A hydrothermal carbonization process for the preparation of activated carbons from hemp straw: an efficient electrode material for supercapacitor application

  • Xia Jiang
  • Gaofeng ShiEmail author
  • Guoying Wang
  • Puranjan Mishra
  • Chao Liu
  • Yucan Dong
  • Peng Zhang
  • Haoqi Tian
  • Yanrong Liu
  • Zhao Wang
  • Qi Zhang
  • Hongquan Zhang
Original Paper
  • 12 Downloads

Abstract

In the present study, a hemp straw activated carbon (HSAC) was simply prepared by hydrothermal process followed by a pre-oxidization and carbonization by KOH solid-state activation. The as-synthesized HSAC shows abundant porosity, which is designed to be beneficial to the fast transportation of electrolyte. The preparation conditions for HSACs under different mass ratios of KOH:precursors were optimized, and the sample obtained by a mass ratio of 4:1 showed an outstanding capacitive property (specific capacitance of 279 F g−1 at 0.5 A g−1 current density). Besides, the capacitance of 91.6% was retained after 5000 charge-discharge cycles under 2 A g−1 current density. The resulting symmetrical supercapacitor obtained by using the HSAC electrodes exhibited an excellent electrochemical performance, which successfully illuminated a LED light. The HSAC has great potentials as electrode material for high-performance supercapacitor, which opens a new way for value increment of natural products.

Keywords

Hydrothermal method Hemp straw Activated carbons Electrode material Supercapacitor 

Notes

Funding information

This work was supported by the National Key Research and Development Program of China (2016YFC0202900), National Natural Science Foundation of China (21567015), Natural Science Foundation of Gansu Province (17JR5RA109), and Gansu Provincial Party Committee Young Creative Talents (Ganzutongzi, 2017/121).

References

  1. 1.
    Aricò AS, Bruce P, Scrosati B, Tarascon JM, Van Schalkwijk W (2005) Nanostructured materials for advanced energy conversion and storage devices. Nat Mater 4(5):366–377Google Scholar
  2. 2.
    Miller JR, Simon P (2008) Electrochemical capacitors for energy management. Science 321(5889):651–652Google Scholar
  3. 3.
    Shao Y, El Kady MF, Wang LJ, Zhang Q, Li Y, Wang H, Mousavi MF, Kaner RB (2015) ChemInform Abstract: Graphene-Based materials for flexible supercapacitors. Chem Soc Rev 44(30):3639–3665Google Scholar
  4. 4.
    Kötz R, Carlen M (2000) Principles and applications of electrochemical capacitors. Electrochim Acta 45(15):2483–2498Google Scholar
  5. 5.
    Simon P, Gogotsi Y (2010) Charge storage mechanism in nanoporous carbons and its consequence for electrical double layer capacitors. Philos Trans Math Phys Eng Sci 368(1923):3457Google Scholar
  6. 6.
    Ojha K, Kumar B, Ganguli AK (2017) Biomass derived graphene-like activated and non-activated porous carbon for advanced supercapacitors. J Chem Sci 129(3):1–8Google Scholar
  7. 7.
    Ekrami E, Dadashian F, Soleimani M (2014) Waste cotton fibers based activated carbon: Optimization of process and product characterization. Fibers Polym 15(9):1855–1864Google Scholar
  8. 8.
    Zhang G, Xiao X, Li B, Gu P, Xue H, Pang H (2017) Transition metal oxides with one-dimensional/one-dimensional-analogue nanostructures for advanced supercapacitors. J Mater Chem A 5(18):8155–8186Google Scholar
  9. 9.
    Huang GY, Xu SM, Yang Y, Cheng YB, Li J (2016) Preparation of Cobalt-Based Bi-Metal-Oxides and the Application in the Field of Electrochemical Energy Storage. Chinese J Inorg Chem 32(10):1693–1703Google Scholar
  10. 10.
    Shayeh JS, Ehsani A, Ganjali MR, Norouzi P, Jaleh B (2015) Conductive polymer/reduced graphene oxide/Au nano particles as efficient composite materials in electrochemical supercapacitors. Appl Surf Sci 353:594–599Google Scholar
  11. 11.
    Duggal AR, Levinson LM (1997) A novel high current density switching effect in electrically conductive polymer composite materials. J Appl Phys 82(11):5532–5539Google Scholar
  12. 12.
    Wang G, Zhang L, Zhang J (2012) A review of electrode materials for electrochemical supercapacitors. Chem Soc Rev 41(18):797–828Google Scholar
  13. 13.
    Wang Q, Yan J, Fan Z (2016) Carbon materials for high volumetric performance supercapacitors: design, progress, challenges and opportunities. Energy Environ Sci 9(3):729–762Google Scholar
  14. 14.
    Qu D (2002) Studies of the activated carbons used in double-layer supercapacitors. J Power Sources 109(2):403–411Google Scholar
  15. 15.
    Ermakova MA, Ermakov DY, Chuvilin AL, Kuvshinov GG (2001) Decomposition of Methane over Iron Catalysts at the Range of Moderate Temperatures: The Influence of Structure of the Catalytic Systems and the Reaction Conditions on the Yield of Carbon and Morphology of Carbon Filaments. J Catal 201(2):183–197Google Scholar
  16. 16.
    Dupuis AC (2005) The catalyst in the CCVD of carbon nanotubes—a review. Prog Mater Sci 50(8):929–961Google Scholar
  17. 17.
    Pai R, Singh A, Simotwo S, Kalra V (2018) In Situ Grown Iron Oxides on Carbon Nanofibers as Freestanding Anodes in Aqueous Supercapacitors. Adv Eng Mater:170–1116Google Scholar
  18. 18.
    Izadi-Najafabadi A, Yasuda S, Kobashi K, Yamada T, Futaba DN, Hatori H, Yumura M, Iijima S, Hata K (2010) Extracting the Full Potential of Single-Walled Carbon Nanotubes as Durable Supercapacitor Electrodes Operable at 4 V with High Power and Energy Density. Adv Mater 22(35):E235–E241Google Scholar
  19. 19.
    Sun H, Xu Z, Gao C (2013) Aerogels: Multifunctional, Ultra-Flyweight, Synergistically Assembled Carbon Aerogels (Adv. Mater. 18/2013). Adv Mater 25(18):2632Google Scholar
  20. 20.
    Yu X, Cheng H, Zhang M, Zhao Y, Qu L, Shi G (2017) Graphene-based smart materials. Nat Rev Mater 2(17046)Google Scholar
  21. 21.
    Hao P, Zhao Z, Leng Y, Tian J, Sang Y, Boughton RI, Wong CP, Liu H, Yang B (2015) Graphene-based nitrogen self-doped hierarchical porous carbon aerogels derived from chitosan for high performance supercapacitors. Nano Energy 15:9–23Google Scholar
  22. 22.
    Xie Q, Zheng A, Zhai S, Wu S, Xie C, Zhang Y, Guan Y (2016) Reed straw derived active carbon/graphene hybrids as sustainable high-performance electrodes for advanced supercapacitors. J Solid State Electrochem 20(2):449–457Google Scholar
  23. 23.
    Arie AA, Kristianto H, Halim M, Lee JK (2017) Synthesis and modification of activated carbon originated from Indonesian local Orange peel for lithium ion Capacitor’s cathode. J Solid State Electrochem 21(5):1–12Google Scholar
  24. 24.
    Zhang J, Gong L, Sun K, Jiang J, Zhang X (2012) Preparation of activated carbon from waste Camellia oleifera shell for supercapacitor application. J Solid State Electrochem 16(6):2179–2186Google Scholar
  25. 25.
    Jiang D, Xiong TY, Fan X, Li MM, Han CL, Gong YT, Wang HY, Yong W (2015) Inspired by bread leavening: one-pot synthesis of hierarchically porous carbon for supercapacitors. Green Chem 17(7):4053–4060Google Scholar
  26. 26.
    Resch G, Held A, Faber T, Panzer C, Toro F, Haas R (2008) Potentials and prospects for renewable energies at global scale. Energ Policy 36(11):4048–4056Google Scholar
  27. 27.
    Wang H, Xu Z, Kohandehghan A, Li Z, Cui K, Tan X, Stephenson TJ, King'Ondu CK, Holt CM, Olsen BC (2013) Interconnected carbon nanosheets derived from hemp for ultrafast supercapacitors with high energy. ACS Nano 7(6):5131–5141Google Scholar
  28. 28.
    Shi G, Liu C, Wang G, Chen X, Li L, Jiang X, Zhang P, Dong Y, Jia S, Tian H (2018) Preparation and electrochemical performance of electrospun biomass-based activated carbon nanofibers. Ionics 1:1–8Google Scholar
  29. 29.
    Li Y, Wei OY, Xu X, Wang M, Hou S, Lu T, Yao Y, Pan L (2018) Micro-/mesoporous carbon nanofibers embedded with ordered carbon for flexible supercapacitors. Electrochim Acta 271:591–598Google Scholar
  30. 30.
    Zhang D, Hao Y, Zheng L, Ma Y, Feng H, Luo H (2013) Nitrogen and sulfur co-doped ordered mesoporous carbon with enhanced electrochemical capacitance performance. J Mater Chem A 1(26):7584–7591Google Scholar
  31. 31.
    Lu SY, Jin M, Zhang Y, Niu YB, Gao JC, Li CM (2017) Chemically Exfoliating Biomass into a Graphene-like Porous Active Carbon with Rational Pore Structure, Good Conductivity, and Large Surface Area for High-Performance Supercapacitors. Adv Energy Mater 1702545Google Scholar
  32. 32.
    Tan Z, Chen G, Zhu Y (2011) Carbon-Based Supercapacitors Produced by the Activation of Graphene. Wiley-Blackwell, pp 211–215Google Scholar
  33. 33.
    Wang R, Wang P, Yan X, Lang J, Peng C, Xue Q (2012) Promising porous carbon derived from celtuce leaves with outstanding supercapacitance and CO2 capture performance. ACS Appl Mater Interfaces 4(11):5800Google Scholar
  34. 34.
    Thommes M, Kaneko K, Neimark AV, Olivier JP, Rodriguezreinoso F, Rouquerol J, Sing KSW (2011) Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Chem Int 38(1):25Google Scholar
  35. 35.
    Leal D, Matsuhiro B, Rossi M, Caruso F (2008) FT-IR spectra of alginic acid block fractions in three species of brown seaweeds. Carbohydr Res 343(2):308Google Scholar
  36. 36.
    Jung N, Kwon S, Lee D, Yoon DM, Park YM, Benayad A, Choi JY, Park JS (2013) Synthesis of chemically bonded graphene/carbon nanotube composites and their application in large volumetric capacitance supercapacitors. Adv Mater 25(47):6854–6858Google Scholar
  37. 37.
    Bertóti I, Mohai M, László K (2015) Surface modification of graphene and graphite by nitrogen plasma: Determination of chemical state alterations and assignments by quantitative X-ray photoelectron spectroscopy. Carbon 84(1):185–196Google Scholar
  38. 38.
    Rantanen J (2007) Process analytical applications of Raman spectroscopy. J Pharm Pharmacol 59(2):171–177Google Scholar
  39. 39.
    Kruk M, Kohlhaas KM, Dufour B, Celer EB, Jaroniec M, Matyjaszewski K, Ruoff RS, Kowalewski T (2007) Partially graphitic, high-surface-area mesoporous carbons from polyacrylonitrile templated by ordered and disordered mesoporous silicas. Microporous Mesoporous Mater 102(1):178–187Google Scholar
  40. 40.
    Li W, Zhang F, Dou Y, Wu Z, Liu H, Qian X, Gu D, Xia Y, Tu B, Zhao D (2011) A Self-Template Strategy for the Synthesis of Mesoporous Carbon Nanofibers as Advanced Supercapacitor Electrodes. Adv Energy Mater 1(3):382–386Google Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2019

Authors and Affiliations

  • Xia Jiang
    • 1
    • 2
  • Gaofeng Shi
    • 1
    Email author
  • Guoying Wang
    • 1
  • Puranjan Mishra
    • 3
  • Chao Liu
    • 1
  • Yucan Dong
    • 1
  • Peng Zhang
    • 1
  • Haoqi Tian
    • 1
  • Yanrong Liu
    • 1
  • Zhao Wang
    • 1
  • Qi Zhang
    • 1
  • Hongquan Zhang
    • 1
  1. 1.School of Petrochemical EngineeringLanzhou University of TechnologyLanzhou cityChina
  2. 2.Gansu Vocational College of AgricultureLanzhou cityChina
  3. 3.Faculty of Engineering TechnologyUniversiti Malaysia PahangKuantanMalaysia

Personalised recommendations