Impulse Excitation Internal Friction Study of Retained Austenite in Ferrous Martensite
- 93 Downloads
Internal friction (IF) measurements were conducted using ferrous lath martensite specimens with different retained austenite fractions. While a distinctive Snoek-Kê-Köster (SKK) peak was detected in the IF spectra, the peak shape did not conform to the peak shape observed for fully martensitic steel. Peak analysis suggests that the peak shape is related to the overlap of the SKK peak with a Finkelstein–Rosin peak, additional Debye-type peak related to the retained austenite.
The authors gratefully acknowledge the support of the POSCO Technical Research Laboratories (South Korea).
- 6. D. Sulistiyo, L. Cho, E. Seo and B.C. De Cooman: Mater. Sci. Technol., 2016, vol. 33, pp. 1-14.Google Scholar
- 8.D.H. Sulistiyo: Master’s Thesis, Pohang University of Science and Technology, Pohang, Republic of Korea, 2016.Google Scholar
- 17.M.S. Blanter, I. Golovin, H. Neuhauser, and H. Sinning (2007) A Handbook Series: Springer Series in Materials Science. Springer, Berlin, pp. 28–30.Google Scholar