Effect of Mechanical Activation Treatment on the Recovery of Vanadium from Converter Slag
- 345 Downloads
The high roasting temperature and low leaching efficiency of vanadium from vanadium-bearing converter slag are regarded as the main factors significantly influencing the application of calcification roasting–acid leaching processes in the cleaner production of vanadium. In this study, a mechanical activation treatment was performed to enhance the extraction of vanadium from converter slag. The enhancement effects obtained from mechanical activation were comprehensively evaluated through indices such as the roasting temperature and leaching efficiency. The effects of mechanical activation time, roasting temperature, leaching temperature, solid to liquid ratio, particle size, and acid concentration on the leaching efficiency were investigated. Microstructure morphology and elemental analyses of the raw materials and leaching residue were also investigated using scanning electron microscopy and energy-dispersive X-ray spectroscopy. The results demonstrated that the mechanical activation significantly decreased the optimum roasting temperature from 1173 K to 1073 K (900 °C to 800 °C) and increased the leaching efficiency from 86.0 to 90.9 pct.
This work was supported by the Natural Science Foundation of China [Grant Numbers 51404047 and 51234010] and the Basic and Frontier Research Program of Chongqing [Grant Number cstc2014jcyjA50011].
- 3.B. Raja: Steelworld, 2007, vol. 13, pp. 19–22.Google Scholar
- 10.J.X. Liu, L.J. Li, S.L. Zheng, S.N. Wang, H. Du, and H.Y. Xie: The Chinese Journal of Process Engineering, 2014, vol. 14, pp. 763–769.Google Scholar
- 11.C.K. Gupta, and N. Krishnamurthy: Extractive metallurgy of vanadium, Elsevier Science Publishers B. V, P. O. Box 211, 1000 AE Amsterdam, The Netherlands, 1992, pp. 203.Google Scholar
- 12.H.S. Chen: Iron Steel Vanadium Titanium, 1992, vol. 13, pp. 1–9.Google Scholar
- 13.D.F. Yin, Y. Peng, Z.H. Sun, and W.Y. He: Metal Mine, 2012, vol. 4, pp. 91–94.Google Scholar
- 14.J.H. Zhang, W. Zhang, L. Zhang, and S.Q. Gu: Journal of Northeastern University (Nature Science), 2014, vol. 35, pp. 1574–1577.Google Scholar
- 16.N.J. Welham: CIM bulletin, 1997, vol. 90, pp. 64–68.Google Scholar
- 17.P. Balaz: Mechanochemistry in Nanoscience and Minerals Engineering, Springer, 2008, pp. 257–92.Google Scholar
- 18.A.L. Vogel: Quantitative Inorganic Analysis, 5nd ed., John Willey and Sons Inc, New York, USA, 1989, pp. 646.Google Scholar