Effects of Pouring Temperature and Electromagnetic Stirring on Porosity and Mechanical Properties of A357 Aluminum Alloy Rheo-Diecasting

  • An Guo
  • Junwen Zhao
  • Chao Xu
  • Hu Li
  • Jing Han
  • Xu Zhang
Article
  • 15 Downloads

Abstract

Semisolid slurry of A357 aluminum alloy was prepared using a temperature-controllable electromagnetic stirrer and rheo-diecast at different temperatures. The effects of pouring temperature and electromagnetic stirring (EMS) on the porosity in rheo-diecast samples, as well as the relation between porosity and mechanical properties, were investigated. The results show that pouring temperature and EMS had minor influences on rheo-diecast microstructure but marked influence on the porosity. With decreasing slurry pouring temperature, the porosity decreased first and then increased, whereas the maximum pore ratio (ratio of shape factor to diameter of the largest pore) increased first and then decreased. The maximum pore ratio determines the level of tensile strength and elongation, and higher mechanical properties can be obtained with smaller and rounder pores in samples. The mechanical properties of the rheo-diecast samples increased linearly with increasing maximum pore ratio. The maximum pore ratio was 1.43 µm−1, and the minimum porosity level was 0.37% under EMS condition for the rheo-diecast samples obtained at a pouring temperature of 608 °C. With this porosity condition, the maximum tensile strength and elongation were achieved at 274 MPa and 4.9%, respectively. It was also revealed that EMS improves mechanical properties by reduction in porosity and an increase in maximum pore ratio.

Keywords

A357 aluminum alloy electromagnetic stirring (EMS) mechanical properties porosity pouring temperature rheo-diecast 

Notes

Acknowledgment

This research was supported by National Key Technology Support Program of China (2015BAG12B01).

References

  1. 1.
    J. Campbell, Entrainment Defects, Mater. Sci. Technol., 2006, 22(2), p 127–145CrossRefGoogle Scholar
  2. 2.
    B. Skallerud, T. Iveland, and G. Harkegard, Fatigue Life Assessment of Aluminum Alloys with Casting Defects, Int. J. Fatigue, 1993, 44(6), p 857–874Google Scholar
  3. 3.
    U.T.S. Pillai, B.C. Pai, K.G. Satyanarayana, and A.D. Damodaran, Fracture Behaviour of Pressure Die-Cast Aluminium-Graphite Composites, J. Mater. Sci., 1995, 30(6), p 1455–1461CrossRefGoogle Scholar
  4. 4.
    J.Y. Buffière, S. Savelli, P.H. Jouneau, E. Maire, and R. Fougères, Experimental Study of Porosity and Its Relation to Fatigue Mechanisms of Model Al-Si7-Mg0.3 Cast Al Alloys, Mater. Sci. Eng. A, 2001, 316(1–2), p 115–126CrossRefGoogle Scholar
  5. 5.
    Z.H. Xiao, J.R. Luo, S.S. Wu, D.N. Li, Y.W. Mao, and X.J. Song, Study on a Semi-Solid Rheo-Diecasting Process with AZ91D Alloy Slurry, J. Mater. Eng. Perform., 2004, 13(1), p 60–63CrossRefGoogle Scholar
  6. 6.
    Y.F. Yan and S.M. Xiong, Effects of Casting Pressure Parameters on Porosities and Tensile Strength of a High Pressure Die Cast ADC12Z Alloy, Rare Metal Mater. Eng., 2010, 39(a01), p 219–222 (in Chinese)Google Scholar
  7. 7.
    C. Xu, J.W. Zhao, A. Guo, H. Li, G.Z. Dai, and X. Zhang, Effects of Injection Velocity on Microstructure, Porosity and Mechanical Properties of a Rheo-Diecast Al-Zn-Mg-Cu Aluminum Alloy, J. Mater. Process. Technol., 2017, 249, p 167–171CrossRefGoogle Scholar
  8. 8.
    S.G. Lee, A.M. Gokhale, G.R. Patel, and M. Evans, Effect of Process Parameters on Porosity Distributions in High-Pressure Die-Cast AM50Mg-Alloy, Mater. Sci. Eng. A, 2006, 427(1), p 99–111CrossRefGoogle Scholar
  9. 9.
    Q. Wan, H.D. Zhao, and J.L. Ge, Effect of Micro-Porosities on Fatigue Behavior of Aluminum Die Castings, Chin. J. Nonferrous Met., 2015, 25(3), p 568–574 (in Chinese)Google Scholar
  10. 10.
    X. Sun, K.S. Choi, and D.S. Li, Predicting the Influence of Pore Characteristics on Ductility of Thin-Walled High Pressure Die Casting Magnesium, Mater. Sci. Eng. A, 2013, 572(11), p 45–55CrossRefGoogle Scholar
  11. 11.
    M.K. Surappa, E. Blank, and E. Jaquet, Effect of Macro-Porosity on the Strength and Ductility of Cast Al-7Si-0.3Mg Alloy, Scr. Metall., 1986, 20, p 1281–1286CrossRefGoogle Scholar
  12. 12.
    C.H. Cáceres and B.I. Selling, Casting Defects and Tensile Properties of an Al-Si-Mg Alloy, Mater. Sci. Eng. A, 1996, 220(1), p 109–116CrossRefGoogle Scholar
  13. 13.
    C.D. Lee, Effects of Microporosity on Tensile Properties of A356 Aluminum Alloy, Mater. Sci. Eng. A, 2007, 464(1–2), p 249–254CrossRefGoogle Scholar
  14. 14.
    C. Vives, Electromagnetic Refining of Aluminum Alloys by the CREM Process: Part I. Working Principle and Metallurgical Results, Metall. Trans. B, 1989, 20(5), p 623–629CrossRefGoogle Scholar
  15. 15.
    C. Vives, Elaboration of Semisolid Alloys by Means of New Electromagnetic Rheocasting Processes, Metall. Trans. B, 1992, 23(2), p 189–206CrossRefGoogle Scholar
  16. 16.
    V. Metan, K. Eigenfeld, D. Räbiger, M. Leonhardt, and S. Eckert, Grain Size Control in Al-Si Alloys by Grain Refinement and Electromagnetic Stirring, J. Alloys Compd., 2009, 487(1–2), p 163–172CrossRefGoogle Scholar
  17. 17.
    C. Mapelli, A. Gruttadauria, and M. Peroni, Application of Electromagnetic Stirring for the Homogenization of Aluminium Billet cast in a Semi-Continuous Machine, J. Mater. Process. Technol., 2010, 210(2), p 306–314CrossRefGoogle Scholar
  18. 18.
    D.A. Currey and C.A. Pickles, Electromagnetic Stirring of Aluminium-Silicon Alloys, J. Mater. Sci., 1988, 23(10), p 3756–3763CrossRefGoogle Scholar
  19. 19.
    C.G. Kang and S.M. Lee, The Effect of Solid Fraction and Indirect Forging Pressure on Mechanical Properties of Wrought Aluminum Alloy Fabricated by Electromagnetic Stirring, Int. J. Adv. Manuf. Technol., 2009, 42(1–2), p 73–82CrossRefGoogle Scholar
  20. 20.
    Z. Yang, P.K. Seo, and C.G. Kang, Grain Size Control of Semisolid A356 Alloy Manufactured by Electromagnetic Stirring, J. Mater. Sci. Technol., 2005, 21(2), p 219–225Google Scholar
  21. 21.
    W.M. Mao, Y.L. Bai, and G.X. Tang, Preparation for Semi-Solid Aluminum Alloy Slurry Under Weak Electromagnetic Stirring Conditions, J. Mater. Sci. Technol., 2006, 22(4), p 447–451Google Scholar
  22. 22.
    W.M. Jiang, Z.T. Fan, Y.C. Dai, and C. Li, Effects of Rare Earth Elements Addition on Microstructures, Tensile Properties and Fractography of A357 Alloy, Mater. Sci. Eng. A, 2014, 597(3), p 237–244CrossRefGoogle Scholar
  23. 23.
    Y.C. Tzeng, C.T. Wu, H.Y. Bor, J.L. Horng, M.L. Tsai, and S.L. Lee, Effects of Scandium Addition on Iron-Bearing Phases and Tensile Properties of Al-7Si-0.6Mg Alloys, Mater. Sci. Eng. A, 2014, 593, p 103–110CrossRefGoogle Scholar
  24. 24.
    S. Jana, R.S. Mishra, J.B. Baumann, and G. Grant, Effect of Friction Stir Processing on Fatigue Behavior of an Investment Cast Al-7Si-0.6Mg Alloy, Acta Mater., 2010, 58(3), p 989–1003CrossRefGoogle Scholar
  25. 25.
    J.W. Zhao, A. Guo, H. Li, X. Zhang, J. Han, and S.S. Wu, Semisolid Slurry of 7A04 Aluminum Alloy Prepared by Electromagnetic Stirring and Sc, Zr additions, China Foundry, 2017, 14(3), p 188–193CrossRefGoogle Scholar
  26. 26.
    Y.L. Zhu, J.W. Zhao, W. Li, Z.Y. Zhu, G.Z. Dai, and K. Zhang, Effect of Electromagnetic Stirring on Microstructure of Large-Volume Semi-Solid Slurry of 7A04 Aluminum Alloy, Chin. J. Nonferrous Met., 2014, 24(11), p 2735–2742 (in Chinese)Google Scholar
  27. 27.
    D. Zhao, Y. Wang, D. Liang, and P. Zhang, Modeling and Process Analysis of Resistance Spot Welded DP600 Joints Based on Regression Analysis, Mater. Des., 2016, 110, p 676–684CrossRefGoogle Scholar
  28. 28.
    J.P. Davim, C. Oliveira, and A. Cardoso, Predicting the Geometric Form of Clad in Laser Cladding by Powder Using Multiple Regression Analysis (MRA), Mater. Des., 2008, 29(2), p 554–557CrossRefGoogle Scholar

Copyright information

© ASM International 2018

Authors and Affiliations

  • An Guo
    • 1
  • Junwen Zhao
    • 1
  • Chao Xu
    • 1
  • Hu Li
    • 1
  • Jing Han
    • 1
  • Xu Zhang
    • 2
  1. 1.School of Materials Science and Engineering, Key Lab of Advanced Technologies of Materials (Ministry of Education)Southwest Jiaotong UniversityChengduChina
  2. 2.School of Mechanics and EngineeringSouthwest Jiaotong UniversityChengduChina

Personalised recommendations