Characterization of graded polyurethane elastomer by FTIR

  • Zhao PeiZhong 
  • Wang YuanSheng 
  • Zhu JinHua 
  • Hua XingYan 
  • Wen QingZhen 
Article
Received:
Accepted:

Abstract

Polyurethane elastomers with graded structure were prepared in the graded temperature field. The samples were characterized by FTIR technology. The results show that the degree of microphase separation in the samples decreases with the decrease of the curing temperature. As far as the molar ratio of NH2 and NCO is concerned, the sample exhibits better graded morphology when the ratio is 0.95. The transparence of the samples prepared also changes gradually, increasing along the direction, in which temperature decreases.

Keywords

FGM polyurethane graded transparence microphase separation FTIR 
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Koizumi M. FGM activities in Japan. Composites Part B, 1997, 28B: 1–4CrossRefGoogle Scholar
  2. 2.
    Kieback B, Neubrand A, Riedel H. Processing techniques for functionally graded materials. Mater Sci Eng A, 2003, 362: 81–105CrossRefGoogle Scholar
  3. 3.
    Huang X T, Yan M. Review and prospects of functional gradient materials. Mater Sci Eng (in Chinese), 1997, 15(4): 35–38Google Scholar
  4. 4.
    Zhang C C, Huang F, Wei L L, Wu L L. Research on functionally gradient polymer. J Wuhan U Tech (in Chinese), 2002, 24(10): 13–16Google Scholar
  5. 5.
    Zou J P, Ruan J M, Zhou Z C, Shen X J, Zhou Z H. Design, preparation and property evaluation of funally graded materials. Mater Sci Eng of Powder Metall (in Chinese), 2005, 10(2): 78–87Google Scholar
  6. 6.
    Furukawa M, Hamada Y, Koijio K. Aggregation structure and mechanical properties of functionally graded polyurethane elastomers. J Polym Sci: Part B: Polym Phys, 2003, 41: 2355–2363CrossRefGoogle Scholar
  7. 7.
    Zhao P Z, Hua X Y, Zhu J H, Wang Y S. Study on damping property of polyurethane by means of viscoelastic damping structure. China Elastomerics (in Chinese), 2005, 15(2): 37–39Google Scholar
  8. 8.
    Li W, Ryan A J. Morphology development via reaction-induced phase separation in flexible polyurethane foam. Macromol, 2002, 35(13): 5034–5042CrossRefGoogle Scholar
  9. 9.
    Chen Z S, Yang W P, Macosko C W. The study of polyurethane and polyureas by transmission spectra of Fourie transform infrared spectroscopy. Polym Mater Sci Eng (in Chinese), 1993, (3): 58–62Google Scholar
  10. 10.
    Tan H, Guo M, Du R, Xie X, Li J, Zhong Y, Fu Q. The effect of fluorinated side chain attached on hard segment on the phase separation and surface topography of polyurethanes. Polym, 2004, 45: 1647–1657CrossRefGoogle Scholar
  11. 11.
    Li Z F, Xu C M, Yin S M, Wen L R. Development of morphology and mechanical properties in polyurethane urea (PUU) curing process. Spectro Spect Anal (in Chinese), 2002, 22(5): 774–778Google Scholar
  12. 12.
    Coleman M M, Lee K H, Skrovanek D J, Painter P C. Hydrogen Bonding in Polymers. 4. Infrared temperature studies of a simple polyurethane. Macromol, 1986, 19(8): 2149–2157CrossRefGoogle Scholar
  13. 13.
    Yang J, Wang G Y, Hu C P. Morphology and mechanical properties of alphatic polyurea with different hard segment contents. Acta Polym Sin (in Chinese), 2003, (6): 794–798Google Scholar

Copyright information

© Science in China Press 2008

Authors and Affiliations

  • Zhao PeiZhong 
    • 1
  • Wang YuanSheng 
    • 2
  • Zhu JinHua 
    • 1
  • Hua XingYan 
    • 1
  • Wen QingZhen 
    • 1
  1. 1.Department of Chemistry and Materials, College of ScienceNaval University of EngineeringWuhanChina
  2. 2.Administrative Office of TrainingNaval University of EngineeringWuhanChina

Personalised recommendations