Recovery of copper sulfate after treating As-containing wastewater by precipitation method

  • Ya-jie Zheng (郑雅杰)Email author
  • Yong Wang (王 勇)
  • Fa-xin Xiao (肖发新)
  • Yuan Luo (罗 圆)
Article

Abstract

The solid sodium hydroxide neutralized acidic As-containing wastewater till pH value was 6. Green copper arsenite was prepared after copper sulfate was added into the neutralized wastewater when the molar ratio of Cu to As was 2:1 and pH value of the neutralized wastewater was adjusted to 8.0 by sodium hydroxide. The arsenious acid solution and red residue were produced after copper arsenite mixed with water according to the ratio of liquid to solid of 4:1 and copper arsenite was reduced by SO2 at 60 °C for 1 h. The white powder was gained after the arsenious acid solution was evaporated and cooled. Copper sulfate solution was obtained after the red residue was leached by H2SO4 solution under the action of air. The results show that red residue is Cu3(SO3)2·2H2O and the white powder is As2O3. The leaching rate of Cu reaches 99.00% when the leaching time is 1.5 h, molar ratio of H2SO4 to Cu is 1.70, H2SO4 concentration is 24% and the leaching temperature is 80 °C. The direct recovery rate of copper sulfate is 79.11% and the content of CuSO4·5H2O is up to 98.33% in the product after evaporating and cooling the copper sulfate solution.

Key words

As-containing wastewater SO2 As2O3 copper sulfate copper arsenite recovery 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    DUTRÉ V, VANDECASTEELE C. Solidification/stabilisation of hazardous arsenic containing waste from a copper refining process [J]. Journal of Hazardous Materials, 1995, 40(1): 55–68.CrossRefGoogle Scholar
  2. [2]
    LEIST M, CASEY R J, CARIDI D. The management of arsenic wastes: Problems and prospects [J]. Journal of Hazardous Materials, 2000, 76(1): 125–138.CrossRefGoogle Scholar
  3. [3]
    RIOS-ARANA J V, WALSH E J, GARDEA-TORRESDEY J L. Assessment of arsenic and heavy metal concentrations in water and sediments of the Rio Grande at El Paso-Juarez metroplex region [J]. Environment International, 2004, 29(7): 957–971.CrossRefGoogle Scholar
  4. [4]
    HELSEN L, van den BULCK E. Review of disposal technologies for chromated copper arsenate (CCA) treated wood waste with detailed analyses of thermochemical conversion processes [J]. Environmental pollution, 2005, 134(2): 301–314.CrossRefGoogle Scholar
  5. [5]
    RIVEROS G, UTIGARD T A. Disposal of arsenic in copper discharge slags [J]. Journal of Hazardous Materials, 2000, 77(1/3): 241–252.CrossRefGoogle Scholar
  6. [6]
    ALEKSAN D, WITKIEWICZ K, BAL W. Damage of zinc fingers in DNA repair proteins, a novel molecular mechanism in carcinogenesis [J]. Toxicology Letters, 2006, 162(1): 29–42.CrossRefGoogle Scholar
  7. [7]
    SHIH C J, LIN C F. Arsenic contaminated site at an abandoned copper smelter plant: Waste characterization and solidification/ stabilization treatment [J]. Chemosphere, 2003, 53(7): 691–703.CrossRefGoogle Scholar
  8. [8]
    SONG S, VALDIVIESO A L, CAMPOS D J H. Arsenic removal from high-arsenic water by enhanced coagulation with ferric ions and coarse calcite [J]. Water Research, 2006, 40(2): 364–372.CrossRefGoogle Scholar
  9. [9]
    SHAABAN E R. Optical characterization of arsenic sulfide semiconducting glass films using the transmittance measurements [J]. Materials Chemistry and Physics, 2006, 100(2/3): 411–417.CrossRefGoogle Scholar
  10. [10]
    JAY J A, BLUTE N K, HEMOND H F. Arsenic-sulfides confound anion exchange resin exchange resin speciation of aqueous arsenic [J]. Water Research, 2004, 38(5): 1155–1158.CrossRefGoogle Scholar
  11. [11]
    MIHAJLOVIC I, STRBAC N, ZIVKOVIC Z, KOVACEVIC R, STEHERNIK M. A potential method for arsenic removal from copper concentrates [J]. Minerals Engineering, 2007, 20(1): 26–33.CrossRefGoogle Scholar
  12. [12]
    LIU Jian-chao, HE Hong-wu, FENG Xin-min. Direction of chemical pesticide development green chemical pesticides [J]. Pesticides, 2005, 44(1): 1–3.Google Scholar
  13. [13]
    GUAN Yu-jiang, CHEN Liu-chen. Study on the treatment of wastewater from sulphuric acid production by lime PFS process [J]. Environmental Protection of Chemical Industry, 1999, 19(6): 328–335. (in Chinese)Google Scholar
  14. [14]
    CHAN B K C, DUDENEY A W L. Reverse osmosis removal of arsenic residues from bioleaching of refractory gold concentrates [J]. Minerals Engineering, 2008, 21(4): 272–278.CrossRefGoogle Scholar
  15. [15]
    NISHIMURA T, ITOH C T, TOZAWA K. Stability and solubilities of metal arsenates and arsenates in water and effect of sulfate and carbonate ions on their solubilities[C]// REDDY R G, HENDRIX J L, QUENEAU P B. Arsenic Fundamentals and Applications. Warrendale, PA: TMS, 1988: 77–97.Google Scholar
  16. [16]
    ZHENG Ya-jie, WANG Yong, ZHAO Pan-feng. A method of producing arsenite copper and arsenate copper from waste acid contained As: CN, 200610031980.7 [P]. 2006-10-25. (in Chinese)Google Scholar
  17. [17]
    ZHENG Ya-jie, XIAO Fa-xin, WANG Yong. Preparation and application of copper arsenite: CN, 200610031980.7 [P]. 2006-07-19. (in Chinese)Google Scholar
  18. [18]
    WANG Yong, ZHAO Pan-feng, ZHENG Ya-jie. Preparation of copper arsenite from waste acid containing arsenic and its application in copper electrolyte purification [J]. Journal of Central South University: Science and Technology, 2007, 38(6): 1115–1120. (in Chinese)Google Scholar
  19. [19]
    KHANDAKER N R, TETER D M, KRUMHANSL J L. Arsenic removal in conjunction with lime softening: US 6802980B1 [P]. 2004-12-12.Google Scholar
  20. [20]
    ZHENG Ya-jie, LUO Yuan, WANG Yong. Method of preparing arsenic trioxide from As-containing wastewater: CN, 200710035704.2 [P]. 2007-09-07. (in Chinese)Google Scholar

Copyright information

© Central South University Press and Springer-Verlag GmbH 2009

Authors and Affiliations

  • Ya-jie Zheng (郑雅杰)
    • 1
    Email author
  • Yong Wang (王 勇)
    • 1
  • Fa-xin Xiao (肖发新)
    • 1
  • Yuan Luo (罗 圆)
    • 1
  1. 1.School of Metallurgical Science and EngineeringCentral South UniversityChangshaChina

Personalised recommendations