Wear Performance Analysis of Aluminum Matrix Composites and Optimization of Process Parameters Using Statistical Techniques
- 54 Downloads
This paper presents the wear behavior of gears manufactured using Al matrix composites (AMCs) reinforced with microparticles (with sizes of 40 µm and contents of 5 and 10 wt pct) and nanoparticles (with sizes of < 100 nm and contents of 1 and 2 wt pct) of SiC, fabricated using stir casting. Specially designed test rig was manufactured for determining the wear performance of these gears and investigated under different applied loads and experiment times. The composite prepared using 2 pct SiC nanoparticle reinforcements was superior to other compositions tested in terms of tribological applications. The effectiveness of nanoparticles compared to that of microparticles was analyzed statistically. Taguchi’s method was used for optimizing the wear parameters. Furthermore, the influence of the experiment time, applied load, and SiC content on the wear was investigated and a regression equation was developed for AMCs reinforced with micro- and nanoparticles. The “smaller is better” characteristic was selected as the objective of this model to analyze the wear resistance. The experiment time and applied load had the most significant effect, followed by the SiC content, in the case of microparticles, whereas for nanoparticles, the applied load was the least significant factor when compared to experiment time and SiC content.
The authors would like to acknowledge the United Arab Emirates University, UAE, for providing the facilities and funding the UPAR research program (Fund Code 31N225), which produced this work.
- 3.A.H. Idrisi and A.H.I. Mourad: in 2019 Advances in Science and Engineering Technology International Conferences (ASET), IEEE, 2019, pp. 1–5.Google Scholar
- 4.A.H. Idrisi and A.-H.I. Mourad: in ASME 2017 Pressure Vessels and Piping Conference, American Society of Mechanical Engineers, 2017, p. V06AT06A033.Google Scholar
- 8.A. Idrisihussain, V. Singhdev, and V. Saxena: Int. J. Sci. Res. Eng. Technol., 2014, vol. 2, pp. 697–704.Google Scholar
- 9.A. Idrisi Hussain and S. Deva: Int. J. Sci. Res. Eng. Technol., 2014, pp. 697–704.Google Scholar
- 23.23 S. Gargatte, R.R. Upadhye, V.S. Dandagi, S.R. Desai, and B.S. Waghamode: J. Miner. Mater. Charact. Eng., 2013, vol. 1, p. 8.Google Scholar
- 25.25 M. Singla, L. Singh, and V. Chawla: J. Miner. Mater. Charact. Eng., 2009, vol. 8, p. 813.Google Scholar
- 28.A.H. Idrisi, A.-H.I. Mourad, D.T. Thekkuden, and J.V. Christy: in IOP Conference Series: Materials Science and Engineering, vol. 324, IOP Publishing, 2018, p. 12087.Google Scholar
- 30.30 R.S. Rana, R. Purohit, and S. Das: Int. J. Sci. Res, 2013, vol. 3, pp. 1–7.Google Scholar
- 35.35 K. Kumar, S. Arul, G. Sriram, V.N. Mani, and V.P. Kumar: Int. J. Curr. Eng. Sci. Res., 2016, vol. 3, pp. 96–103.Google Scholar