivity of a Magnesium-Aluminium Alloy in Acidic Fluoride Solutions Studied by Electrochemical Techniques and XPS.” Appl. Surf. Sci., 235 (4) 513–524 (2004)CrossRefGoogle Scholar
  35. 35.
    Lostak, T, Maljusch, A, Klink, B, Krebs, S, Kimpel, M, Flock, J, Schulz, S, Schuhmann, W, “Zr-Based Conversion Layer on Zn-Al-Mg Alloy Coated Steel Sheets: Insights into the Formation Mechanism.” Electrochim. Acta, 137 65–74 (2014)CrossRefGoogle Scholar
  36. 36.
    Deck, P, Moon, M, Sujdak, R, “Investigation of Fluoacid Based Conversion Coatings on Aluminium.” Prog. Org. Coat., 34 39–48 (1998)CrossRefGoogle Scholar
  37. 37.
    Saarimaa, V, Markkula, A, Arstila, K, Manni, J, Juhanoja, J, “Effect of Hot Dip Galvanized Steel Surface Chemistry and Morphology on Titanium Hexafluoride Pretreatment.” Adv. Mater. Phys. Chem., 7 28–41 (2017)CrossRefGoogle Scholar
  38. 38.
    Saarimaa, V, Markkula, A, Juhanoja, J, Skrifvars, B-J, “Novel Insight to Aluminum Compounds in the Outermost Layers of Hot Dip Galvanized Steel and How They Affect the Reactivity of the Zinc Surface.” Surf. Coat. Technol., 306 (2016)CrossRefGoogle Scholar

Copyright information

© American Coatings Association 2019

Authors and Affiliations

  1. 1.Top Analytica OyTurkuFinland
  2. 2.Materials Science and Environmental EngineeringTampere UniversityTampereFinland
  3. 3.SSAB Europe OyHämeenlinnaFinland

Personalised recommendations