Effects of Co3O4 Addition on Friction and Dry Sliding Wear Characteristics of 8 mol% Yttria-Stabilized Cubic Zirconia

  • Bulent AktasEmail author
  • Hakan Tekin
Article
  • 16 Downloads

Abstract

The aim of the present study was to investigate the influence of Co3O4 additive on the microstructure, wear, and tribological properties of 8 mol% yttria-stabilized cubic zirconia (8YSZ) using a pin-on-disk tribometer, surface profilometer, hardness tester, and a scanning electron microscopy system. Specimens were produced by doping 1-15 wt.% Co3O4 in 8YSZ using a colloidal process, sintering at 1500 °C for 1 h, and subsequent annealing at 1500 °C for 10 and 50 h. Microstructural analysis showed that Co3O4 dissolved partially in 8YSZ, with the undissolved Co3O4 precipitating as a secondary phase at the grain boundaries. Further, the addition of Co3O4 enhanced the grain size. Wear tests were carried out using an Al2O3 ball as the counterface against ceramic disk under dry sliding friction conditions at room temperature (24 °C). The wear volume of 8YSZ decreased from 0.30 to 0.11 mm3 as a result of the addition of 15 wt.% Co3O4. Additionally, friction coefficient of the 8YSZ significantly reduced from 0.55 to 0.17 at the beginning stage of the sliding after the addition of 15 wt.% Co3O4. This was because Co3O4 creates a thin lubricating layer on the friction surface. In addition, the undoped and Co3O4-doped 8YSZ specimens exhibited abrasive wear under the dry sliding friction conditions, owing to the formation and propagation of microcracks, which resulted in the removal of material from the surface. The specific wear rate of 8YSZ decreased with increasing the Co3O4 content. Thus, the addition of Co3O4 to 8YSZ improves its wear resistance and surface topography.

Keywords

8 mol% yttria-stabilized cubic zirconia (8YSZ) dry sliding wear friction solid lubricant Co3O4 

Notes

Acknowledgments

This work was supported by the Scientific Research Projects Commission of Harran University (HUBAK), Sanliurfa, Turkey (Project Number 14150).

References

  1. 1.
    M. Chen, K. Kato, and K. Adachi, Friction and Wear of Self-Mated SiC and Si3N4 Sliding in Water, Wear, 2001, 250(1–12), p 246–255CrossRefGoogle Scholar
  2. 2.
    P. Andersson and A. Blomberg, Alumina in Unlubricated Sliding Point, Pine and Plane Contacts, Wear, 1993, 170(2), p 191–198Google Scholar
  3. 3.
    J. Olofsson, Friction and Wear Mechanisms of Ceramic Surfaces: With Applications to Micro Motors and Hip Joint Replacements, Ph.D. Thesis. Uppsala (Sweden): Uppsala University, 2011Google Scholar
  4. 4.
    M. Valefi, Wear and Friction of Self-Lubricating CuO-TZP Composites, Ph.D. Thesis. Enschede (Netherlands): University of Twente, 2012Google Scholar
  5. 5.
    S. Ran, L. Winnubst, D.H.A. Blank, H.R. Pasaribu, J.W. Sloetjes, and D.J. Schipper, Effect of Microstructure on the Tribological and Mechanical Properties of CuO-Doped 3Y-TZP Ceramics, J. Am. Ceram. Soc., 2007, 90(9), p 2747–2752CrossRefGoogle Scholar
  6. 6.
    S. Ran, L. Winnubst, D.H.A. Blank, J.W. Sloetjes, and D.J. Schipper, Dry-Sliding Self-Lubricating Ceramics: CuO Doped 3Y-TZP, Wear, 2009, 267(9–10), p 1696–1701CrossRefGoogle Scholar
  7. 7.
    J. Song, M. Valefi, M. Rooij, D.J. Schipper, and L. Winnubst, The Effect of an Alumina Counterface on Friction Reduction of CuO/3Y-TZP Composite at Room Temperature, Wear, 2012, 274–275, p 75–83CrossRefGoogle Scholar
  8. 8.
    M. Valefi, M. Rooij, D.J. Schipper, L. Winnubst, and R. Cutler, High-Temperature Tribological and Self-Lubricating Behavior of Copper Oxide-Doped Y-TZP Composite Sliding Against Alumina, J. Am. Ceram. Soc., 2011, 94(12), p 4426–4434CrossRefGoogle Scholar
  9. 9.
    A.S. Shahraki, S.M. Rafiaei, S. Ghadami, and K.A. Nekouee, Densification and Mechanical Properties of Spark Plasma Sintered Si3N4/ZrO2 Nano-Composites, J. Alloys Compd., 2019, 776(5), p 798–806CrossRefGoogle Scholar
  10. 10.
    A. Wojteczko, G. Wiązania, M. Kot, and Z. Pędzich, Friction and Wear of Composites in Alumina/Zirconia System, Compos. Theory Pract., 2018, 18(1), p 51–56Google Scholar
  11. 11.
    N.F. Strey and C. Scandian, Tribological Transitions During Sliding of Zirconia Against Alumina and ZTA in Water, Wear, 2017, 376–377(Part A), p 343–351CrossRefGoogle Scholar
  12. 12.
    H.R. Pasaribu, K.M. Reuver, D.J. Schipper, S. Ran, K.W. Wiratha, A.J.A. Winnubst, and D.H.A. Blank, Environmental Effects on Friction and Wear of Dry Sliding Zirconia and Alumina Ceramics Doped with Copper Oxide, Int. J. Refract. Met. Hard Mater., 2005, 23(4–6), p 386–390CrossRefGoogle Scholar
  13. 13.
    E. Rabinowicz, Friction Wear of Materials, Wiley, New York, 1965Google Scholar
  14. 14.
    B. Aktas and S. Tekeli, Influence of Co3O4 Addition on the Ionic Conductivity and Microstructural Properties of Yttria-Stabilized Zirconia (8YSZ), Int. J. Mater. Res., 2014, 105(6), p 577–583CrossRefGoogle Scholar
  15. 15.
    B. Aktas and S. Tekeli, Effect of Co3O4 on the Fracture Toughness and Microstructure of Yttria-Stabilized Cubic Zirconia (8YSZ), Acta Phys. Pol. A, 2015, 127(4), p 1384–1387CrossRefGoogle Scholar
  16. 16.
    B. Basu, J. Vleugels, and O.V.D. Biest, Microstructure–Toughness–Wear Relationship of Tetragonal Zirconia Ceramics, J. Eur. Ceram. Soc., 2004, 24(7), p 2031–2340CrossRefGoogle Scholar
  17. 17.
    B. Bhushan, Introduction to Tribology, Wiley, New York, 2013CrossRefGoogle Scholar
  18. 18.
    D. Tabor, Fundamentals of Friction: Macroscopic and Microscopic Processes, Springer, Dordrecht, 1992Google Scholar
  19. 19.
    T. Akhadejdamrong, T. Aizawa, M. Yoshitake, A. Mitsuo, T. Yamamoto, and Y. Ikuhara, Self-Lubrication Mechanism of Chlorine Implanted TiN Coatings, Wear, 2003, 254(7–8), p 668–679CrossRefGoogle Scholar
  20. 20.
    T. Aizawa, T. Akhadejdamrong, and A. Mitsuo, Self-Lubrication of Nitride Ceramic Coating by the Chlorine Ion Implantation, Surf. Coat. Technol., 2004, 177–178, p 573–581CrossRefGoogle Scholar
  21. 21.
    D. Jianxin, C. Tongkun, and L. Lili, Self-Lubricating Behaviors of Al2O3/TiB2 Ceramic Tools in Dry High-Speed Machining of Hardened Steel, J. Eur. Ceram. Soc., 2005, 25(7), p 1073–1079CrossRefGoogle Scholar
  22. 22.
    D. Jianxin, C. Tongkun, D. Zeliang, L. Jianhua, S. Junlong, and Z. Jinlong, Tribological Behaviors of Hot-Pressed Al2O3/TiC Ceramic Composites with the Additions of CaF2 Solid Lubricants, J. Eur. Ceram. Soc., 2006, 26(8), p 1317–1323CrossRefGoogle Scholar
  23. 23.
    O.O. Ajayi and K.C. Ludema, Surface Damage of Structural Ceramics: Implications for Wear Modeling, Wear, 1988, 124(2), p 237–257CrossRefGoogle Scholar
  24. 24.
    Y. He, L. Winnubst, A.J. Burggraaf, and H. Verweij, Grain-Size Dependence of Sliding Wear in Tetragonal Zirconia Polycrystals, J. Am. Ceram. Soc., 1996, 79(12), p 3090–3096CrossRefGoogle Scholar
  25. 25.
    K. Kato and K. Adachi, Wear of Advanced Ceramics, Wear, 2002, 253(11–12), p 1097–1104CrossRefGoogle Scholar
  26. 26.
    K.H. ZumGahr and J. Schneider, Surface Modification of Ceramics for Improved Tribological Properties, Ceram. Int., 2000, 26(4), p 363–370CrossRefGoogle Scholar
  27. 27.
    A. Blomberg, M. Olsson, and S. Hogmark, Wear Mechanisms and Tribo Mapping of Al2O3 and SiC in Dry Sliding, Wear, 1994, 171(1–2), p 77–89CrossRefGoogle Scholar

Copyright information

© ASM International 2018

Authors and Affiliations

  1. 1.Department of Mechanical EngineeringHarran UniversitySanliurfaTurkey
  2. 2.Institute of Natural and Applied SciencesHarran UniversitySanliurfaTurkey

Personalised recommendations