Annealing Impact on Interface Properties of Sprayed Al2O3-Based MIS Structure for Silicon Surface Passivation

  • L. ZougarEmail author
  • S. Sali
  • S. Kermadi
  • A. Boucheham
  • M. Boumaour
  • M. Kechouane
Article
  • 9 Downloads

Abstract

Aluminum oxide (Al2O3) films of different thicknesses were deposited on quartz and silicon (100) substrates by an ultrasonic spray method from a solution of aluminum acetylacetonate dissolved in N,N-dimethylformamide with different molar concentrations. The optical, morphological and electrical properties were investigated. Increasing the molar concentration leads to a refractive index decrease, an increase in the optical band gap from 5.26 eV to 5.52 eV and a change in the surface roughness of the films. The electrical parameters at the Al2O3/Si interface such as the flat band voltage (VFB), effective charge density (Qeff) and interface trap density (Dit) were explored as a function of the molar concentration, film thickness and heat treatment. The latter, done by two annealing processes, namely, the post deposition annealing (PDA) and post metallization annealing (PMA) on the structure, lead to remarkable interface properties. It was found that the positive flat band voltage VFB shift is correlated with the generation of negative effective charge during PMA. A decrease of the Dit distribution in the PMA samples with no significant effect in the case of PDA samples was clearly observed for different molar concentrations. Furthermore, as the Al2O3 film thickness decreases, Dit decreases in both PDA and PMA samples while the relatively high density Qeff and its negative charge polarity were obtained for thinner films. A noticeable passivation effect on the Al2O3/Si interface has been confirmed on samples that underwent the annealing process. These findings related specifically to the interface properties are promising for silicon surface passivation, in particular for solar cells applications.

Keywords

Al2O3 ultrasonic spray post-deposition annealing  post-metallization annealing surface passivation 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Notes

Acknowledgments

This work was supported by the National Research Funds (DG-RSDT/MESRS- Algeria).

References

  1. 1.
    W. Fuessel, M. Schmidt, H. Angermann, G. Mende, and H. Flietner, Nucl. Instrum. Methods Phys. Res. A 377, 177 (1996).CrossRefGoogle Scholar
  2. 2.
    H. Mäckle and R. Lüdemann, J. Appl. Phys. 92, 2602 (2002).CrossRefGoogle Scholar
  3. 3.
    J. Hong, W.M.M. Kessels, W.J. Soppe, A.W. Weeber, W.M. Arnoldbik, and M.C.M. van de Sanden, J. Vac. Sci. Technol. B 21, 2123 (2003).CrossRefGoogle Scholar
  4. 4.
    J. Seiffe, L. Gautero, M. Hofmann, J. Rentsch, R. Preu, S. Weber, and R.A. Eichel, J. Appl. Phys. 109, 034105 (2011).CrossRefGoogle Scholar
  5. 5.
    M. Schaper, J. Schmidt, H. Plagwitz, and R. Berndel, Prog. Photovolt. 13, 381 (2005).CrossRefGoogle Scholar
  6. 6.
    S. de Wolf, B. Demaurex, A. Descoeudres, and C. Ballif, Phys. Rev. B 83, 233301 (2011).CrossRefGoogle Scholar
  7. 7.
    B. Hoex, S.B.S. Heil, E. Langereis, M.C.M. van de Sanden, and W.M.M. Kessels, Appl. Phys. Lett. 89, 042112 (2006).CrossRefGoogle Scholar
  8. 8.
    J. Schmidt, A. Merkle, R. Brendel, B. Hoex, M.C.M. van de Sanden, and W.M.M. Kessels, Prog. Photovolt. Res. Appl. 16, 461 (2008).CrossRefGoogle Scholar
  9. 9.
    B. Hoex, J. Schmidt, P. Pohl, M.C.M. van de Sanden, and W.M.M. Kessels, J. Appl. Phys. 104, 044903 (2008).CrossRefGoogle Scholar
  10. 10.
    G. Agostinelli, A. Delabie, P. Vitanov, Z. Alexieva, H.F.W. Dekkers, S. De Wolf, and G. Beaucarne, Sol. Energy Mat. Sol. Cells 90, 3438 (2006).CrossRefGoogle Scholar
  11. 11.
    T. Murayama and T. Nakai, Appl. Phys. Lett. 58, 2079 (1991).CrossRefGoogle Scholar
  12. 12.
    A.C. Jones, D.J. Hoalton, and S.A. Rushworth, J. Phys. 5, 557 (1995).Google Scholar
  13. 13.
    N. Ozer, J.P. Cronin, Y. Yao, and A.P. Tomson, Sol. Energy Mater. Sol. Cells 59, 355 (1999).CrossRefGoogle Scholar
  14. 14.
    S. Mansour, G.N. Al-Robaee, K. Subbanna, N. Rao, and S. Mohan, Vacuum 45, 97 (1994).CrossRefGoogle Scholar
  15. 15.
    T.A. Li, S. Ruffell, M. Tucci, Y. Mansoulie, C. Samundsett, S. De Iullis, L. Serenelli, and A. Cuevas, Sol. Energy Mater. Sol. Cells 95, 69 (2011).CrossRefGoogle Scholar
  16. 16.
    M. Aguilar-Frutis, M. Garcia, and C. Falcony, Appl. Phys. Lett. 72, 1700 (1998).CrossRefGoogle Scholar
  17. 17.
    M. Agular-Frutis, M. Garcia, C. Falcony, G. Plesch, and S. Jimenez-Sandoval, Thin Solid Films 389, 200 (2001).CrossRefGoogle Scholar
  18. 18.
    K.S. Shamala, L.C.S. Murthy, and K. Narasimha Raob, Mater. Sci. Eng. B 106, 269 (2004).CrossRefGoogle Scholar
  19. 19.
    J. Lappalainen, J. Hiltunen, and V. Lantto, J. Eur. Ceram. Soc. 25, 2273 (2005).CrossRefGoogle Scholar
  20. 20.
    B.P. Dhonge, T. Mathews, S. Tripura Sundari, C. Thinaharan, M. Kamruddin, S. Dash, and A.K. Tyagi, Appl. Surf. Sci. 258, 1091 (2011).CrossRefGoogle Scholar
  21. 21.
    J. Tauc, R. Grigorovici, and A. Vancu, Phys. Status Solidi B 15, 627 (1966).CrossRefGoogle Scholar
  22. 22.
    S.D. Mo and W.Y. Ching, Phys. Rev. B 57, 15297 (1997).Google Scholar
  23. 23.
    I. Costina and R. Franchy, Appl. Phys. Lett. 78, 4139 (2001).CrossRefGoogle Scholar
  24. 24.
    F. Urbach, Phys. Rev. 92, 1324 (1953).CrossRefGoogle Scholar
  25. 25.
    S. Riaz, S. Rehman, M. Abutalib, and S. Naseem, J. Elecron. Mater. 45, 5185 (2016).CrossRefGoogle Scholar
  26. 26.
    E. H. Nicollian and. J. R. Brews, MOS (Metal Oxide Semiconductor) Physics and Technology (New York: Wiley, 1982)Google Scholar
  27. 27.
    E.H. Nicollian and A. Goetzberger, Appl. Phys. Lett. 7, 216 (1965).CrossRefGoogle Scholar
  28. 28.
    N. Konofaos, E.K. Evangelou, Z. Wang, V. Kugler, and U. Helmersson, J. Non-Crystal Solids 303, 185 (2002).CrossRefGoogle Scholar
  29. 29.
    S. Dauwe, J. Schmidt, A. Metz, and R. Hezel. 29th IEEE Photovoltaic Specialists Conference, p. 162 (2002).Google Scholar
  30. 30.
    B.E. Deal, M. Sklar, A.S. Grove, and E.H. Snow, J. Electrochem. Soc. 114, 266 (1967).CrossRefGoogle Scholar
  31. 31.
    Q.-H. Luc, E.Y. Chang, H.-D. Trinh, H.-Q. Nguyen, B.-T. Tran, and Y.C. Lin, Jpn. J. Appl. Phys. 53, 04EF04-1 (2014).CrossRefGoogle Scholar
  32. 32.
    R.S. Johnson, G. Lucovski, and I. Baumvol, J. Vac. Sci. Technol. A 19, 1353 (2001).CrossRefGoogle Scholar
  33. 33.
    K. Kimoto, Y. Matsui, T. Nabatame, T. Yasuda, T. Mizoguchi, I. Tanaka, and A. Toriumi, Appl. Phys. Lett. 83, 4306 (2003).CrossRefGoogle Scholar
  34. 34.
    Y.L. Ren, N.M. Nursam, D. Wang, and K.J. Weber. 35th IEEE Photovoltaic Specialists Conference, p. 897 (2010).Google Scholar
  35. 35.
    K. Matsunaga, T. Tanaka, T. Yamamoto, and Y. Ikuhara, Phys. Rev. B 68, 085110 (2003).CrossRefGoogle Scholar
  36. 36.
    M. Yun, M.-S. Kim, Y.-D. Ko, T.-H. Moon, J.-H. Hong, J.-M. Myoung, and I. Yun, Microelectron. Eng. 77, 48 (2005).CrossRefGoogle Scholar
  37. 37.
    G. Dingemans, R. Seguin, P. Engelhart, M.C.M. van de Sanden, and W.M.M. Kessels, Phys. Status Solidi 4, 10 (2010).Google Scholar
  38. 38.
    F. Werner, B. Veith, D. Zielke, L. Kuhnemund, C. Tegenkamp, M. Seibt, R. Brendel, and J. Schmidt, J. Appl. Phys. 109, 113701 (2011).CrossRefGoogle Scholar
  39. 39.
    N.M. Terlinden, G. Dingemans, M.C.M. van de Sanden, and W.M.M. Kessels, Appl. Phys. Lett. 96, 112101 (2010).CrossRefGoogle Scholar
  40. 40.
    W.M.M. Kessels, J.A. Van Delft, G. Dingemans, and M.M. Mandoc. c-Si Workshop. Breckenridge, USA (2011).Google Scholar
  41. 41.
    J. Albohn, W. Füssel, N.D. Sinh, K. Kliefoth, and W. Fuhs, J. Appl. Phys. 88, 842 (2000).CrossRefGoogle Scholar
  42. 42.
    R. Kotipalli, R. Delamare, F. Henry, J. Proost, and D. Flandre, 28th European Photovoltaic Solar Energy Conference and exhibition (EU PVSEC 2013) Google Scholar
  43. 43.
    F. Werner and J. Schmidt, Appl. Phys. Lett. 104, 091604 (2014).CrossRefGoogle Scholar
  44. 44.
    S.M. Sze and K.K. Ng, Physics of Semiconductor Devices (NJ: Hoboken, 2006), p. 197.Google Scholar
  45. 45.
    E.H. Nicollian and A. Gotzberger, Bell Syst. Technol. J. 46, 1055 (1967).CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2018

Authors and Affiliations

  • L. Zougar
    • 1
    Email author
  • S. Sali
    • 1
  • S. Kermadi
    • 1
  • A. Boucheham
    • 1
  • M. Boumaour
    • 1
  • M. Kechouane
    • 2
  1. 1.Research Center in Semiconductors Technology for EnergyDivision DDCSAlgiersAlgeria
  2. 2.Faculty of PhysicsHouari Boumediene UniversityEl Alia, AlgiersAlgeria

Personalised recommendations