Synthesis of Coarse-Grained Tungsten Carbide Directly from Scheelite/Wolframite by Carbothermal Reduction and Crystallization

  • Fenglong Sun
  • Xingyu Chen
  • Zhongwei ZhaoEmail author
Design, Development, Manufacturing, and Applications of Refractory Metals and Materials
  • 5 Downloads

Abstract

A novel method is proposed in this study to synthesize coarse-grained tungsten carbide (WC) directly from scheelite/wolframite concentrates. The synthetic process was divided into two parts, carburization and crystallization. WC was enriched in iron melt with the increase of temperature and further purified by crystallizing during the cooling process. The thermodynamics calculation for the reduction process and phase diagram analysis for crystallization were investigated. The scanning microscope (SEM) showed that the obtained sample was on the millimeter scale with a tri-prism shape, and all peaks detected by x-ray diffraction matched well with the WC structure. This method will shorten the WC preparation process greatly, and the obtained coarse-crystalline WC may have potential application in conventional cemented carbide, especially for mining and construction tools.

Notes

Acknowledgements

This work was financially supported by the National Natural Science Foundation of China (Key Program, Project 51334008) and Program for Changjiang Scholars.

References

  1. 1.
    F. Medeiros, S. Oliveira, C. Souza, A. Silva, U. Gomes, and J. Souza, Mater. Sci. Eng. A 58–62, 315 (2001).Google Scholar
  2. 2.
    Z. Zhao, Y. Liang, and H. Li, Int. J. Refract. Met. Hard Mater. 289–292, 29 (2011).Google Scholar
  3. 3.
    M. Marashi, J. Khaki, and S. Zebarjad, Int. J. Refract. Met. Hard Mater. 177–179, 30 (2012).Google Scholar
  4. 4.
    J. Gomes, A. Raddatz, and T. Carnahan, JOM 29–32, 12 (1985).Google Scholar
  5. 5.
    E. Smith, J. Cryst. Growth 75–79, 89 (1988).Google Scholar
  6. 6.
    R. Polini, E. Palmieri, and G. Marcheselli, Int. J. Refract. Met. Hard Mater. 289–300, 51 (2015).Google Scholar
  7. 7.
    A. Kumar, K. Singh, and O. Pandey, Int. J. Refract. Met. Hard Mater. 555–558, 29 (2011).Google Scholar
  8. 8.
    N. Welham, AIChE J. 68–71, 46 (2000).Google Scholar
  9. 9.
    M. Sakaki, A. Behnami, and M. Bafghi, Int. J. Refract. Met. Hard Mater. 142–147, 44 (2014).Google Scholar
  10. 10.
    H. Singh and O. Pandey, Ceram. Int. 10481–10487, 41 (2015).Google Scholar
  11. 11.
    H. Singh and O. Pandey, Ceram. Int. 785–790, 39 (2013).Google Scholar
  12. 12.
    L. Niu, M. Hojamberdiev, and Y. Xu, J. Mater. Process. Technol. 1986–1990, 210 (2010).Google Scholar
  13. 13.
    L. Niu, X. Wang, and Z. Fan, J. Wuhan Univ. Technol. Mater. Sci. Ed. 449-454, 28 (2013).Google Scholar
  14. 14.
    J. Chi, H. Li, J. Zhao, S. Wang, M. Li, Q. Ji, and J. Li, J. Mater. Eng. Perform. 3859–3866, 23 (2014).Google Scholar
  15. 15.
    I. Konyashin, F. Schäfer, R. Cooper, B. Ries, J. Mayer, and T. Weirich, Int. J. Refract. Met. Hard Mater. 225–232, 23 (2005).Google Scholar
  16. 16.
    F. Sun, X. Chen, and Z. Zhao, Ceram. Int. 1434–1437, 44 (2018).Google Scholar
  17. 17.
    A. Roine, HSC Chem. (2006).Google Scholar
  18. 18.
    S. Bolokang, C. Banganayi, and M. Phasha, Int. J. Refract. Met. Hard Mater. 211–216, 28 (2010).Google Scholar
  19. 19.
    R. Yang, T. Xing, R. Xu, and M. Li, Int. J. Refract. Met. Hard Mater. 138–140, 29 (2011).Google Scholar
  20. 20.
    K. MacKenzie, J. Temuujin, C. McCammon, and M. Senna, J. Eur. Ceram. Soc. 2581–2585, 26 (2006).Google Scholar
  21. 21.
    A. Koutsospyros, W. Braida, C. Christodoulatos, D. Dermatas, and N. Strigul, J. Hazard. Mater. 1–19, 136 (2006).Google Scholar
  22. 22.
    C. Hanyaloglu, B. Aksakal, and J. Bolton, Mater. Charact. 315–322, 47 (2001).Google Scholar
  23. 23.
    K. Korniyenko, In Iron Systems, Part 2: Selected Systems from Al-B-Fe to C-Co-Fe (Berlin: Springer, Berlin Heidelberg, 2008), pp. 476–512.CrossRefGoogle Scholar
  24. 24.
    Y. Liao and Z. Zhao, JOM 581–586, 70 (2018).Google Scholar
  25. 25.
    F. Tamura and H. Suito, Metall. Trans. B 121–130, 24 (1993).Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.School of Metallurgy and EnvironmentCentral South UniversityChangshaPeople’s Republic of China
  2. 2.Key Laboratory for Metallurgy and Material Processing of Rare MetalsCentral South UniversityChangshaPeople’s Republic of China

Personalised recommendations