, Volume 25, Issue 3, pp 1331–1340 | Cite as

Investigation of the pseudocapacitive properties of polyaniline nanostructures obtained from scalable chemical oxidative synthesis routes

  • Hossein MahdaviEmail author
  • Taieb Shahalizade
Original Paper
  • 54 Downloads

Abstract

In this study, polyaniline (PANi) nanostructures synthesized through a vast majority of straightforward chemical oxidative methods to compare capacitance and rate capability of the products obtained using inexpensive, scalable, and well-established procedures. Effects of deployed method and conditions are assessed on the chemical and pseudocapacitance properties of PANI in aqueous electrolyte. There was a correlation between morphology and electrochemical performance of the samples and a relatively high specific capacity (901 F g−1 at 10 mV s−1) observed for nanofibrous PANi synthesized by interfacial polymerization at room temperature. Ultrasonic assisted polymerization studies showed that higher temperature and irradiation times convert morphology from nanorod to granule and decrease doping degree. However, by deploying HCl as dopant, electrochemical results were comparable with other methods. For instance, lowest charge transfer resistance value (smallest semicircle) and a relatively high capacitance (704 F g−1 at 10 mV s−1) were determined for PANi sample synthesized via ultrasonic assisted polymerization. On the other hand, p-toluenesulfonic acid was a better dopant for PANi synthesized via rapidly mixed reaction. It was shown that three-like nanostructures with high capacitance are obtainable via a template-free rapidly mixed reaction. Results showed that a specific condition and dopant are optimal for each synthetic route and it is possible to obtain PANi with adequate electrochemical performances and morphology in short reaction times even at room temperature, which is very interesting from the industrial point of view.

Keywords

Polyaniline Pseudocapacitance Electrochemical properties Oxidative polymerization Ultrasonic assisted polymerization 

References

  1. 1.
    Wang H, Lin J, Shen ZX (2016) Polyaniline (PANi) based electrode materials for energy storage and conversion. J Sci Adv Mater Devices 1:225–255.  https://doi.org/10.1016/j.jsamd.2016.08.001 CrossRefGoogle Scholar
  2. 2.
    Tang S-J, Wang A-T, Lin S-Y, Huang KY, Yang CC, Yeh JM, Chiu KC (2011) Polymerization of aniline under various concentrations of APS and HCl. Polym J 43:667–675.  https://doi.org/10.1038/pj.2011.43 CrossRefGoogle Scholar
  3. 3.
    Imani A, Farzi G (2015) Facile route for multi-walled carbon nanotube coating with polyaniline: tubular morphology nanocomposites for supercapacitor applications. J Mater Sci Mater Electron 26:7438–7444.  https://doi.org/10.1007/s10854-015-3377-5 CrossRefGoogle Scholar
  4. 4.
    Cogal S, Cogal GC, Oksuz AU (2017) Plasma-modified multiwalled carbon nanotubes with polyaniline for glucose biosensor applications. Int J Polym Mater Polym Biomater 67(0):1–8.  https://doi.org/10.1080/00914037.2017.1342252 Google Scholar
  5. 5.
    Rajender B, Palaniappan S (2015) Simultaneous oxidation and doping of aniline to polyaniline by oxidative template: electrochemical performance in supercapacitor. Int J Polym Mater Polym Biomater 64:939–945.  https://doi.org/10.1080/00914037.2015.1038814 CrossRefGoogle Scholar
  6. 6.
    Fedorovskaya EO, Okotrub AV, Bulusheva LG (2012) Supercapacitor performance of aligned carbon nanotube/polyaniline composite depending on the duration of aniline polycondensation. Fullerenes Nanotub Carbon Nanostructures 20:519–522.  https://doi.org/10.1080/1536383X.2012.655961
  7. 7.
    Meng Q, Cai K, Chen Y, Chen L (2017) Research progress on conducting polymer based supercapacitor electrode materials. Nano Energy 36:268–285.  https://doi.org/10.1016/j.nanoen.2017.04.040 CrossRefGoogle Scholar
  8. 8.
    Ravi B, Rajender B, Palaniappan S (2016) Improving the electrochemical performance by sulfonation of polyaniline-graphene-silica composite for high performance supercapacitor. Int J Polym Mater Polym Biomater 65:835–840.  https://doi.org/10.1080/00914037.2016.1171221 CrossRefGoogle Scholar
  9. 9.
    Mike JF, Lutkenhaus JL (2013) Recent advances in conjugated polymer energy storage. J Polym Sci Part B Polym Phys 51:468–480.  https://doi.org/10.1002/polb.23256 CrossRefGoogle Scholar
  10. 10.
    Stejskal J, Gilbert RG (2002) Polyaniline. Preparation of a conducting polymer(IUPAC Technical Report). Pure Appl Chem.  https://doi.org/10.1351/pac200274050857
  11. 11.
    Huang W-S, Humphrey BD, MacDiarmid AG (1986) Polyaniline, a novel conducting polymer. Morphology and chemistry of its oxidation and reduction in aqueous electrolytes. J Chem Soc Faraday Trans 1 Phys Chem Condens Phases 82:2385.  https://doi.org/10.1039/f19868202385 Google Scholar
  12. 12.
    Simotwo SK, Kalra V (2016) Polyaniline-based electrodes: recent application in supercapacitors and next generation rechargeable batteries. Curr Opin Chem Eng 13:150–160.  https://doi.org/10.1016/j.coche.2016.09.001 CrossRefGoogle Scholar
  13. 13.
    Ismail YA, Chang J, Shin SR, Mane RS, Han SH, Kim SJ (2009) Hydrogel-assisted polyaniline microfiber as controllable electrochemical Actuatable supercapacitor. J Electrochem Soc 156:A313.  https://doi.org/10.1149/1.3077597 CrossRefGoogle Scholar
  14. 14.
    Eftekhari A, Li L, Yang Y (2017) Polyaniline supercapacitors. J Power Sources 347:86–107.  https://doi.org/10.1016/j.jpowsour.2017.02.054 CrossRefGoogle Scholar
  15. 15.
    Kuang H, Cao Q, Wang X, Jing B, Wang Q, Zhou L (2013) Influence of the reaction temperature on polyaniline morphology and evaluation of their performance as supercapacitor electrode. J Appl Polym Sci 130:3753–3758.  https://doi.org/10.1002/app.39650 CrossRefGoogle Scholar
  16. 16.
    Pouget JP, Jozefowicz ME, Epstein AJ, Tang X, MacDiarmid AG (1991) X-ray structure of polyaniline. Macromolecules 24:779–789.  https://doi.org/10.1021/ma00003a022 CrossRefGoogle Scholar
  17. 17.
    Tran HD, Li D, Kaner RB (2009) One-dimensional conducting polymer nanostructures: bulk synthesis and applications. Adv Mater 21:1487–1499.  https://doi.org/10.1002/adma.200802289 CrossRefGoogle Scholar
  18. 18.
    Huang J, Kaner RB (2004) Nanofiber formation in the chemical polymerization of aniline: a mechanistic study. Angew Chem 116:5941–5945CrossRefGoogle Scholar
  19. 19.
    Huang J, Kaner RB (2004) A general chemical route to polyaniline nanofibers. J Am Chem Soc 126:851–855.  https://doi.org/10.1021/ja0371754 CrossRefGoogle Scholar
  20. 20.
    Xia H, Wang Q (2002) Ultrasonic irradiation: a novel approach to prepare conductive polyaniline/nanocrystalline titanium oxide composites. Chem Mater 14:2158–2165.  https://doi.org/10.1021/cm0109591 CrossRefGoogle Scholar
  21. 21.
    Dan LI, Huang J, Kaner RB (2009) Polyaniline nanofibers: a unique polymer nanostructure for versatile applications. Acc Chem Res 42:135–145.  https://doi.org/10.1021/ar800080n CrossRefGoogle Scholar
  22. 22.
    Deng J, Wang T, Guo J, Liu P (2017) Electrochemical capacity fading of polyaniline electrode in supercapacitor: an XPS analysis. Prog Nat Sci Mater Int 27:257–260.  https://doi.org/10.1016/j.pnsc.2017.02.007 CrossRefGoogle Scholar
  23. 23.
    Moghadam PN, Khalafy J, Taheri T (2010) Sonochemical synthetic methods to produce functionalized conducting copolymers. Polym Adv Technol 21:235–243.  https://doi.org/10.1002/pat.1419 CrossRefGoogle Scholar
  24. 24.
    Liu H, Hu XB, Wang JY, Boughton RI (2002) Structure, conductivity, and thermopower of crystalline polyaniline synthesized by the ultrasonic irradiation polymerization method. Macromolecules 35:9414–9419.  https://doi.org/10.1021/ma0119326 CrossRefGoogle Scholar
  25. 25.
    Stejskal J, Kratochvíl P, Radhakrishnan N (1993) Polyaniline dispersions 2. UV-vis absorption spectra. Synth Met 61:225–231.  https://doi.org/10.1016/0379-6779(93)91266-5 CrossRefGoogle Scholar
  26. 26.
    Gruger A, Novak A, Régis A, Colomban P (1994) Infrared and Raman study of polyaniline part II: influence of ortho substituents on hydrogen bonding and UV/Vis-near-IR electron charge transfer. J Mol Struct 328:153–167.  https://doi.org/10.1016/0022-2860(94)08368-1 CrossRefGoogle Scholar
  27. 27.
    Du X-S, Zhou C-F, Wang G-T, Mai Y-W (2008) Novel solid-state and template-free synthesis of branched polyaniline nanofibers. Chem Mater 20:3806–3808CrossRefGoogle Scholar
  28. 28.
    Wang Q, Lei Z, Chen Y, Ouyang Q, Gao P, Qi L, Zhu C, Zhang J (2013) Branched polyaniline/molybdenum oxide organic/inorganic heteronanostructures: synthesis and electromagnetic absorption properties. J Mater Chem A 1:11795–11801CrossRefGoogle Scholar
  29. 29.
    Mahdavi H, Kahriz PK, Gholipour-Ranjbar H, Shahalizade T (2017) Synthesis and performance study of amino functionalized graphene aerogel grafted with polyaniline nanofibers as an efficient supercapacitor material. J Mater Sci Mater Electron 28:4295–4305.  https://doi.org/10.1007/s10854-016-6053-5 CrossRefGoogle Scholar
  30. 30.
    Genies EM, Lapkowski M, Penneau JF (1988) Cyclic voltammetry of polyanilinez interpretation of the add peak. J Electroanal Chem 249:97–107.  https://doi.org/10.1016/0022-0728(88)80351-6 CrossRefGoogle Scholar
  31. 31.
    Wang Y, Song Y, Xia Y (2016) Electrochemical capacitors: mechanism, materials, systems, characterization and applications. Chem Soc Rev 45:5925–5950.  https://doi.org/10.1039/C5CS00580A CrossRefGoogle Scholar
  32. 32.
    Dou Y, Wang Y, Tian D et al (2017) Atomically thin Co3O4 nanosheet-coated stainless steel mesh with enhanced capacitive Na+ storage for high-performance sodium-ion batteries. 2D Mater 4:15022.  https://doi.org/10.1088/2053-1583/4/1/015022 CrossRefGoogle Scholar
  33. 33.
    Gholipour-Ranjbar H, Ganjali MR, Norouzi P, Naderi HR (2016) Synthesis of cross-linked graphene aerogel/Fe2O3 nanocomposite with enhanced supercapacitive performance. Ceram Int 42:12097–12104.  https://doi.org/10.1016/j.ceramint.2016.04.140 CrossRefGoogle Scholar
  34. 34.
    Dhawale DS, Vinu a, Lokhande CD (2011) Stable nanostructured polyaniline electrode for supercapacitor application. Electrochim Acta 56:9482–9487.  https://doi.org/10.1016/j.electacta.2011.08.042 CrossRefGoogle Scholar
  35. 35.
    Wang K, Wu H, Meng Y, Wei Z (2014) Conducting polymer nanowire arrays for high performance supercapacitors. Small 10:14–31.  https://doi.org/10.1002/smll.201301991 CrossRefGoogle Scholar
  36. 36.
    Sivaraman P, Kushwaha RK, Shashidhara K, Hande VR, Thakur AP, Samui AB, Khandpekar MM (2010) All solid supercapacitor based on polyaniline and crosslinked sulfonated poly[ether ketone]. Electrochim Acta 55:2451–2456.  https://doi.org/10.1016/j.electacta.2009.12.009 CrossRefGoogle Scholar
  37. 37.
    Bian LJ, Luan F, Liu SS, Liu XX (2012) Self-doped polyaniline on functionalized carbon cloth as electroactive materials for supercapacitor. Electrochim Acta 64:17–22.  https://doi.org/10.1016/j.electacta.2011.12.012 CrossRefGoogle Scholar
  38. 38.
    Kim BC, Kwon JS, Ko JM, Park JH, Too CO, Wallace GG (2010) Preparation and enhanced stability of flexible supercapacitor prepared from Nafion/polyaniline nanofiber. Synth Met 160:94–98.  https://doi.org/10.1016/j.synthmet.2009.10.011 CrossRefGoogle Scholar
  39. 39.
    Prasad KR, Munichandraiah N (2002) Electrochemical studies of polyaniline in a gel polymer electrolyte. Electrochem Solid-State Lett 5:A271–A274.  https://doi.org/10.1149/1.1516910 CrossRefGoogle Scholar
  40. 40.
    Gupta V, Miura N (2005) Electrochemically deposited polyaniline Nanowire’s network. Electrochem Solid-State Lett 8:A630.  https://doi.org/10.1149/1.2087207 CrossRefGoogle Scholar
  41. 41.
    Dhawale DS, Salunkhe RR, Jamadade VS, Dubal DP, Pawar SM, Lokhande CD (2010) Hydrophilic polyaniline nanofibrous architecture using electrosynthesis method for supercapacitor application. Curr Appl Phys 10:904–909.  https://doi.org/10.1016/j.cap.2009.10.020 CrossRefGoogle Scholar
  42. 42.
    Jia R, Wu Y, Zan G, Liu D (2017) Synthesis and characterization of nanotree-like polyaniline electrode material for supercapacitors. J Mater Sci Mater Electron 28:2366–2376CrossRefGoogle Scholar
  43. 43.
    Yoon SB, Yoon EH, Kim KB (2011) Electrochemical properties of leucoemeraldine, emeraldine, and pernigraniline forms of polyaniline/multi-wall carbon nanotube nanocomposites for supercapacitor applications. J Power Sources 196:10791–10797.  https://doi.org/10.1016/j.jpowsour.2011.08.107 CrossRefGoogle Scholar
  44. 44.
    Mahdavi H, Kahriz PK, Gholipour Ranjbar H, Shahalizade T (2016) Enhancing supercapacitive performance of polyaniline by interfacial copolymerization with melamine. J Mater Sci Mater Electron 27:7407–7414.  https://doi.org/10.1007/s10854-016-4715-y CrossRefGoogle Scholar
  45. 45.
    Bian C, Yu A (2010) De-doped polyaniline nanofibres with micropores for high-rate aqueous electrochemical capacitor. Synth Met 160:1579–1583.  https://doi.org/10.1016/j.synthmet.2010.04.019 CrossRefGoogle Scholar
  46. 46.
    Kampouris DK, Ji X, Randviir EP, Banks CE (2015) A new approach for the improved interpretation of capacitance measurements for materials utilised in energy storage. RSC Adv 5:12782–12791.  https://doi.org/10.1039/C4RA17132B CrossRefGoogle Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  1. 1.School of Chemistry, College of ScienceUniversity of TehranTehranIran

Personalised recommendations