Mechanism and characteristics of thermal action of HMX explosive mixture containing high-efficiency fuel

  • JiPing LiuEmail author
  • WeiWei Yang
  • Ying Liu
  • XiaoBo Liu
Article
  • 14 Downloads

Abstract

In this study, the thermal stability and detonation properties of three types of explosives were investigated. Results indicated that nanoaluminum powder improved the detonation properties of HMX by increasing the specific surface area of HMX, which substantially increased the explosion heat and power. The decomposition temperatures of the three explosives containing aluminum hydride, ammonia borane, and nanoaluminum powder during slow cook-off at heating rates of 1.5 and 10°C min–1 were measured as 246°C and 241°C, 256°C and 261°C, and 238°C and 264°C, respectively. The explosives containing hydrogen storage materials swelled; however, the nanoaluminum powder was only slightly peeled off at the edge of the grains during cookoff. Differential scanning calorimetry (DSC) curves of the explosives containing hydrogen storage materials exhibited endothermic and exothermic peaks before the major exothermic reaction peak during the cook-off tests. In contrast, only one weak peak was observed in the DSC curve of the explosive containing nanoaluminum powder before the major exothermic reaction. In addition, the additives and adhesives catalyzed the slow cook-off decomposition, which caused the transformation of HMX crystals and accelerated the thermal decomposition reaction of HMX. The addition of high-density hydrogen storage materials to HMX resulted in detonation heats and explosion powers much greater than cure HMX. This improved performance was attributed to the hydrogen storage materials in the explosives participating in a secondary reaction in the reaction zone at the instant of the explosion, effectively realizing complementary lossless energy and thus greatly improving the explosive power of the explosives.

Keywords

high-density hydrogen storage material nanoparticles thermal stability cook-off explosive performance detonation reaction 

References

  1. 1.
    Zhang C, Sun C, Hu B, et al. Synthesis and characterization of the pentazolate anion cyclo-N5 - in (N5)6(H3O)3(NH4)4Cl. Science, 2017, 355: 374–376CrossRefGoogle Scholar
  2. 2.
    Wang Z Y. New progress in the study of high-energy density compounds abroad. Aircraft Missile, 2003, 2: 34–37Google Scholar
  3. 3.
    Lei Y P, Xu S L, Yang S Q, et al. Overview of overseas research institutions and main research results of high-energy materials. Pyrotechnics, 2006, 5: 45–50Google Scholar
  4. 4.
    Gao H, Shreeve J M. Azole-based energetic salts. Chem Rev, 2011, 111: 7377–7436CrossRefGoogle Scholar
  5. 5.
    Schwarz R B, Brown G W, Thompson D G, et al. The Effect of shear strain on texture in pressed plastic bonded explosives. Propell Explos Pyrotech, 2013, 38: 685–694CrossRefGoogle Scholar
  6. 6.
    Klapötke T M, Witkowski T G, Wilk Z, et al. Determination of theinitiating capability of detonators containing TKX-50, MAD-X1, PETNC, DAAF, RDX, HMX or PETN as a base charge, by underwater explosion test. Propell Explos Pyrotech, 2016, 41: 92–97CrossRefGoogle Scholar
  7. 7.
    Meng L I, Zhao F Q, Yang L, et al. Energetic characteristics computation of propellants containing dihydroxylammonium 5,5'-bistetrazole- 1,1'-diolate (TKX-50). Chin J Energ Mater, 2014, 3: 286–290Google Scholar
  8. 8.
    Byrd E F C, Scuseria G E, Chabalowski C F. An ab initio study of solid nitromethane, HMX, RDX, and CL20: Successes and failures of DFT. J Phys Chem B, 2004, 108: 13100–13106CrossRefGoogle Scholar
  9. 9.
    Nouri A, Zahedi E, Ehsani M, et al. Understanding the kinetics and molecular mechanism of the Curtius rearrangement of 3-oxocyclobutane- 1-carbonyl azide. Comput Theor Chem, 2018, 1130: 121–129CrossRefGoogle Scholar
  10. 10.
    Bi X L, Liu J P, Ma C. Research on the performance of boron particles with HTPB. J Beijing Inst Technol, 2014, 23: 206–209Google Scholar
  11. 11.
    Tang C, Yan H, Li M, et al. A novel phosphorus-containing polysiloxane for fabricating high performance electronic material with excellent dielectric and thermal properties. J Mater Sci-Mater Electron, 2018, 29: 195–204CrossRefGoogle Scholar
  12. 12.
    Zhang W, Liu Y F, Xie W X, et al. Study on compatibility of AlH3 with compositions of solid propellant by thermal analysis method. Chin J Explos Propell, 2015, 1: 41–46Google Scholar
  13. 13.
    Allaria E, Diviacco B, Callegari C, et al. Control of the polarization of a vacuum-ultraviolet, high-gain, free-electron laser. Phys Rev X, 2014, 4: 041040Google Scholar
  14. 14.
    Dong H S. Development and countermeasures of high energy density materials. Energy Contain Mater, 2004, 12: 1–12Google Scholar
  15. 15.
    özhava D, özkar S. Nanoalumina-supported rhodium(0) nanoparticles as catalyst in hydrogen generation from the methanolysis of ammonia borane. Mol Catal, 2017, 439: 50–59CrossRefGoogle Scholar
  16. 16.
    Agrawal J P. Some new high energy materials and their formulations for specialized applications. Propell Explos Pyrotech, 2005, 30: 316–328CrossRefGoogle Scholar
  17. 17.
    Zhou L, Xie Z, Wei X. Comparison of underwater shock wave attenuation of a new insensitive high explosive with different explosives. Combust Explos Shock Waves, 2011, 47: 721–726CrossRefGoogle Scholar
  18. 18.
    Koutsospyros A, Christodoulatos C, Panikov N, et al. Environmental relevance of CL-20: Preliminary findings. Water Air Soil Pollut-Focus, 2004, 4: 459–470CrossRefGoogle Scholar
  19. 19.
    Guo Y, Yu X, Sun W, et al. The hydrogen-enriched Al-B-N system as an advanced solid hydrogen-storage candidate. Angew Chem Int Ed, 2011, 50: 1087–1091CrossRefGoogle Scholar
  20. 20.
    Ben-Itzhak I, Wells E, Studanski D, et al. Double and single ionization of hydrogen molecules by fast-proton impact. J Phys B-At Mol Opt Phys, 2001, 34: 1143–1161CrossRefGoogle Scholar
  21. 21.
    Victor A C. Simple calculation methods for munitions cookoff times and temperatures. Propellants Explos Pyrotech, 1995, 20: 252–259CrossRefGoogle Scholar
  22. 22.
    Ramskill P K. A description of the “engulf” computer codes-codes to model the thermal response of an LPG tank either fully or partially engulfed by fire. J Hazard Mater, 1988, 20: 177–196CrossRefGoogle Scholar
  23. 23.
    Aydemir E, Ulas A, Serin N. Thermal decomposition and ignition of PBXN-110 plastic-bonded explosive. Propell Explos Pyrotech, 2012, 37: 308–315CrossRefGoogle Scholar
  24. 24.
    Ma X, Chen L, Lu F, et al. Calculation on multi-step thermal decomposition of HMX-and TATB-based composite explosive under cook-off conditions. Explos Shock Waves, 2014, 1: 67–74Google Scholar
  25. 25.
    Bazyn T, Eyer R, Krier H, et al. Combustion characteristics of aluminum hydride at elevated pressure and temperature. J Propul Power, 2004, 20: 427–431CrossRefGoogle Scholar
  26. 26.
    DeLuca L T, Galfetti L, Severini F, et al. Physical and ballistic characterization of AlH3-based space propellants. Aerosp Sci Tech, 2007, 11: 18–25CrossRefGoogle Scholar
  27. 27.
    Il’in A P, Bychin N V, Gromov A A. Products of combustion of aluminum hydride in air. Combust Explos Shock Waves, 2001, 37: 490–491CrossRefGoogle Scholar
  28. 28.
    Xu B, Liu J, Zhao L, et al. Theoretical study on the structure and stability of aluminum hydride (AlnH3n) clusters. J Mater Sci, 2013, 48: 2647–2658CrossRefGoogle Scholar
  29. 29.
    Chen D S, Wong D S H, Chen C Y. Neural network correlations of detonation properties of high energy explosives. Propell Explos Pyrotech, 1998, 23: 296–300CrossRefGoogle Scholar
  30. 30.
    Wang C, Dong X Z, Shu C W. Parallel adaptive mesh refinement method based on WENO finite difference scheme for the simulation of multi-dimensional detonation. J Comput Phys, 2015, 298: 161–175MathSciNetCrossRefzbMATHGoogle Scholar
  31. 31.
    Wang C, Zhang X, Shu C W, et al. Robust high order discontinuous Galerkin schemes for two-dimensional gaseous detonations. J Comput Phys, 2012, 231: 653–665MathSciNetCrossRefzbMATHGoogle Scholar

Copyright information

© Science China Press and Springer-Verlag GmbH Germany, part of Springer Nature 2019

Authors and Affiliations

  • JiPing Liu
    • 1
    • 2
    Email author
  • WeiWei Yang
    • 1
  • Ying Liu
    • 1
  • XiaoBo Liu
    • 1
  1. 1.School of Materials Science & EngineeringBeijing Institute of TechnologyBeijingChina
  2. 2.State Key Laboratory of Explosion Science and TechnologyBeijing Institute of TechnologyBeijingChina

Personalised recommendations