Abstract
The thermal effect of the growth temperature on interface morphology and stimulated emission in ultraviolet AlGaN/InGaN multiple quantum wells (MQWs) are experimentally investigated. During the MOCVD epitaxial growth of AlGaN/InGaN MQWs, the ramping rate from a lower temperature for InGaN quantum wells (QWs) to a higher one for AlGaN quantum barriers (QBs) is intentionally changed from 1.0°C/s to 4.0°C/s. Atomic force microscopy images show that the surface morphology of InGaN QWs, which is improved by a thermal effect when the growth temperature rises to the set value of the AlGaN QBs, varies with different temperature ramping rates. The results of stimulated emission indicate that the threshold pumping power density of MQWs is decreased with increasing temperature ramping rate from 1.0°C/s to 3.0°C/s and then slightly increased when the ramping rate is 4.0°C/s. This phenomenon is believed to result from the thermal degradation effect during the temperature ramp step. A long-time high-temperature annealing will reduce the density of indium-rich microstructures as well as the corresponding localized state density, which is assumed to contribute to the radiative recombination in the InGaN QWs. Given the great difference between optimal growth temperatures for AlGaN and InGaN layers, a higher ramping rate would be more appropriate for the growth of ultraviolet AlGaN/InGaN MQWs.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
I. Akasaki and H. Amano, Jpn. J. Appl. Phys. 36, 5393 (1997).
R.D. Dupuis and M.R. Krames, IEEE J. Lightwave Technol. 26, 1154 (2008).
M.T. Hardy, D.F. Feezell, S.P. DenBaars, and S. Nakamura, Mater. Today 14, 408 (2011).
M. Razeghi, IEEE Photonics J. 3, 263 (2011).
I. Akasaki, S. Sota, H. Sakai, T. Tanaka, M. Koike, and H. Amano, Electron. Lett. 32, 1105 (1996).
Y. Taniyasu, M. Kasu, and T. Makimoto, Nature 441, 325 (2006).
A. Khan, K. Balakrishnan, and T. Katona, Nat. Photonics 2, 77 (2008).
M. Kneissl, T. Kolbe, C. Chua, V. Kueller, N. Lobo, J. Stellmach, A. Knauer, H. Rodriguez, S. Einfeldt, Z. Yang, N.M. Johnson, and M. Weyers, Semicond. Sci. Technol. 26, 014036 (2011).
D.G. Zhao, J. Yang, Z.S. Liu, P. Chen, J.J. Zhu, D.S. Jiang, Y.S. Shi, H. Wang, L.H. Duan, L.Q. Zhang, and H. Yang, J. Semicond. 38, 051001 (2017).
S.H. Baek, J.H. Kim, M.K. Kwon, I.K. Park, S.I. Na, J.Y. Kim, B.J. Kim, and S.J. Park, IEEE Photonics Technol. Lett. 18, 1276 (2006).
A. Knauer, H. Wenzel, T. Kolbe, S. Einfeldt, M. Weyers, M. Kneissl, and G. Tränkle, Appl. Phys. Lett. 92, 191912 (2008).
Y.-S. Liu, A.F.M.S. Haq, K. Mehta, T.-T. Kao, S. Wang, H.E. Xie, S.-C. Shen, P.D. Yoder, F.A. Ponce, T. Detchprohm, and R.D. Dupuis, Appl. Phys. Express 9, 111002 (2016).
K. Mehta, Y.-S. Liu, J.L. Wang, H. Jeong, T. Detchprohm, Y.J. Park, S.R. Alugubelli, S. Wang, F.A. Ponce, S.-C. Shen, R.D. Dupuis, and P.D. Yoder, IEEE J. Quantum Electron. 54, 2400507 (2018).
M.X. Feng, Z.C. Li, J. Wang, R. Zhou, Q. Sun, X.J. Sun, D.B. Li, H.W. Gao, Y. Zhou, S.M. Zhang, D.Y. Li, L.Q. Zhang, J.P. Li, H.B. Wang, M. Ikeda, X.H. Zheng, and H. Yang, ACS Photonics 5, 699 (2018).
Y.T. Moon, D.J. Kim, K.M. Song, C.J. Choi, S.H. Han, T.Y. Seong, and S.J. Park, J. Appl. Phys. 89, 6514 (2001).
J.Z. Hu, L.Q. Yang, and M.W. Shin, J. Phys. D Appl. Phys. 41, 035107 (2008).
Z.C. Li, J.P. Liu, M.X. Feng, K. Zhou, S.M. Zhang, H. Wang, D.Y. Li, L.Q. Zhang, D.G. Zhao, D.S. Jiang, H.B. Wang, and H. Yang, Appl. Phys. Lett. 103, 152109 (2013).
S. Ruffenach-Clur, O. Briot, J.L. Rouvière, B. Gil, and R.L. Aulombard, Mater. Sci. Eng. B 50, 219 (1997).
J.C. Rojo, L.J. Schowalter, R. Gaska, M. Shur, M.A. Khan, J. Yang, and D.D. Koleske, J. Cryst. Growth 240, 508 (2002).
M. Takeuchi, H. Shimizu, R. Kajitani, K. Kawasaki, T. Kinoshita, K. Takada, H. Murakami, Y. Kumagai, A. Koukitu, T. Koyama, S.F. Chichibu, and Y. Aoyagi, J. Cryst. Growth 305, 360 (2007).
D.G. Zhao, D.S. Jiang, L.L. Wu, L.C. Le, L. Li, P. Chen, Z.S. Liu, J.J. Zhu, H. Wang, S.M. Zhang, and H. Yang, J. Alloys Compd. 544, 94 (2012).
X.H. Li, Y.O. Wei, S. Wang, H.E. Xie, T.-T. Kao, M.M. Satter, S.-C. Shen, P.D. Yoder, T. Detchprohm, R.D. Dupuis, A.M. Fischer, and F.A. Ponce, J. Cryst. Growth 414, 76 (2015).
S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, Appl. Phys. Lett. 70, 2822 (1997).
Y. Narukawa, Y. Kawakami, M. Funato, S. Fujita, S. Fujita, and S. Nakamura, Appl. Phys. Lett. 70, 981 (1997).
H. Hirayama, S. Tanaka, P. Ramvall, and Y. Aoyagi, Appl. Phys. Lett. 72, 1736 (1998).
R.A. Oliver, S.E. Bennett, T. Zhu, D.J. Beesley, M.J. Kappers, D.W. Saxey, A. Cerezo, and C.J. Humphreys, J. Phys. D Appl. Phys. 43, 354003 (2010).
D.G. Zhao, D.S. Jiang, L.C. Le, L.L. Wu, L. Li, J.J. Zhu, H. Wang, Z.S. Liu, S.M. Zhang, Q.J. Jia, and H. Yang, J. Alloys Compd. 540, 46 (2012).
C.-H. Lu, Y.-C. Li, Y.-H. Chen, S.-C. Tsai, Y.-L. Lai, Y.-L. Li, and C.-P. Liu, J. Alloys Compd. 555, 250 (2013).
H. Jeong, H.J. Jeong, H.M. Oh, C.-H. Hong, E.-K. Suh, G. Lerondel, and M.S. Jeong, Sci. Rep. 5, 9373 (2015).
J. Yang, D.G. Zhao, D.S. Jiang, P. Chen, J.J. Zhu, Z.S. Liu, J.P. Liu, L.Q. Zhang, H. Yang, Y.T. Zhang, and G.T. Du, J. Alloys Compd. 681, 522 (2016).
Y. Xing, D.G. Zhao, D.S. Jiang, Z.S. Liu, J.J. Zhu, P. Chen, J. Yang, W. Liu, F. Liang, S.T. Liu, L.Q. Zhang, W.J. Wang, M. Li, Y.T. Zhang, and G.T. Du, Superlattices Microstruct. 117, 228 (2018).
Acknowledgments
This work is partially supported by the US Defense Advanced Research Projects Agency, the Steve W. Chaddick Endowed Chair in Electro-Optics, the Georgia Research Alliance, and the National Natural Science Foundation of China (61674139). This work was performed in part at the Georgia Tech Institute for Electronics and Nanotechnology, a member of the National Nanotechnology Coordinated Infrastructure (NNCI), which is supported by the National Science Foundation (Grant ECCS-1542174).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Chen, P., Park, Y.J., Liu, YS. et al. Epitaxial Growth and Optically Pumped Stimulated Emission in AlGaN/InGaN Ultraviolet Multi-Quantum-Well Structures. J. Electron. Mater. 49, 2326–2331 (2020). https://doi.org/10.1007/s11664-019-07932-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-019-07932-x