Effects of Mg Content on the Fatigue Strength and Fracture Behavior of Al-Si-Mg Casting Alloys

  • Ming-Ze Wu
  • Ji-Wang Zhang
  • Yan-Bin Zhang
  • Hua-Qiang Wang
Article
  • 37 Downloads

Abstract

In order to investigate the influence of Mg content on the fatigue properties in Al-Si-Mg alloy, uniaxial tensile tests and rotating bending fatigue tests were conducted on two Al-7Si-Mg casting alloys, with different Mg contents of 0.3 and 0.6 wt.%. The fracture surfaces of the specimens were observed by scanning electron microscopy, and the fatigue crack growth process was obtained by the replica method. The results indicate that the increase in Mg content enhances the yield strength and tensile strength of the alloy, whereas it reduces its elongation. There is an obvious knee point in the S–N curves of Al-7Si-0.6Mg alloy while that of Al-7Si-0.3Mg alloy shows continuous decrease. The fatigue strength at 5 × 105 cycles is 60 MPa for Al-7Si-0.3Mg alloy and 80 MPa for Al-7Si-0.6Mg alloy. For the two types of specimens, the fatigue failure can initiate from crystal slip and casting defects. The replica results suggest that cracks in Al-7Si-0.6Mg alloy grow more slowly than that in Al-7Si-0.3Mg alloy.

Keywords

Al-7Si-Mg alloys fatigue properties fracture behavior Mg content S–N curve 

Notes

Acknowledgments

This work was supported by National Natural Science Foundation of China (Nos. U1534209, 51675445) and Fundamental Research Funds for the Central Universities (No. 2682017CX039).

References

  1. 1.
    Y.H. Fan, S.H. Liu, and Y. Wang, Application of EN AC-AlSi7Mg0.6 Aluminum Alloy for Railway Contact Network, Hot Working Technol., 2015, 7, p 108–109Google Scholar
  2. 2.
    G.F. Qi, Reflections on Improving the Reliability of Catenary in Passenger Dedicated Line, Chin. Railw., 2005, 9, p 29–31+10Google Scholar
  3. 3.
    W.S. Huo, in Analysis of the Destruction and Influence of Alternating Stress on Catenary Equipment and Components, Excellent Essay Collection of Henan Railway Society in 2007 Academic Month, vol 7 (2007)Google Scholar
  4. 4.
    Y.Q. Liu, W.Q. Jie, S.N. Wang, and H.J. Luo, Investigation of Rotary Bending Gigacycle Fatigue Properties of Al-7Si-0.3Mg Alloys, Chin. J. Mater. Res., 2012, 26(3), p 284–288Google Scholar
  5. 5.
    G. Atxaga, A. Pelayo, and A.M. Irisarri, Effect of Microstructure on Fatigue Behaviour of Cast Al-7Si-Mg Alloy, Mater. Sci. Technol., 2013, 17(4), p 446–450CrossRefGoogle Scholar
  6. 6.
    X.S. Jiang, G.Q. He, and B. Liu, Microstructure-Based Analysis of Fatigue Behaviour of Al-Si-Mg Alloy, Trans. Nonferrous Met. Soc. China, 2011, 21(3), p 443–448CrossRefGoogle Scholar
  7. 7.
    X.S. Jiang, G.Q. He, and B. Liu, Fatigue Behaviour and Microstructure Evolution of Al-Mg-Si Alloy Under Constant and Variable Amplitude Loadings, Rare Met. Mater. Eng., 2010, 39(3), p 459–463Google Scholar
  8. 8.
    X.S. Jiang, G.Q. He, and B. Liu, Fatigue Characteristics and Microcosmic Mechanism of Al-Si-Mg Alloys Under Multiaxial Proportional Loadings, Int. J. Miner. Metall. Mater., 2011, 18(4), p 437CrossRefGoogle Scholar
  9. 9.
    J.Z. Yi, Y.X. Gao, and P.D. Lee, Microstructure-Based Fatigue Life Prediction for Cast A356-T6 Aluminum-Silicon Alloys, Metall. Mater. Trans. B, 2006, 37(2), p 301–311CrossRefGoogle Scholar
  10. 10.
    H. Jiang, P. Bowen, and J.F. Knott, Fatigue Performance of a Cast Aluminum Alloy Al-7Si-Mg with Surface Defects, J. Mater. Sci., 1999, 34(4), p 719–725CrossRefGoogle Scholar
  11. 11.
    D.A. Lados and D. Apelian, Fatigue Crack Growth Characteristics in Cast Al-Si-Mg Alloys: Part I. Effect of Processing Conditions and Microstructure, Mater. Sci. Eng. A, 2004, 385(1), p 200–211Google Scholar
  12. 12.
    D.A. Lados and D. Apelian, Fatigue Crack Growth Characteristics in Cast Al-Si-Mg Alloys: Part II. Life Predictions Using Fatigue Crack Growth Data, Mater. Sci. Eng. A, 2004, 385(1), p 187–199Google Scholar
  13. 13.
    H. Özdeş and M. Tiryakioğlu, On Estimating High-Cycle Fatigue Life of Cast Al-Si-Mg-(Cu) Alloys from Tensile Test Results, Mater. Sci. Eng. A, 2017, 688, p 9–15CrossRefGoogle Scholar
  14. 14.
    A. Mandal, N. Chippa, and K. Jayasankar, Effect of High Magnesium Content on Microstructure of Al-7Si Alloy, Mater. Lett., 2014, 117(7), p 168–170CrossRefGoogle Scholar
  15. 15.
    E.A. Elsharkawi, E. Samuel, and A.M. Samuel, Effects of Mg, Fe, Be Additions and Solution Heat Treatment on the π-AlMgFeSi Iron Intermetallic Phase in Al-7Si-Mg Alloys, J. Mater. Sci., 2010, 45(6), p 1528–1539CrossRefGoogle Scholar
  16. 16.
    C.H. Caceres, C.J. Davidson, and J.R. Griffiths, The Effect of Mg on the Microstructure and Mechanical Behaviour of Al-Si-Mg Casting Alloys, Metall. Mater. Trans. A, 1999, 30(10), p 2611–2618CrossRefGoogle Scholar
  17. 17.
    A. Thirugnanam, K. Sukumaran, and U.T.S. Pillai, Effect of Mg on the Fracture Characteristics of Cast Al-7Si-Mg Alloys, Mater. Sci. Eng. A, 2007, 445–446, p 405–414CrossRefGoogle Scholar
  18. 18.
    Z.W. Chen and W.Q. Jie, Effects of Mg on the Microstructure and Mechanical Property of Al-Si-Mg Casting Alloys, J. Mater. Sci. Eng., 2004, 22(5), p 647–652Google Scholar
  19. 19.
    D.H. Chen, W.S. Huang, and J.J. Tang, Effect of Cu and Mg on Mechanical Properties of Al-Si-Cu-Mg Alloy, Spec. Cast. Nonferrous Alloys, 2011, 31(4), p 367–368Google Scholar
  20. 20.
    H. Möller, G. Govender, and W. Stumpf, Factors Influencing Tensile Mechanical Properties of Al-7Si-Mg Casting Alloys A356/7, Light Met., 2012, 510(1), p 467–471Google Scholar
  21. 21.
    S.A. Kori, M.S. Prabhudev, and T.M. Chandrashekharaiah, Studies on the Microstructure and Mechanical Properties of A356 Alloy with Minor Additions of Copper and Magnesium, Trans. Indian Inst. Met., 2009, 62(4–5), p 353–356CrossRefGoogle Scholar
  22. 22.
    R. Chen, Q.Y. Xu, and H.T. Guo, Correlation of Solidification Microstructure Refining Scale, Mg Composition and Heat Treatment Conditions with Mechanical Properties in Al-7Si-Mg Cast Aluminum Alloys, Mater. Sci. Eng. A, 2016, 685, p 391–402CrossRefGoogle Scholar
  23. 23.
    G. Ran, J.E. Zhou, and Y.F. Wang, Tensile Properties and Fracture Analysis of Casting A356 Aluminum Alloy, Rare Met. Mater. Eng., 2006, 35(10), p 1620–1624Google Scholar
  24. 24.
    J.A. Francis and G.M.D. Cantin, The Role of Defects in the Fracture of an Al-Si-Mg Cast Alloy, Mater. Sci. Eng. A, 2005, 407(1–2), p 322–329CrossRefGoogle Scholar
  25. 25.
    Y. Murakami, Metal Fatigue: Effects of Small Defects and Nonmetallic Inclusions, Yokendo Ltd, Tokyo, 1993Google Scholar
  26. 26.
    F.B.A. Samsol, The Role of Magnesium-Induced Work Hardening on the Fatigue Crack Growth Rate Scatter in new Al6061-T6 Aluminum Alloy, in Ph.D. Thesis, Kyushu University, Japan, 2017.Google Scholar

Copyright information

© ASM International 2018

Authors and Affiliations

  • Ming-Ze Wu
    • 1
  • Ji-Wang Zhang
    • 1
  • Yan-Bin Zhang
    • 2
  • Hua-Qiang Wang
    • 1
  1. 1.State Key Laboratory of Traction PowerSouthwest Jiaotong UniversityChengduChina
  2. 2.School of Mechanical EngineeringSouthwest Jiaotong UniversityChengduChina

Personalised recommendations