Fixing Induction Heat Treatment Flaws of an Automotive Transmission Output Shaft

  • M. HaghshenasEmail author
  • W. Savich
Technical Article---Peer-Reviewed
  • 80 Downloads

Abstract

In the automotive manufacturing industries, heat treatment processes such as induction hardening or case hardening are required to meet the daunting demands of the customers in terms of quality and load-bearing capability of individual components. One of the key automobile engine components which almost always goes through some surface hardening is the transmission output shaft. Improper hardening of these components can create serious issues (i.e., catastrophic fracture) during actual service. Current article aims at understanding the mechanics of output shaft torque transfer, its vulnerabilities, the defects encountered during the induction hardening process and their relation to the premature failure of the transmission system output shaft. To this end, a comprehensive failure analysis has been performed on a defective induction-hardened part which showed significantly lower fatigue life including microstructural assessments, hardness testing, torque measurements and finite element analysis to shed light on the nature of failure and fracture of the component. Different possible contributing parameters were studied, and some remedial actions were provided to improve the process and to counter the reasons of the cracking in the process. The findings of this paper are in particular interests of failure analysis researchers, heat treatment experts, metallurgists and automotive engineers in industry and academia.

Keywords

Induction heating Case depth Output shaft Transmission system Martensite Failure Finite element 

References

  1. 1.
    O. Lucia, P. Maussion, E. Dede, J. Burdio, Induction heating technology and its applications: past developments, current technology, and future challenges. IEEE Trans. Industr. Electron. 61, 2509–2520 (2013)CrossRefGoogle Scholar
  2. 2.
    S. Brill, D.M. Schibisch, Induction hardening versus case hardening: a comparison. Induc. Technol. Rep. 1, 76–83 (2015)Google Scholar
  3. 3.
    V. Rudnev, Metallurgical ‘fine points’ of induction hardening. Ind. Heat. 2005, 37–42 (2005)Google Scholar
  4. 4.
    V.I. Rudnev, R. Cook, D. Loveles, M. Black, J. Murray, Induction hardening basics for iron and steel. Mod. Appl. News 11, 58–61 (2000)Google Scholar
  5. 5.
    H. Hammi, A. El Ouafi, N. Barka, Study of frequency effects on hardness profile of spline shaft heat-treated by induction. J. Mater. Sci. Chem. Eng. 4, 1–9 (2016)Google Scholar
  6. 6.
    A. Vieweg, G. Ressel, P. Prevedel, P. Raninger, M. Panzen, S. Marsoner, R. Ebner, Induction hardening: differences to a conventional heat treatment process and optimization of its parameters. IOP Conf. Ser. Mater. Sci. Eng. 119, 012019 (2016).  https://doi.org/10.1088/1757-899X/119/1/012019 CrossRefGoogle Scholar
  7. 7.
    M. Sharma, J.S. Kohli, S. Akhai, Metallurgical analysis of cracks encountered during induction hardening of crankshafts. Int. J. Res. Advent Technol. 2, 295–304 (2014)Google Scholar
  8. 8.
    S. Brill, M. Schibisch, Induction hardening versus case hardening: a comparison. Heat Process. 1/2015, 76–83 (2015)Google Scholar
  9. 9.
    A. Deshmukh, D.H. Burande, A review: induction hardening on axle shaft. Int. J. Eng. Trends Technol. (IJETT) 35, 43–46 (2016)CrossRefGoogle Scholar
  10. 10.
    C.K. Clarke, D. Halimunanda, Failure analysis of induction hardened automotive axles. J. Fail. Anal. Prev. (2008).  https://doi.org/10.1007/s11668-008-9148-3 CrossRefGoogle Scholar
  11. 11.
    A. Deshmukh, D.H. Burande, Induction Hardening on drive axle shaft and it’s FEA. Int. Eng. Res. J. 2, 1197–1201 (2016)Google Scholar
  12. 12.
    Z. Li, B.L. Ferguson, A. Freborg, R. Goldstein, J. Jackowski, V. Nemkov, G. Fett, Typical heat treatment defects of gears and solutions using FEA modeling. Therm. Process. Gear Solut. 2, 50–58 (2016)Google Scholar
  13. 13.
    G.V.B. Lemos, T.K. Hirsch, A.S. da Rocha, R.M. Nunes, Residual stress analysis of drive shafts after induction hardening. Mater. Res. 17(Suppl 1), 70–74 (2014).  https://doi.org/10.1590/S1516-14392014005000077 CrossRefGoogle Scholar
  14. 14.
    V. Rudnev, The day after tomorrow: the future of induction heating. Heat Process. Rep. 4(45–5), 2 (2017)Google Scholar
  15. 15.
    R.E. Haimbaugh, Practical Induction Heat Treating (Materials Park, ASM International, 2001), pp. 3–284Google Scholar
  16. 16.
    H. Ma, The quantitative assessment of retained austenite in induction hardened ductile iron. Electronic theses and dissertations. 197. (2012), https://scholar.uwindsor.ca/etd/197

Copyright information

© ASM International 2018

Authors and Affiliations

  1. 1.Department of Mechanical EngineeringUniversity of North DakotaGrand ForksUSA
  2. 2.Frank Hasenfratz Centre of Excellence in ManufacturingLinamar CorporationGuelphCanada

Personalised recommendations