Journal of Failure Analysis and Prevention

, Volume 17, Issue 5, pp 871–881 | Cite as

Premature Failure of an Industrial Mixer Timing Gears

Technical Article---Peer-Reviewed
  • 79 Downloads

Abstract

A systematic and practical methodology was adopted to determine the root cause(s) of the premature failure of a pelletizer mixer timing gear. The investigation activities covered all possible causes of failure and included field examination, interview of engineers and operators, lubrication analysis, metallurgical examination. Fracture surfaces and microstructure of gear material were examined, and hardness profiles were developed. Analyses of shaft misalignment and teeth profiles were performed and found to be within acceptable limits. Results clearly indicate the surface hardness deficiencies in many locations specifically at center of the driven gear, area of severe pitting. The developed hardness profile for all locations is lower than that specified by the manufacturer. Fractographic analysis revealed that failure occurred by pitting followed by crack propagation. A number of cracks are seen to branch in different directions indicating the presence of high contact stresses combined with weak surface strength. Bending fatigue and pitting fatigue stress calculations revealed that the safety factor under contact is well below the desired value.

Keywords

Gear failures Gear tooth stress analysis Heat treatment Misalignment Pitting 

Notes

Acknowledgments

The authors acknowledge the support provided by King Fahd University of Petroleum & Minerals, Dhahran, Saudi Arabia.

References

  1. 1.
    O. Asi, Fatigue failure of a helical gear in a gearbox. Eng. Fail. Anal. 13, 1116–1125 (2006)CrossRefGoogle Scholar
  2. 2.
    L. Alban, Number 1 gear failure—tooth bending fatigue. SAE technical paper 841088 (1984)Google Scholar
  3. 3.
    G.W. Powell, Failure analysis and prevention, in ASM Handbook (American Society for Metals, Metals Park, OH, 1986), p. 11Google Scholar
  4. 4.
    P.J.L. Fernandes, Tooth bending fatigue failures in gears. Eng. Fail. Anal. 3, 219–225 (1996)CrossRefGoogle Scholar
  5. 5.
    S. Netpu, P. Srichandr, Failure analysis of a herringbone gear. Key Eng. Mater. 462–463, 366–371 (2011)CrossRefGoogle Scholar
  6. 6.
    Y. Ding, N.F. Rieger, Spalling formation mechanism for gears. Wear 254, 1307–1317 (2003)CrossRefGoogle Scholar
  7. 7.
    Y. Ding, R. Jones, B.T. Kuhnell, Elastic–plastic finite element analysis of spall formation in gears. Wear 197(1), 197–205 (1996)CrossRefGoogle Scholar
  8. 8.
    B.-R. Michaeli, K. Höhn, Influence of oil temperature on gear failures. Tribol. Int. 37, 103–109 (2004)CrossRefGoogle Scholar
  9. 9.
    P.J.L. Fernandes, A. James, Failure analysis report, metallurgical and corrosion services, CSIR 1994Google Scholar
  10. 10.
    P.J.L. Fernandes, C. McDuling, Surface contact fatigue failures in gears. Eng. Fail. Anal. 4(2), 99–107 (1997)CrossRefGoogle Scholar
  11. 11.
    A.D. Deutschman, W.J. Michels, C.E. Wilson, Machine Design, Theory and Practice (Macmillan, London, 1975)Google Scholar
  12. 12.
    C.R. Das, S.K. Albert, A.K. Bhaduri, S.K. Ray, Failure analysis of a pinion. Eng. Fail. Anal. 12, 287–298 (2005)CrossRefGoogle Scholar

Copyright information

© ASM International 2017

Authors and Affiliations

  1. 1.Mechanical Engineering DepartmentKing Fahd University of Petroleum and MineralsDhahranSaudi Arabia

Personalised recommendations