Premature Corrosion of Steak Knives Due to Extensive Precipitation of Chromium Carbides

Case History---Peer-Reviewed

Abstract

Steak knives from three different suppliers were brought to our facility to conduct a comparative analysis of their metallurgical properties. Although they have allegedly been used and cleaned in similar conditions in several restaurants across North America, only knives coming from one supplier showed signs of premature corrosion. Our investigation found that even though they have similar chemical and mechanical properties, and had been submitted to the same heat treatment, major microstructure discrepancies made some of these knives prone to rapid corrosion. As per our examination, the prematurely corroded knives experienced extensive chromium carbides precipitation during heat treatment, which determined a massive chromium depletion of the matrix and lowered their corrosion resistance. On the contrary, the knives that never corroded kept all their chromium content inside the matrix, thus contributing to better corrosion resistance.

Keywords

Martensitic stainless steel Corrosion Heat treated Chromium carbides precipitation 

References

  1. 1.
    Heat Treater’s Guide: Standard Practice and Procedures for Steel, 6th edn., p. 432. ASM International (1993)Google Scholar
  2. 2.
    Corrosion. In: Metal Handbook, vol. 13, 9th edn., p. 550. ASM International (1998)Google Scholar
  3. 3.
    Cutlery&Allied Trades Research Association (CATRA): Care of Cutlery and Flatware: Care of Stainless Steel Cutlery, http://www.catra.org/pages/products/sharpening/careof.htm
  4. 4.
    Corrosion. In: Metal Handbook, vol. 13, 9th edn., p. 559. ASM International (1998)Google Scholar
  5. 5.
    Candelaria, A.F., Pinedo, C.E.: Influence of the heat treatment on the corrosion resistance of the martensitic stainless steel type AISI 420. J. Mater. Sci. Lett. 22, 1151–1153 (2003)CrossRefGoogle Scholar
  6. 6.
    Garcia de Andres, C., Alvarez, L.F.: Optimization of the properties obtained by quenching in martensitic steels X30–40Cr13 and X40–60CrMoV14. J. Mater. Sci. 28, 1264–1268 (1993)CrossRefADSGoogle Scholar

Copyright information

© ASM International 2010

Authors and Affiliations

  1. 1.SGS Canada Inc.—Materials EngineeringMontrealCanada

Personalised recommendations