Effect of Retrogression Heat Treatment Time on Microstructure and Mechanical Properties of AA7010

Article
  • 58 Downloads

Abstract

The effect of retrogression time during retrogression and re-aging (RRA) treatment of AA7010 is evaluated by performing tensile tests and characterizing the microchemistry of the grain boundary precipitates (GBPs) using transmission electron microscope coupled with the energy-dispersive spectroscopy. Retrogression time is evaluated so that the ultimate tensile strength of the RRA-treated sample is equal to that of the T6-treated sample and the grain boundary microstructure similar to that of the over-aged (T7451) condition. The investigation reveals that the sample retrogressed at 200 °C for 20 min has UTS of 586 MPa which is equivalent to that of the T6 sample and 11.5% higher than that of the T7451 condition. The fracture toughness of the RRA-treated sample was 41 MPa√m. Microstructure of the RRA-treated sample is similar to T7451, along the grain boundaries and in the grain interior similar to that of the T6-treated sample. Energy-dispersive spectroscopy confirmed the increment of Cu content on the GBP’s with increase in the retrogression time, which is expected to improve the stress corrosion cracking resistance of the alloy.

Keywords

fracture toughness GBP peak aging RRA SCC TEM 

Notes

Acknowledgments

Authors are thankful to The Director, NITK, and The Director, CSIR-NAL, for facilitating to conduct this research work and also for their continuous encouragement. One of the authors Mr. Nandana would like to thank the MHRD-Government of India for providing the scholarship grant. The technical staff at the Department of Metallurgical and Materials Engineering, NITK, is thanked for their support.

References

  1. 1.
    Y.L. Wu, F.H. Froes, A. Alvarez, C.G. Li, and J. Liu, Microstructure and Properties of a New Super-High-Strength Al-Zn-Mg-Cu Alloy C912, Mater. Des., 1988, 18, p 211–215CrossRefGoogle Scholar
  2. 2.
    F. Viana, A.M.P. Pinto, H.M.C. Santos, and A.B. Lopes, Retrogression and Re-ageing of 7075 Aluminium Alloy: Microstructural Characterization, J. Mater. Process. Technol., 1999, 92–93, p 54–59CrossRefGoogle Scholar
  3. 3.
    J. Schijve, Fatigue Damage in Aircraft Structures, Not Wanted, But Tolerated?, Int. J. Fatigue, 2009, 31(6), p 998–1011CrossRefGoogle Scholar
  4. 4.
    L.P. Borrego, J.M. Costa, S. Silva, and J.M. Ferreira, Microstructure Dependent Fatigue Crack Growth in Aged Hardened Aluminium Alloys, Int. J. Fatigue, 2004, 26(12), p 1321–1331CrossRefGoogle Scholar
  5. 5.
    M. Puiggali, A. Zielinski, J.M. Olive, E. Renauld, D. Desjardins, and M. Cid, Effect of Microstructure on Stress Corrosion Cracking of an Al-Zn-Mg-Cu Alloy, Corros. Sci., 1998, 40(4–5), p 805–819CrossRefGoogle Scholar
  6. 6.
    H.L. Liao, J.C. Lin, and S.L. Lee, Effect of Pre-immersion on the SCC of Heat-Treated AA7050 in an Alkaline 3.5%NaCl, Corros. Sci., 2009, 51(2), p 209–216CrossRefGoogle Scholar
  7. 7.
    M. Dixit, R.S. Mishra, and K.K. Sankaran, Structure Property Correlations in Al 7050 and Al 7055 High-Strength Aluminum Alloys, Mater. Sci. Eng., A, 2008, 478, p 163–172CrossRefGoogle Scholar
  8. 8.
    P. Rout, M. Ghosh, and K. Ghosh, Microstructural, Mechanical and Electrochemical Behavior of a 7017 Al-Zn-Mg Alloy of Different Tempers, Mater. Charact., 2015, 104, p 49–60CrossRefGoogle Scholar
  9. 9.
    B. Cina, Reducing Stress Corrosion Cracking in Aluminium Alloys, U.S. Patent 3856584, 24 December 1974Google Scholar
  10. 10.
    H. Ji-Wu, W. Tao, Y. Zhi-Min, S. Kai, and L. Jie, Single Ageing Characteristics of 7055 Aluminium Alloy, Trans. Nonferrous Met. Soc. China, 2017, 17, p 548–552Google Scholar
  11. 11.
    X. Chen, Z. Liu, M. Lin, A. Ning, and S. Zeng, Enhanced Fatigue Crack Propagation Resistance in an Al-Zn-Mg-Cu Alloy by Retrogression and Re-agieng Treatment, J. Mater. Eng. Perform., 2012, 21, p 2345–2353CrossRefGoogle Scholar
  12. 12.
    J.S. Robinson, S.D. Whelan, and R.L. Cudd, Retrogression and Re-ageing of 7010 Open Die Forgings, Mater. Sci. Technol., 2013, 15(6), p 717–724CrossRefGoogle Scholar
  13. 13.
    M. Angappan, V. Sampath, B. Ashok, and V.P. Deepkumar, Retrogression and Re-aging Treatment on Short Transverse Tensile Properties of 7010 Aluminium Alloy Extrusions, Mater. Des., 2011, 32, p 4050–4053CrossRefGoogle Scholar
  14. 14.
    A.F. Oliveira, M.C. De Barros, K.R. Cardoso, and D.N. Travessa, The Effect of RRA on the Strength and SCC Resistance on AA7050 and AA7150 Aluminium Alloys, Mater. Sci. Eng., A, 2004, 379, p 321–326CrossRefGoogle Scholar
  15. 15.
    T. Marlaud, A. Deschamps, F. Bley, W. Lefebvre, and B. Baroux, Evolution of Precipitate Microstructures During the Retrogression and Re-ageing Heat Treatment of an Al-Zn-Mg-Cu alloy, Acta Mater., 2010, 58(14), p 4814–4826CrossRefGoogle Scholar
  16. 16.
    J. Buha, R.N. Lumley, and A.G. Crosky, Secondary Ageing in an Aluminium Alloy 7050, Mater. Sci. Eng., A, 2008, 492(1–2), p 1–10CrossRefGoogle Scholar
  17. 17.
    C.F. Meng, H.W. Long, and Y. Zheng, A Study of the Mechanism of Hardness Change of Al-Zn-Mg Alloy During Retrogression Re-ageing Treatments by Small Angle X-Ray Scattering (SAXS), Metall. Mater. Trans. A, 1997, 28(10), p 2067–2071CrossRefGoogle Scholar
  18. 18.
    J.S. Robinson, Influence of Retrogression and Reaging on Fracture Toughness of 7010 Aluminium Alloy, Mater. Sci. Technol., 2003, 19(12), p 1697–1704CrossRefGoogle Scholar
  19. 19.
    J.F. Li, N. Birbilis, C.X. Li, Z.Q. Jia, B. Cai, and Z.Q. Zheng, Influence of Retrogression Temperature and Time on the Mechanical Properties and Exfoliation Corrosion Behavior of Aluminium Alloy AA7150, Mater. Charact., 2009, 60(11), p 1334–1341CrossRefGoogle Scholar
  20. 20.
    J.F. Li, Z.Q. Zheng, S.C. Li, W.J. Chen, W.D. Ren, and X.S. Zhao, Simulation Study on Function Mechanism of Some Precipitates in Localized Corrosion of Al Alloys, Corros. Sci., 2007, 49(6), p 2436–2449CrossRefGoogle Scholar
  21. 21.
    P. Xia, Z. Liu, S. Bai, L. Lu, and L. Gao, Enhanced Fatigue Crack Propagation Resistance in a Super High Strength Al-Zn-Mg-Cu Alloy by Modifying RRA Treatment, Mater. Charact., 2016, 118, p 438–445CrossRefGoogle Scholar
  22. 22.
    M.N. Desmukh, R.K. Pandey, and A.K. Mukhopadhyay, Effect of Aging Treatments on the Kinetics of Fatigue Crack Growth in 7010 Aluminum Alloy, Mater. Sci. Eng., A, 2006, 435–436, p 318–326CrossRefGoogle Scholar

Copyright information

© ASM International 2018

Authors and Affiliations

  • M. S. Nandana
    • 1
  • K. Udaya Bhat
    • 1
  • C. M. Manjunatha
    • 2
  1. 1.Department of Metallurgical and Materials EngineeringNational Institute of Technology KarnatakaSurathkalIndia
  2. 2.Structural Technologies DivisionCSIR-National Aerospace LaboratoriesBangaloreIndia

Personalised recommendations