Effect of Compositional Variation in TiO2-Based Flux-Cored Arc Welding Fluxes on the Thermo-physical Properties and Mechanical Behavior of a Weld Zone
- 2 Downloads
The effect of compositional variation in TiO2-based flux-cored arc welding fluxes on viscosity, wettability, and electronegativity was studied. The thermo-physical properties of the retrieved fluxes and their relationship with the mechanical properties of the weld zone, including tensile strength and micro-Vickers hardness, after welding were identified. Microstructural observation under similar welding conditions revealed significant grain coarsening at a corrected optical basicity (Λcorr) of 0.62, resulting in reduced strength and hardness due to greater heat transfer. Welding fluxes containing TiO2-based simple structural units should result in greater heat transfer due to the deficiency in complex [AlO4]5−- and [SiO4]4−-based structural units, as identified through spectroscopic analyses using fourier transform infrared spectroscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy. The electronegativity of the retrieved fluxes was also evaluated since higher electronegativity results in greater absorption of electrons in the arc, resulting in arc condensation towards the center direction. Consequently, deeper penetration could be obtained, where the highest electronegativity was identified to be approximately 0.62 of the corrected optical basicity. Thus, both the thermal conductivity and electronegativity of the welding fluxes were identified to determine the heat transfer phenomenon during flux-cored arc welding.
This study was supported by the Brain Korea 21 (BK21) Project of the Division of Humantronics Information Materials Grant No. 2017-11-0016 and the Ministry of Trade, Industry and Energy Grant No. 10044705.
- 3.S. Kou: Welding Metallurgy, Wiley, Hoboken.Google Scholar
- 5.J.E. Spear: Occup. Health Saf., 2011, vol. 80, pp. 64-5.Google Scholar
- 6.J.S. Kim, Y.K. Woo, and B.Y. Lee: Journal KWJS, 2012, vol. 30, pp. 304-8.Google Scholar
- 7.D.T. Cicic, G. Amza, C. Rontescu, S. Raise, and Z. Apostolescu: Global Journal Advances in Pure & Applied Sciences, 2013, vol.1, pp. 506-12.Google Scholar
- 8.K.H. Tseng, and K.L. Chen: J. Nanosci. Nanotech., vol. 12, pp. 6359–67.Google Scholar
- 10.D.D. Schwemmer, D.L. Olson and D.L. Williamson: Weld. J., 1979.vol. 58, p. 153.Google Scholar
- 12.Standard, Standard Test Methods for Tension Testing of Metallic Materials, ASTM International, West Coshohocken, 2013.Google Scholar
- 13.C.S. Smith and L. Guttman: Trans. Aime., 1953, vol. 197, pp. 81-7.Google Scholar
- 46.G.W. Toop and C.S. Samis: Trans. AIME 1962, vol. 224, p. 878-87.Google Scholar
- 48.L. Pauling: The Nature of the Chemical Bond and the Structure of Molecules and Crystals: an Introduction to Modern Structural Chemistry, Cornell University Press, Ithaca, NY, 1960.Google Scholar