, Volume 71, Issue 9, pp 3023–3030 | Cite as

Effects of Minor Cu, Ni and Ag Additions on the Reactions Between Sn-Based Solders and Co Substrate

  • Chao-hong WangEmail author
  • Chun-yi Kuo
  • Yu-bin Guo
Advanced Electronic Interconnection
  • 17 Downloads

Abstract

This study investigated the effects of minor Cu, Ni, and Ag additions in the interfacial reactions between Sn-based solders and Co. In the liquid-state reactions, the Cu contents greatly affected the formed intermetallic compounds and their growth rate. In the Sn-0.7 wt.%Cu/Co at 250°C, the CoSn3 growth was significantly inhibited by ~ 35%, in comparison with the Sn/Co reaction. With increasing to 0.9–2 wt.%Cu contents, both the (Cu,Co)6Sn5 and CoSn3 phases were simultaneously formed, and the interfacial evolutions were examined. With 0.7 wt.%Ni addition, the CoSn3 growth was slightly retarded by ~ 20%. In contrast, the 3.5 wt.%Ag addition showed no obvious difference. The inhibiting effects of adding these elements were Cu > Ni > Ag (= pure Sn). In the solid-state reactions with 0.7 wt.%Cu addition at 200°C, the CoSn3 growth was strongly retarded by ~ 55%. Minor additions of 0.7 wt.%Ni or 3.5 wt.%Ag exhibited a weak inhibiting effect on the CoSn3 growth.

Notes

Acknowledgements

Funding support of this research by Ministry of Science and Technology of Taiwan under Project No. MOST 107-2221-E-194-016 is gratefully acknowledged.

References

  1. 1.
    L. Zhang and K.N. Tu, Mater. Sci. Eng. R 82, 1 (2014).CrossRefGoogle Scholar
  2. 2.
    S. Cheng, C.M. Huang, and M. Pecht, Microelectron. Reliab. 75, 77 (2017).CrossRefGoogle Scholar
  3. 3.
    K.S. Kim, S.H. Huh, and K. Suganuma, J. Alloys Compd. 352, 226 (2003).CrossRefGoogle Scholar
  4. 4.
    H.-K. Cheng, C.-W. Huang, H. Lee, Y.-L. Wang, T.-F. Liu, and C.-M. Chen, J. Alloys Compd. 622, 529 (2015).CrossRefGoogle Scholar
  5. 5.
    T. Laurila, V. Vuorinen, and J.K. Kivilahti, Mater. Sci. Eng. R 49, 1 (2005).CrossRefGoogle Scholar
  6. 6.
    Y.-W. Yen, P.-H. Tsai, Y.-K. Fang, S.-C. Lo, Y.-P. Hsieh, and C. Lee, J. Alloys Compd. 503, 25 (2010).CrossRefGoogle Scholar
  7. 7.
    C.-H. Wang and S.-W. Chen, Acta Mater. 54, 247 (2006).CrossRefGoogle Scholar
  8. 8.
    C.E. Ho, S.C. Yang, and C.R. Kao, J. Mater. Sci. Mater. Electron. 18, 155 (2007).CrossRefGoogle Scholar
  9. 9.
    S.C. Yang, C.E. Ho, C.W. Chang, and C.R. Kao, J. Appl. Phys. 101, 084911 (2007).CrossRefGoogle Scholar
  10. 10.
    C.-F. Tseng, C.J. Lee, and J.-G. Duh, Mater. Sci. Eng. A 574, 60 (2013).CrossRefGoogle Scholar
  11. 11.
    G. Humpston, J. Mater. Sci. Mater. Electron. 21, 584 (2010).CrossRefGoogle Scholar
  12. 12.
    L. Magagnin, V. Sirtori, S. Seregni, A. Origo, and P.L. Cavallotti, Electrochim. Acta 50, 4621 (2005).CrossRefGoogle Scholar
  13. 13.
    N. Lu, D. Yang, and L. Li, Acta Mater. 71, 4581 (2013).CrossRefGoogle Scholar
  14. 14.
    C.-H. Wang and S.-W. Chen, Intermetallics 16, 524 (2008).CrossRefGoogle Scholar
  15. 15.
    C.-H. Wang and C.-Y. Kuo, Mater. Chem. Phys. 130, 651 (2011).CrossRefGoogle Scholar
  16. 16.
    W.J. Zhu, J. Wang, H.S. Liu, Z.P. Jin, and W.P. Gong, Mater. Sci. Eng. A 456, 109 (2007).CrossRefGoogle Scholar
  17. 17.
    H. Chen, Y.L. Tsai, Y.T. Chang, and A.T. Wu, J. Alloys Compd. 671, 100 (2016).CrossRefGoogle Scholar
  18. 18.
    C.-H. Wang and K.-T. Li, J. Mater. Sci. 51, 7309 (2016).CrossRefGoogle Scholar
  19. 19.
    C.-H. Wang, C.-C. Wen, and C.-Y. Lin, J. Alloys Compd. 662, 475 (2016).CrossRefGoogle Scholar
  20. 20.
    Y. Yang, J.N. Balaraju, Y. Huang, H. Liu, and Z. Chen, Acta Mater. 71, 69 (2014).CrossRefGoogle Scholar
  21. 21.
    C.-H. Wang, S.E. Huang, and K.T. Li, Intermetallics 56, 68 (2015).CrossRefGoogle Scholar
  22. 22.
    C.-H. Wang and K.T. Li, J. Alloys Compd. 649, 1197 (2015).CrossRefGoogle Scholar
  23. 23.
    Z.L. Ma and C.M. Gourlay, J. Alloys Compd. 706, 596 (2017).CrossRefGoogle Scholar
  24. 24.
    C.-H. Wang, C.-Y. Kuo, S.-E. Huang, and P.-Y. Li, Intermetallics 32, 57 (2013).CrossRefGoogle Scholar
  25. 25.
    Y.-K. Chen, C.-M. Hsu, S.-W. Chen, C.-M. Chen, and Y.-C. Huang, Metall. Mater. Trans. A 43, 3586 (2012).CrossRefGoogle Scholar
  26. 26.
    Y.-H. Chao, S.-W. Chen, C.-H. Chang, and C.-C. Chen, Metall. Mater. Trans. A 39, 477 (2008).CrossRefGoogle Scholar
  27. 27.
    C.-C. Chen and Y.-T. Chan, Intermetallics 18, 649 (2010).CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Department of Chemical EngineeringNational Chung Cheng UniversityChia-YiTaiwan

Personalised recommendations