Thermodynamics of the Sn-In-Ag solder system
- 436 Downloads
- 46 Citations
Abstract
The lead-free solder system Sn-In-Ag was studied both experimentally and by thermodynamic modeling. Thermodynamic descriptions for the phases in Ag-In and In-Sn binary systems were optimized taking into account the available thermodynamic and phase equilibria data. They were combined with the previously assessed Ag-Sn binary system to get a complete thermodynamic description of the Sn-In-Ag system. The thermodynamic functions obtained are used to model the solidifying behavior of the alloys with diagrams of the relative amount of phases (microstructures) as a function of temperature and the effect of diffusional segregation on the solidification path. The solidification of alloys of different compositions and its relevance to the microstructure and mechanical properties of the solidified solder are discussed. In the experimental research, alloys of different compositions were heat treated and analyzed by differential scanning calorimetry (DSC), optical microscopy, and scanning electron microscopy/electron probe microanalysis techniques. Ternary alloys were annealed at 250°C to gain information about the location of the phase boundaries at this rather typical soldering temperature. Diffusion couple experiments were performed to investigate the interfacial reaction between Ag and binary SnIn and to find out the diffusion paths taken by the system. The melting/solidification behavior of the alloys in the Sn corner of the ternary diagram were investigated by DSC. It was discovered that a strong segregation takes place during the cooling of some In-containing solder alloys as the In component is rejected from the solid with an excess of In remaining in the liquid. At high enough In concentrations (>16%), this results in partial melting of the solder at temperatures in excess of 113°C.
Key words
Pb-free solder phase diagrams thermodynamic modelingPreview
Unable to display preview. Download preview PDF.
References
- 1.U.R. Kattner and W.J. Boettinger, J. Electron. Mater. 23, 603 (1994).Google Scholar
- 2.W.J. Tomlinson and I. Collier, J. Mater. Sci. 22, 1835 (1987).CrossRefGoogle Scholar
- 3.I. Karakaya and W.T. Thompson, Bull. Alloy Phase Diagrams 8, 340 (1987).Google Scholar
- 4.P.-Y. Chevalier, Thermochim. Acta 136, 45 (1988).CrossRefGoogle Scholar
- 5.A.T. Dinsdale, CALPHAD 15, 317 (1991).CrossRefGoogle Scholar
- 6.O. Redlich, A. Kister, Ind. Eng. Chem. 40, 3618 (1948).Google Scholar
- 7.Y.-M. Muggianu, M. Gambino and J.-P. Bros, J. Chim. Phys. 72, 85 (1975).Google Scholar
- 8.B.-J. Lee, C.-S. Oh and J.H. Shim, J. Electron. Mater. 25, 983 (1998).Google Scholar
- 9.M.R. Baren, Phase Diagrams of Indium Alloys and Their Engineering Applications, eds. C.E.T. White and H. Okamoto (Materials Park, OH: ASM Intl., 1992), p. 15.Google Scholar
- 10.F. Weibke and H. Eggers, Z. Anorg. Chem. 222, 145 (1935).CrossRefGoogle Scholar
- 11.A.N. Campbell, R Wageman and R.B. Ferguson, Can. J. Chem. 48, 1703 (1970).CrossRefGoogle Scholar
- 12.C.B. Alcock, R. Sridhar and R.C. Svedberg, Acta Met. 17, 839 (1969).CrossRefGoogle Scholar
- 13.G. Qi, M. Hino and T. Azakami, Mater. Trans. JIM 30, 575 (1989).Google Scholar
- 14.K Kameda, Y. Toshida and S. Sakairi, J. Jpn. Inst. Metals 45, 614 (1981).Google Scholar
- 15.T. Nozaki, M. Shimoji and K. Niwa, Trans. Jpn. Inst. Metals 7, 52 (1966).Google Scholar
- 16.R. Castanet, Y. Clair and M. Laffitte, J. Chim. Phys. 67, 789 (1970).Google Scholar
- 17.R. Beja and M. Laffitte, C.R. Acad. Sci. 267C, 123 (1968).Google Scholar
- 18.O.J. Kleppa, J. Phys. Chem. 60, 846 (1956).CrossRefGoogle Scholar
- 19.D.B. Masson and S.S. Prahad, Metall. Trans. A 4, 991 (1973).Google Scholar
- 20.C.B. Alcock, K.R. Jacob and T. Palamutcu, Acta Metall. 21, 1003 (1973).CrossRefGoogle Scholar
- 21.H. Okamoto, Phase Diagrams of Indium Alloys and Their Engineering Applications, eds. C.E.T. White and H. Okamoto (Materials Park, OH: ASM Intl., 1992), p. 255.Google Scholar
- 22.T. Heumann and O. Alpaut, J. Less-Common Metals 6, 108 (1964).CrossRefGoogle Scholar
- 23.B. Predel and T. Godecke, Z. Metallkd. 66, 654 (1975).Google Scholar
- 24.O. Cakir and O. Alpaut, J. Less Common Metals 141, 11 (1988).CrossRefGoogle Scholar
- 25.J.P. Bros and M. Laffitte, J. Chem. Thermodynamics 2, 151 (1970).CrossRefGoogle Scholar
- 26.F.E. Wittig and P. Scheidt, Z. Phys. Chem. 28, 120 (1961).Google Scholar
- 27.O.J. Kleppa, J. Phys. Chem. 60, 842 (1956).CrossRefGoogle Scholar
- 28.J. Terpilowski and E. Przezdziecka-Mycielska, Arch. Hutn. 5, 281 (1960).Google Scholar
- 29.O. Alpaut and T. Heumann, Acta Metall. 13, 543 (1965).CrossRefGoogle Scholar
- 30.R. Hultgren, P. Desai, D. Hawkins, M. Gleiser, K. Kelley, Selected Values of the Thermodynamic Properties of Binary Alloys, (Materials Park, OH: ASM Intl., 1973), p. 1031.Google Scholar
- 31.P.-Y. Chevalier, CALPHAD 12, 383 (1988).CrossRefGoogle Scholar
- 32.J.P. Nabot and I. Ansara, Bull. Alloy Phase Diagrams 8, 246 (1987).Google Scholar
- 33.V.J. Kuck, Thermochimica Acta 99, 233 (1986).CrossRefGoogle Scholar
- 34.I. Artaki, A.M. Jackson and P.T. Vianco, Soldering and Surface Mount Technology 20, 27 (1995).Google Scholar