Isothermal Section of Er-Ag-Sn System at 873 K

  • Dmitry ElnyakovEmail author
  • Konstantin Kalmykov
  • Sergey Dunaev


The isothermal section of the Er-Ag-Sn system at 873 K was constructed with the use of scanning electron microscopy, energy-dispersive x-ray microanalysis and x-ray powder diffraction. Two ternary compounds were confirmed at this temperature: ErAgSn (LiGaGe structure type, P63mc, Z = 2, a = 4.6595(2) Å, c = 7.2872(3) Å) and non-stoichiometric phase ErAg1−xSn2+x (Cu3Au structure type, Pm-3m, Z = 1). For the last one homogeneity range was established (0.08 < x < 0.24) and lattice parameters were determined (a = 4.5007(4), 4.5040(2), 4.5107(1), 4.5412(1) Å for the compositions Er25.4Ag23.4Sn51.2, Er25.7Ag23.0Sn51.3, Er25.7Ag21.7Sn52.6, Er25.2Ag18.6Sn56.2 (at.%) respectively). Melting point of the phase Er25.7Ag21.7Sn52.6 (at.%) was determined to be 1199 K by differential thermal analysis.


experimental phase equilibria intermetallics ternary system 



X-ray part of this study was supported by the Russian Ministry of Science and Education (Grant No. RFMEFI61616X0069).


  1. 1.
    E. Morosan and D. Natelson, Strongly Correlated Materials, Adv. Mater., 2012, 24, p 4896-4923CrossRefGoogle Scholar
  2. 2.
    D. Elnyakov, K. Kalmykov, S. Tarelkin, and S. Dunaev, Isothermal Sections of Tm-Ag-Sn and Lu-Ag-Sn Ternary Systems at 873 K, J. Alloys Compd., 2016, 688, p 828-839CrossRefGoogle Scholar
  3. 3.
    I. Karakaya and W.T. Thompson, The Ag-Sn (Silver-Tin) System, Bull. Alloy Phase Diagr., 1987, 8, p 340-347CrossRefGoogle Scholar
  4. 4.
    R.H. Kane, B.G. Giessen, and N.G. Grant, New Metastable Phases in Binary Tin Alloy Systems, Acta Metall., 1967, 14, p 605-609CrossRefGoogle Scholar
  5. 5.
    Y. Ning and X. Zhou, Metastable Extension of Solid Solubility of Alloying Elements in Silver, J. Alloys Compd., 1992, 182, p 131-144CrossRefGoogle Scholar
  6. 6.
    H. Okamoto, Comment on Er-Sn (Erbium-Tin), J. Phase Equilib., 1995, 16, p 197-198CrossRefGoogle Scholar
  7. 7.
    W. Jeitschko and E. Parthe, Phases of the Rare Earth Elements with the Tin and Lead, Acta Crystallogr., 1976, 22, p 551-555CrossRefGoogle Scholar
  8. 8.
    M.L. Fornasini, F. Merlo, and G.B. Bonino, Composti di formula M5Sn4 e M11Sn10 formati dalle terre rare con lo stagno, Atti Accad. Naz. Lincei Rend. Cl. Sci. Fiz. Mat. Nat., 1971, 50, p 186-196Google Scholar
  9. 9.
    A. Palenzona and P. Manfrinetti, The Tin-Rich Side of the Rare Earth-Tin Systems (R = Gd, Tb, Dy, Ho, Er, Tm, Lu and Y), J. Alloys Compd., 1993, 201, p 43-47CrossRefGoogle Scholar
  10. 10.
    A. Iandelli, A. Palenzona, and G.B. Bonino, Sulla struttura dei composti intermetallici delle terre rare di formula MSn2, Atti Accad. Naz. Lincei Rend. Cl. Sci. Fiz. Mat. Nat., 1966, 40, p 623-628Google Scholar
  11. 11.
    K. Meier, L.O. Vasylechko, R.H. Cardoso-Gil, U. Burkhart, W. Schnelle, Y. Grin, and U. Schwarz, High-Pressure High-Temperature Synthesis, Magnetic Properties and X-ray Absorption Spectroscopy of Phases RE3Sn7 and hp-RESn3−x (RE = Tb, Ho, Er), Z. Anorg. Allg. Chem., 2010, 636, p 1695-1702CrossRefGoogle Scholar
  12. 12.
    K.A. Gschneidner and F.W. Calderwood, Ag-Er (silver-erbium), Binary Alloys Phase Diagrams, Vol 1, T.B. Massalski, Ed., ASM International, Materials Park, 1990, p 30-32Google Scholar
  13. 13.
    S. Steeb, D. Godel, and C. Löhr, On the Structure of the Compounds Ag3R.E. (R.E. = Y, La, Ce, Sm, Gd, Dy, Ho, Er), J. Less Common Met., 1968, 15, p 137-141CrossRefGoogle Scholar
  14. 14.
    C.C. Chao, H.L. Luo, and P. Dumez, CsCl-Type Compounds in Binary Alloys of Rare-Earth Metals with Gold and Silver, J. Appl. Phys., 1963, 34, p 1971-1973ADSCrossRefGoogle Scholar
  15. 15.
    O.D. McMasters, K.A. Gschneidner, and R.F. Venteicher, Crystallography of the Silver-Rich Rare-Earth-Silver Intermetallic Compounds, Acta Crystallogr. Sect. B Struct. Sci., 1970, 26, p 1224-1229CrossRefGoogle Scholar
  16. 16.
    C.P. Sebastian, G. Heymann, B. Heying, U.C. Rodewald, H. Huppertz, and R. Pöttgen, Dimorphic ErAgSn and TmAgSn—High-Temperature and High-Pressure Driven Phase Transitions, Z. Anorg. Allg. Chem., 2007, 633, p 1551-1555CrossRefGoogle Scholar
  17. 17.
    V.V. Romaka, V. Davydov, L. Romaka, and Y.V. Stadnyk, Crystal Structure of New RAgSn2 Ternary Compounds (R = Y, Gd, Tb, Dy, Ho, Er), J. Alloys Compd., 2008, 457, p 329-331CrossRefGoogle Scholar
  18. 18.
    J. Rodríguez-Carvajal, Recent Developments of the Program FULLPROF, Comm. Powder Diffr. (IUCr) Newsl., 2001, 26, p 12-19Google Scholar
  19. 19.
    D.D. Elnyakov, K.B. Kalmykov, K.V. Pokholok, and S.F. Dunaev, Crystal Structure and Phase Transitions of Ternary Compounds in the Thulium-Silver-Tin System, Russ. J. Inorg. Chem., 2015, 60, p 1173-1178CrossRefGoogle Scholar
  20. 20.
    R.D. Shannon, Revised Effective Ionic Radii and Systematic Studies of Interatomic Distances in Halides and Chalcogenides, Acta. Cryst., 1976, A32, p 751-767CrossRefGoogle Scholar
  21. 21.
    J. Liang, C. Liao, Y. Du, Y. Tang, Y. Han, Y. He, and S. Liu, The Isothermal Section of the Ag-La-Sn Ternary System at 400 °C, J. Alloys Compd., 2010, 493, p 122-127CrossRefGoogle Scholar
  22. 22.
    P. Boulet, D. Mazzone, H. Noel, P. Riani, P. Rogl, and R. Ferro, The System Ce-Ag-Sn: Phase Equilibria and Magnetic Properties, Intermetallics, 1999, 7, p 931-935CrossRefGoogle Scholar
  23. 23.
    D. Mazzone, P. Riani, G. Zanicchi, R. Marazza, and R. Ferro, The Isothermal Section at 400 °C of the Pr-Ag-Sn Ternary System, Intermetallics, 2002, 10, p 801-809CrossRefGoogle Scholar
  24. 24.
    K. Latka, J. Gurgul, W. Chajec, R. Kmiec, and A.W. Pacyna, Magnetic and Spectroscopic Properties of NdTSn (T = Ag, Au) Compounds, J. Alloys Compd., 2004, 385, p 64-73CrossRefGoogle Scholar
  25. 25.
    D. Mazzone, D. Rossi, R. Marazza, and R. Ferro, A Contribution to the Crystal Chemistry of Ternary 1:1:1 Alloys: RAgSn and RCuTl Compounds (R = Rare Earth), J. Less Common Met., 1981, 80, p 47-52CrossRefGoogle Scholar
  26. 26.
    K. Latka, E.A. Görlich, W. Chajec, R. Kmiec, and A.W. Pacyna, Crystal and Magnetic Properties of GdTSn Compounds (T = Ag, Au), J. Alloys Compd., 1997, 262, p 108-113CrossRefGoogle Scholar
  27. 27.
    C.P. Sebastian, G. Heymann, B. Heying, U.C. Rodewald, H. Huppertz, and R. Pöttgen, Dimorphic ErAgSn and TmAgSn—High-Pressure and High-Temperature Driven Phase Transitions, Z. Anorg. Allg. Chem., 2007, 633, p 1551-1555CrossRefGoogle Scholar
  28. 28.
    B. Heying, U.C. Rodewald, G. Heymann, W. Hermes, F.M. Schappacher, J.F. Riecken, C.P. Sebastian, H. Huppertz, and R. Pöttgen, The High-Temperature Modification of LuAgSn and High-Pressure High-Temperature Experiments on DyAgSn, HoAgSn, and YbAgSn, Z. Naturforsch. B Chem. Sci., 2008, 63, p 193-198Google Scholar

Copyright information

© ASM International 2018

Authors and Affiliations

  • Dmitry Elnyakov
    • 1
    Email author
  • Konstantin Kalmykov
    • 1
  • Sergey Dunaev
    • 1
  1. 1.Department of ChemistryLomonosov Moscow State UniversityMoscowRussia

Personalised recommendations