Effect of the Mass Fraction of Ceramic Particles on the Porosity of Wear-Resistant Composites Fabricated by Combustion Synthesis
- 97 Downloads
Combustion synthesis was employed to fabricate a wear-resistant composite using reactions between Ti, Al, Fe3O4, B4C, and CrO3 powders on the steel plate. CaF2 was used to improve the fluidity and decrease the melting temperature of Al2O3. A large number of holes were found in the top of the composite with different contents of ceramic particles. To elucidate the relationship between the mass fraction of ceramic particles and porosity, the adiabatic temperatures of different combustion systems were calculated. The porosity and size distribution of the holes of samples with different ceramic particle contents were studied, and the distributions and compositions of the ceramic particles were analyzed. The compositions surrounding and inside the holes were studied, and the hardness of the composite was also tested. The results show that the formation of holes is associated with the vaporization of Al and Cr. The porosity increases with an increase in the ceramic particle contents which is the combined effect of the decreasing adiabatic temperature, the increasing nucleation rate, the increasing ceramic particle sizes, the increasing viscosity of the metal, and the wetting angle between the liquid and solid phase, while the composition of ceramic particles has little effect. The hardness values of all composites exceed 60 HRC.
This work was financially supported by the National Natural Science Foundation of China No. 51471002 and Science and Technology Planning Project of Guangdong Province No. 2016B090931005. One of the authors (Sufen Tao) would like to extend her most sincere gratitude to associate professor Yunjin Xia and professor Jie Li. We are also very grateful to Dr. Zengchao Yang and Jing Zhang for their valuable discussions.
- 2.E. Pagounis, V.K. Lindroos, M. Talvitie: Mater. Sci. Eng. A, 1996, vol. 27, pp. 4171-4181.Google Scholar
- 18.R.J. Li: Ceramic-metal composites(In Chinese), 2nd ed., Metallurgical Industry Press, Beijing, 2004, pp. 242-50.Google Scholar
- 21.A. Varma, A.S. Rogachev, A.S. Mukasyan, S. Hwang: Adv. Chem. Eng., 1998, vol. 24, pp. 179-226.Google Scholar
- 23.D. Ye and J. Hu (Eds): Handbook of Thermodynamic Data of Inorganic Substances(In Chinese), 2nd ed., Metallurgy Industry Press, Beijing, 2002, pp. 842–45.Google Scholar
- 24.X. Su, F. Fu, Y. Yan, G. Zheng, T. Liang, Q. Zhang, X. Cheng, D. Yang, H. Chi, X. Tang, Q. Zhang, C. Uhera: Nat. Commun., 2014, vol. 5, pp. 1-7.Google Scholar