Microstructure and Thermophysical Properties of SrZrO3 Thermal Barrier Coating Prepared by Solution Precursor Plasma Spray
- 106 Downloads
Strontium zirconate (SrZrO3) thermal barrier coatings were deposited by solution precursor plasma spray (SPPS) using an aqueous precursor solution. The phase transition of the SrZrO3 coating and the influence of the aging time at 1400 °C on the microstructure, phase stability, thermal expansion coefficient, and thermal conductivity of the coating were investigated. The unique features of SPPS coatings, such as interpass boundary (IPB) structures, nano- and micrometer porosity, and through-thickness vertical cracks, were clearly observed evidently in the coatings. The vertical cracks of the coatings remained substantially unchanged while the IPB structures gradually diminished with prolonged heat treatment time. t-ZrO2 developed in the coatings transformed completely to m-ZrO2 phase after heat treatment for 100 h. Meanwhile, the SrZrO3 phase in the coatings exhibited good phase stability upon heat treatment. Three phase transitions in the SrZrO3 coatings were revealed by thermal expansion measurements. The thermal conductivity of the as-sprayed SrZrO3 coating was ~1.25 W m−1 K−1 at 1000 °C and remained stable after heat treatment at 1400 °C for 360 h, revealing good sintering resistance.
Keywordsperovskites segmented coatings solution precursor plasma spray thermal barrier coatings (TBCs) thermophysical properties
The work is sponsored by the National Natural Science Foundation of China (Nos. 51462026 and 51672136) and the Inner Mongolia Natural Science Foundation (No. 2017MS0503).
- 15.X. Zhou, D. Liu, H. Bu, L. Deng, H. Liu, P. Yuan, P. Du, and H. Song, XRD-Based Quantitative Analysis of Clay Minerals Using Reference Intensity Ratios, Mineral Intensity Factors, Rietveld, and Full Pattern Summation Method: A Critical Review, Solid Earth Sci., 2018, 3, p 16-29CrossRefGoogle Scholar
- 16.N. Jacobson, Thermodynamic Properties of Some Metal Oxide Zirconia Systems, NASA TM 102351, (1989) p 1-63Google Scholar
- 21.D.P.H. Hasselman, L.F. Johnson, L.D. Bentsen, R. Syed, H.L. Lee, and M.V. Swain, Thermal Diffusivity and Conductivity of Dense Polycrystalline ZrO2 Ceramics: A Survey, Am. Ceram. Soc. Bull., 1987, 66, p 799-806Google Scholar