Effect of sulfur on the cell performance in a molten carbonate fuel cell

  • Ki-Jeong Lee
  • Samuel Koomson
  • Choong-Gon LeeEmail author
Materials (Organic, Inorganic, Electronic, Thin Films)
  • 26 Downloads

Abstract

This study evaluated the performance characteristics of a molten carbonate fuel cell (MCFC) under sulfur poisoning condition. A 100 cm2 bench-scale MCFC was used for the performance test. The performance of the cell at the normal operation condition was measured at 620 °C under atmospheric pressure. To evaluate the sulfur poisoning effect, 50 ppm H2S/Balanced N2 gas mixture at a flow rate of 30 ml/min was injected into the anode. The cell performance was analyzed via steady-state polarization (SSP) and inert gas step addition (ISA) methods. The overpotential of the cell was observed to have been changed by the injection of H2S gas, and an overpotential increase of ca. 40% was recorded after about 100 hours from the point of addition of the H2S gas. A voltage reduction rate of −2.62×10−4 mV/s was recorded at a current density of 150mA/cm2 after about 240 hours. The steady-state polarization characteristics of the cell showed that the sulfur poisoning was relatively slow. In addition, the effect of H2S gas on the cell performance was quantitatively measured by the ISA method.

Keywords

Molten Carbonate Fuel Cell Anode Inert Gas Step Addition Sulphur Poisoning Overpotential 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    T. Ohta, T. N. Veziroglu, ENERGY CARRIERS AND CONVERSION SYSTEMS WITH EMPHASIS ON HYDROGEN, in Energy Carriers and Conversion Systems, [Ed. Tokio Ohta], in Encyclopedia of Life Support Systems (EOLSS), Developed under the Auspices of the UNESCO, Eolss Publishers, Oxford, UK, [http://www.eolss.net], 1 (2006).
  2. 2.
    I. Rexed, Application for Molten Carbonate Fuel Cells [Unpublished Doctoral dissertation]. KTH Royal Institute of Technology: Stockholm (2014).Google Scholar
  3. 3.
    C. G. Lee, J. Electroanal. Chem., 701, 36 (2013).CrossRefGoogle Scholar
  4. 4.
    S. J. McPhail, L. Leto, M.D. Pitra, V. Cigolotti and A. Moreno, International Status of Molten Carbonate Fuel Cells Technology; Advanced Fuel Cells Implementing Agreement, Annex 23 - MCFC; E.N.E.A.: Rome, Italy (2015).Google Scholar
  5. 5.
    H. J. Choi, J. J. Lee, S. H. Hyun and H. C. Lim, Int. J. Hydrogen Energy, 36, 11048 (2011).CrossRefGoogle Scholar
  6. 6.
    N. Di Giulio, B. Bosio, V. Cigolotti and S. W. Nam, Int. J. Hydrogen Energy, 37, 19329 (2012).CrossRefGoogle Scholar
  7. 7.
    I. Rexed, C. Lagergren and G. Lindbergh, Int. J. Hydrogen Energy, 39, 12242 (2014).CrossRefGoogle Scholar
  8. 8.
    M. Kawase, Y. Mugikura, T. Watanabe, Y. Hiraga and T. Ujihara, J. Power Sources, 104, 265 (2002).CrossRefGoogle Scholar
  9. 9.
    V. Cigolotti, S. McPhail, A. Moreno, S. P. Yoon, J. H. Han, S. W. Nam and T. Lim, Int. J. Hydrogen Energy, 36, 10311 (2011).CrossRefGoogle Scholar
  10. 10.
    E. Audasso, S. Nam, E. Arato and B. Bosio, J. Power Sources, 352, 216 (2017).CrossRefGoogle Scholar
  11. 11.
    H. V. P. Nguyen, S. A. Song, D. Seo, J. Han, S. P. Yoon, H. C. Ham, S. W. Nam, M. R. Othman and J. Kim, J. Power Sources, 230, 282 (2013).CrossRefGoogle Scholar
  12. 12.
    D. Weaver and J. Winnick, J. Electrochem. Soc., 136, 1679 (1989).CrossRefGoogle Scholar
  13. 13.
    H. Devianto, E. Simonetti, S. J. McPhail, F. Zaza, V. Cigolotti, C. Paoletti, A. Moreno, A. La Barbera and I. Luisetto, Int. J. Hydrogen Energy, 37, 19312 (2012).CrossRefGoogle Scholar
  14. 14.
    K. J. Lee, T. K. Kim, S. Koomson and C. G. Lee, Korean J. Chem. Eng., 35, 2010 (2018).CrossRefGoogle Scholar
  15. 15.
    C. G. Lee, J. Electroanal. Chem., 785, 152 (2017).CrossRefGoogle Scholar
  16. 16.
    C. G. Lee, B. S. Kang, H. K. Seo and H. C. Lim, J. Electroanal. Chem., 540, 169 (2003).CrossRefGoogle Scholar

Copyright information

© The Korean Institute of Chemical Engineers 2019

Authors and Affiliations

  1. 1.Department of Chemical & Biological EngineeringHanbat National UniversityDaejeonKorea

Personalised recommendations