Effect of copper seed aging on electroplating-induced defects in copper interconnects
- 175 Downloads
- 6 Citations
Abstract
Voids in copper thin films, observed after electroplating, have been linked to seed aging that occurs when a wafer is exposed, over time, to clean-room ambient. Oxidation of the copper seed surface prevents wetting during subsequent copper electroplating, leading to voids. Several surface treatments were employed to counteract the seed aging effect, including reduction of the copper oxide film by hydrogen, reverse plating of the copper surface, and rinsing the wafer surface with electrolyte. Each treatment was applied to wafers increasingly aged from 2 to 14 days, just prior to electroplating. Results showed a significant decrease in postelectroplating defects with all three treatments. The reduction of copper oxide by hydrogen exhibited the most marked results. An increase in surface wetting is shown by a decrease in contact angle measurements and an increase in film reflectivity for treated versus untreated copper wafers. This study shows that, although the copper surface exhibits strong aging effects over a short period of time, using proper surface treatments can eliminate such effects and voids.
Key words
Copper thin films interconnects electroplating defects wetting behavior seed aging surface treatmentPreview
Unable to display preview. Download preview PDF.
References
- 1.S. Ventakesan et al., Proc. IEEE-IEDM 97, 769 (1997).Google Scholar
- 2.D. Edelstein et al., Proc. IEEE-IEDM 97, 773 (1997).Google Scholar
- 3.R. Mikkola et al., Proc. IEEE-IEDM 99, 117 (1999).Google Scholar
- 4.J. Dini, in Modern Electroplating, ed. M. Schelsinger and M. Paunovic (New York: John Wiley & Sons, 2000), pp. 61–139.Google Scholar
- 5.M. Oh, D. Ramappa, D. Contestable-Gilkes, S.M. Merchant, D.E. Jones, K. Subramanian, and S.A. Lytle, Proc. Advanced Metallization Conf. 2001, ed. A.J. McKerrow et al. (Warrendale, PA: MRS Publications, 2002), pp. 85–89.Google Scholar
- 6.J. Lu et al., Proc. IEEE-IITC 280 (2001).Google Scholar
- 7.D. Contestable-Gilkes, S.M. Merchant, and M. Oh, Semiconductor FabTech, 15th ed. (London: ICG Publ. Ltd., 2002), pp. 157–162.Google Scholar