Sulfide Stress Corrosion Cracking Behavior of G105 and S135 High-Strength Drill Pipe Steels in H2S Environment

  • Sheji LuoEmail author
  • Ming LiuEmail author
  • Yi Shen
  • Xiuzhou Lin
Article

Abstract

Slow strain rate testing was employed to investigate the sulfide stress corrosion cracking (SSCC) behavior of low-carbon high-strength drill pipe steels (G105 and S135) in the simulated drilling environment containing H2S. Results reveal that both G105 and S135 steels have a high SSCC susceptibility in the simulated drilling environment containing H2S. In the range of experimental slow strain rate, the SSCC sensitivity of drill pipe steel increases with the decrease in slow strain rate, and the ductility and fracture properties of drill pipe steels also decrease obviously. With the increase in the steel strength, the SSCC sensitivity of the drill pipe steel increases, and the S135 drill pipe steel has higher SSCC sensitivity than G105. There is no obvious plastic deformation on the fracture surface of G105 and S135 steels in H2S solution. The cracks of fracture sprout on the surface of the specimen, the instantaneous fracture zone is in the middle, and the fracture can be divided into the cracking and the final fracture zone. The SSCC mechanisms of two drill pipe steels are hydrogen embrittlement. The hydrogen enters the steel and reduces the binding force of the iron atom, resulting in cleavage fracture.

Keywords

cleavage fracture drill pipe steel hydrogen sulfide stress corrosion cracking 

Notes

Acknowledgments

This work was supported by the National Natural Science Foundation of China (No. 51801149), the Opening Project of Material Corrosion and Protection Key Laboratory of Sichuan province (No. 2018CL16), the China postdoctoral Science Foundation (No. 2017M620448) and the Youth Science and Technology Innovation Fund of Xi’an Shiyou University (No. 2015QN014).

References

  1. 1.
    S. Navabzadeh, B. Brown, and S. Nesic, Verification of an Electrochemical Model for Aqueous Corrosion of Mild Steel for H2S Partial Pressures up to 0.1 MPa, Corrosion, 2017, 73, p 144–154Google Scholar
  2. 2.
    M. Monnot, R.P. Nogueira, V. Roche, B. Berthomé, E. Chauyeau, R. Estevez, and M. Mantel, Sulfide Stress Corrosion Study of a Super Martensitic Stainless Steel in H2S Sour Environments: Metallic Sulfides Formation and Hydrogen Embrittlement, Appl. Surf. Sci., 2017, 394, p 132–141Google Scholar
  3. 3.
    Z. Zhang, N. Zhang, Z.W. Liu, and W.T. Zhao, Synergistic Effects of Corrosion Time and Stress on Corrosion of Casing Steel in H2S/CO2 Gas Wells, Mater. Corros., 2017, 69, p 386–392Google Scholar
  4. 4.
    T.J. Mesquita, E. Chauveau, M. Mantel, N. Bouvier, and D. Koschel, Corrosion and Metallurgical Investigation of Two Supermartensitic Stainless Steels for Oil and Gas Environments, Corros. Sci., 2014, 81, p 152–161Google Scholar
  5. 5.
    C. Yang, Gas Production Project, China Petroleum Industry Press, Beijing, 2001Google Scholar
  6. 6.
    Q. Liu, Z. Li, Z.Y. Liu, X.G. Li, and S.Q. Wang, Effects of H2S/HS, on Stress Corrosion Cracking Behavior of X100 Pipeline Steel Under Simulated Sulfate-Reducing Bacteria Metabolite Conditions, J. Mater. Eng. Perform., 2017, 26, p 2763–2775Google Scholar
  7. 7.
    D. Zeng, H. Li, G. Tian, F. Liu, B. Li, S.J. Yue, Z.Y. Ouyang, and T.H. Shi, Fatigue Behavior of High-Strength Steel S135 Under Coupling Multi-Factor in Complex Environments, Mater. Sci. Eng. A, 2018, 724, p 385–402Google Scholar
  8. 8.
    L.W. Tsay, W.Y. Chen, R.K. Shine, and R.H. Shine, Stress Corrosion Cracking of A588 Steel Weldments in Flue Gas Related Environments, J. Mater. Eng. Perform., 2001, 10, p 371–377Google Scholar
  9. 9.
    X.H. Wang, F.P. Li, Y.G. Liu, Y.R. Feng, and L.J. Zhu, A Comprehensive Analysis on the Longitudinal Fracture in the Tool Joints of Drill Pipes, Eng. Fail. Anal., 2017, 79, p 1–7Google Scholar
  10. 10.
    F. Huang, S. Liu, J. Liu, and T.H. Xi, Sulfide Stress Cracking Resistance of the Welded WDL690D HSLA Steel in H2S Environment, Mater. Sci. Eng. A, 2014, 591, p 159–166Google Scholar
  11. 11.
    Z.Y. Liu, X.Z. Wang, R.K. Liu, C.W. Du, and X.G. Li, Electrochemical and Sulfide Stress Corrosion Cracking Behaviors of Tubing Steels in a H2S/CO2 Annular Environment, J. Mater. Eng. Perform., 2014, 23, p 1279–1287Google Scholar
  12. 12.
    F.P. Li, Y.G. Liu, X.H. Wang, and C.H. Lu, Failure Analysis of \( \emptyset \) 127 mm IEU G105 Drill Pipe Wash Out, Eng. Fail. Anal., 2011, 18, p 1867–1872Google Scholar
  13. 13.
    Y. Han, X.H. Zhao, Z.Q. Bai, and C.X. Yin, Failure Analysis on Fracture of a S135 Drill Pipe, Proc. Mater. Sci., 2014, 3, p 447–453Google Scholar
  14. 14.
    S.L. Lv, P.B. Yuan, F.Q. Luo, Y.J. Kang, T. Jiang, and X.T. Yang, Case History Sulfide Stress Cracking of a S135 Drill Pipe, Mater. Perform., 2010, 49, p 66–69Google Scholar
  15. 15.
    M. Gojić, L. Kosec, and L. Vehovar, The Susceptibility to Sulphide Stress Cracking of Low Alloy Steels, Mater. Corros., 1998, 49, p 27–33Google Scholar
  16. 16.
    M.A. Veloz and I.G. Martínez, Effect of Some Pyridine Derivatives on the Corrosion Behavior of Carbon Steel in an Environment Like NACE TM0177, Corrosion, 2006, 62, p 283–292Google Scholar
  17. 17.
    Standard Practice for Slow Strain Rate Testing to Evaluate the susceptibility of metallic materials to environmentally assisted cracking [S]. ASTM G129, 2000.Google Scholar
  18. 18.
    H.C. Ma, Z.Y. Liu, C.W. Du, H.P. Wang, X.G. Li, D.W. Zhang, and Z.Y. Liu, Stress Corrosion Cracking of E690 Steel as a Welded Joint in a Simulated Marine Atmosphere Containing Sulphur Dioxide, Corros. Sci., 2015, 100, p 627–641Google Scholar
  19. 19.
    W.H. Hao, Z.Y. Liu, W. Wu, X.G. Li, C.W. Du, and D.W. Zhang, Electrochemical Characterization and Stress Corrosion Cracking of E690 High Strength Steel in Wet-dry Cyclic Marine Environments, Mater. Sci. Eng. A, 2018, 710, p 318–328Google Scholar
  20. 20.
    T.L. Zhao, Z.Y. Liu, S.S. Hu, C.W. Du, and X.G. Li, Effect of Hydrogen Charging on the Stress Corrosion Behavior of 2205 Duplex Stainless Steel Under 35 wt.% NaCl Thin Electrolyte Layer, J. Mater. Eng. Perform., 2017, 26, p 2837–2846Google Scholar
  21. 21.
    P. Fassina, M.F. Brunella, L. Lazzari, L. Vergani, and A. Sciuccati, Effect of Hydrogen and Low Temperature on Fatigue Crack Growth of Pipeline Steels, Eng. Fract. Mech., 2013, 103, p 10–25Google Scholar
  22. 22.
    B.T. Lu, J.L. Luo, and D.G. Ivey, Near-Neutral pH Stress Corrosion Cracking Susceptibility of Plastically Prestrained X70 Steel Weldment, Metall. Mater. Trans. A, 2010, 41, p 2538–2547Google Scholar
  23. 23.
    R. Wang, Fracture Model of Corrosion Fatigue Crack Propagation, J. Chin. Soc. Corros. Prot., 1998, 18, p 88–94Google Scholar
  24. 24.
    F.L. Sun, S. Ren, Z. Li, Z.Y. Liu, X.G. Liu, and C.W. Du, Comparative Study on the Stress Corrosion cracking of X70 Pipeline Steel in Simulated Shallow and Deep Sea Environments, Mater. Sci. Eng. A, 2016, 685, p 145–153Google Scholar
  25. 25.
    M. Sun, X. Li, and J. Li, Stress Corrosion Cracking Behavior of a New Kind of Ultrahigh Strength Steel Cr12Ni4Mo2Co14 in Acid Environment, Acta. Metall. Sin., 2016, 11, p 1372–1378Google Scholar
  26. 26.
    Z. Zhang, G. Obasis, R. Morana, and M. Preuss, Hydrogen Assisted Crack Initiation and Propagation in a Nickel-Based Superalloy, Acta. Mater., 2016, 113, p 272–283Google Scholar
  27. 27.
    W.K. Hao, Z.Y. Liu, H.C. Ma, C.W. Du, X.G. Li, and S.S. Hu, Stress Corrosion Cracking Behavior of 16 mn Steel and Heat-Affected Zone in Alkaline Sulfide with Different pH Value, J. Mater. Eng., 2015, 43, p 28–34Google Scholar
  28. 28.
    Z.Y. Liu, C.F. Dong, X.G. Li, and L.X. Wang, Effect of Electrochemical Property of UNS J91450 Stainless Steel on Stress Corrosion Cracking in Hydrogen Sulfide Solutions, Electrochemistry, 2009, 15, p 157–162Google Scholar
  29. 29.
    A.H.S. Bueno, E.D. Moreira, and J.A.C.P. Gomes, Evaluation of Stress Corrosion Cracking and Hydrogen Embrittlement in an API, Grade Steel, Eng. Fail. Anal., 2014, 36, p 423–431Google Scholar
  30. 30.
    X.F. Li, J. Zhang, E.J. Akiyama, Q.Z. Li, and Y.F. Wang, Effect of Heat Treatment on Hydrogen-Assisted Fracture Behavior of PH13-8Mo Steel, Corros. Sci., 2017, 128, p 387–392Google Scholar
  31. 31.
    W.J. Hui, Z.B. Xu, Y.J. Zhang, X.L. Zhao, C.G. Shao, and Y.Q. Weng, Hydrogen Embrittlement Behavior of High Strength Rail Steels: A Comparison Between Pearlitic and Bainitic Microstructures, Mater. Sci. Eng. A, 2017, 704, p 199–206Google Scholar
  32. 32.
    J.G.E. Ramírez, R. González, A. Torres-Islas, S. Serna, B. Campillo, G. Dominguez-Patiño, and J.A. Juárez-Islas, Effect of Microstructure on the Sulphide Stress Cracking Susceptibility of a High Strength Pipeline Steel, Corros. Sci., 2008, 50, p 3534–3541Google Scholar

Copyright information

© ASM International 2019

Authors and Affiliations

  1. 1.School of Materials Science and EngineeringXi’an Shiyou UniversityXi’anPeople’s Republic of China
  2. 2.State Key Laboratory for Strength and Vibration of Mechanical StructuresXi’an Jiaotong UniversityXi’anPeople’s Republic of China
  3. 3.MOE Key Laboratory for Multifunctional Materials and StructuresXi’an Jiaotong UniversityXi’anPeople’s Republic of China
  4. 4.Material Corrosion and Protection Key Laboratory of Sichuan provinceSichuan University of Science and EngineeringZigongPeople’s Republic of China

Personalised recommendations