Removal of benzene by non-thermal plasma catalysis over manganese oxides through a facile synthesis method

  • Hao Guo
  • Xin Liu
  • Hajime Hojo
  • Xin Yao
  • Hisahiro EinagaEmail author
  • Wenfeng ShangguanEmail author
Research Article
  • 22 Downloads

Abstract

Three manganese oxide catalysts (MnOx) were synthesized via a simple method, and then they were introduced into the non-thermal plasma (NTP) system for benzene removal. The XRD and EXAFS results showed the MnOx were mainly in the Mn3O4 phase, and from the analysis of N2 adsorption/desorption isotherms, we knew the MnOx calcined at 250 °C (Mn250) had the largest surface area of 274.5 m2 g−1. Besides, Mn250 also exerted higher benzene adsorption capacity (0.430 mmol g−1) according to C6H6-TPD. O2-TPD indicated that Mn250 showed better oxygen mobility than Mn300. Moreover, by analyzing XPS results, it revealed that Mn250 exhibited rich abundant of surface adsorbed oxygen species (Oads) and moderate ratio of Mn4+/Mn3+, and the reducibility temperature was also the lowest among all the MnOx catalysts drawn by H2-TPR profiles. As a result, Mn250 combined with NTP could remove 96.9% of benzene at a low input power of 3 W (benzene concentration 200 ppm, and GHSV 60,000 mL gcat.−1 h−1), performing the best catalytic activity among the three catalysts and plasma only. Furthermore, the “NTP + Mn250” system also produced the highest CO2 concentration and lowest CO concentration in downstream, and the residual O3 after catalytic reaction was also the lowest, that is to say, the synergistic effect between NTP and Mn250 was more effective than other catalysts in benzene removal.

Graphical abstract

Keywords

Benzene Non-thermal plasma Manganese oxides Facile synthesis method 

Notes

Acknowledgments

The authors would like to thank Hamada Shoma-san in Einaga-Hojo-lab for adjusting the non-thermal plasma system in this experiment. This work was financially supported by the National Key Research & Development Plan (2017YFC0211804).

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. Bauer U, Gleichweit C, Höfert O, Späth F, Gotterbarm K, Steinrück H-P, Papp C (2018) Reactivity studies of ethylene, benzene and cyclohexane on carbide-modified Mo (110) using high resolution X-ray photoelectron spectroscopy. Surf Sci 678:11–19CrossRefGoogle Scholar
  2. Cai W, Zhong Q, Zhao W, Bu Y (2014) Focus on the modified CexZr1-xO2 with the rigid benzene-muti-carboxylate ligands and its catalysis in oxidation of NO. Appl Catal B Environ 158-159:258–268CrossRefGoogle Scholar
  3. Chen J, Chen X, Chen X, Xu W, Xu Z, Jia H, Chen J (2018) Homogeneous introduction of CeOy into MnOx-based catalyst for oxidation of aromatic VOCs. Appl Catal B Environ 224:825–835CrossRefGoogle Scholar
  4. Einaga H, Ogata A (2009) Benzene oxidation with ozone over supported manganese oxide catalysts: effect of catalyst support and reaction conditions. J Hazard Mater 164:1236–1241CrossRefGoogle Scholar
  5. Einaga H, Teraoka Y, Ogata A (2013) Catalytic oxidation of benzene by ozone over manganese oxides supported on USY zeolite. J Catal 305:227–237CrossRefGoogle Scholar
  6. Fang R, Huang H, Ji J, He M, Feng Q, Zhan Y, Leung DYC (2018) Efficient MnOx supported on coconut shell activated carbon for catalytic oxidation of indoor formaldehyde at room temperature. Chem Eng J 334:2050–2057CrossRefGoogle Scholar
  7. Gao X, Dollimore D (1993) The thermal decomposition of oxalates: part 26. A kinetic study of the thermal decomposition of manganese (II) oxalate dihydrate. Thermochim Acta 215:47–63CrossRefGoogle Scholar
  8. Guo Y-F, Ye D-Q, Chen K-F, He J-C, Chen W-L (2006) Toluene decomposition using a wire-plate dielectric barrier discharge reactor with manganese oxide catalyst in situ. J Mol Catal A Chem 245:93–100CrossRefGoogle Scholar
  9. Hamada S, Hojo H, Einaga H (2018) Effect of catalyst composition and reactor configuration on benzene oxidation with a nonthermal plasma-catalyst combined reactor. Catal Today.  https://doi.org/10.1016/j.cattod.2018.07.055
  10. He C, Liu X, Shi J, Ma C, Pan H, Li G (2015) Anionic starch-induced Cu-based composite with flake-like mesostructure for gas-phase propanal efficient removal. J Colloid Interface Sci 454:216–225CrossRefGoogle Scholar
  11. Ikhlaq A, Kasprzyk-Hordern B (2017) Catalytic ozonation of chlorinated VOCs on ZSM-5 zeolites and alumina: formation of chlorides. Appl Catal B Environ 200:274–282CrossRefGoogle Scholar
  12. Ji J, Xu Y, Huang H, He M, Liu S, Liu G, Xie R, Feng Q, Shu Y, Zhan Y, Fang R, Ye X, Leung DYC (2017) Mesoporous TiO2 under VUV irradiation: enhanced photocatalytic oxidation for VOCs degradation at room temperature. Chem Eng J 327:490–499CrossRefGoogle Scholar
  13. Karuppiah J, Reddy EL, Reddy PMK, Ramaraju B, Subrahmanyam C (2014) Catalytic nonthermal plasma reactor for the abatement of low concentrations of benzene. Int J Environ Sci Technol 11:311–318CrossRefGoogle Scholar
  14. Kim M, Park E, Jurng J (2018) Oxidation of gaseous formaldehyde with ozone over MnOx/TiO2 catalysts at room temperature (25 °C). Powder Technol 325:368–372CrossRefGoogle Scholar
  15. Li H, Lee S, Wang Z, Huang Y, Ho W, Cui L (2017) Peroxymonosulfate activated by amorphous particulate MnO2 for mineralization of benzene gas: redox reaction, weighting analysis, and numerical modelling. Chem Eng J 316:61–69CrossRefGoogle Scholar
  16. Li Y, Fan Z, Shi J, Liu Z, Zhou J, Shangguan W (2014) Removal of volatile organic compounds (VOCs) at room temperature using dielectric barrier discharge and plasma-catalysis. Plasma Chem Plasma Process 34:801–810CrossRefGoogle Scholar
  17. Lian S, Browne MP, Domínguez C, Stamatin SN, Nolan H, Duesberg GS, Lyons MEG, Fonda E, Colavita PE (2017) Template-free synthesis of mesoporous manganese oxides with catalytic activity in the oxygen evolution reaction. Sustain Energy Fuels 1:780–788CrossRefGoogle Scholar
  18. Liao Y, Zhang X, Peng R, Zhao M, Ye D (2017) Catalytic properties of manganese oxide polyhedra with hollow and solid morphologies in toluene removal. Appl Surf Sci 405:20–28CrossRefGoogle Scholar
  19. Liu G, Ji J, Huang H, Xie R, Feng Q, Shu Y, Zhan Y, Fang R, He M, Liu S, Ye X, Leung DYC (2017) UV/H2O2: an efficient aqueous advanced oxidation process for VOCs removal. Chem Eng J 324:44–50CrossRefGoogle Scholar
  20. Liu W, Carrasco J, Santra B, Michaelides A, Scheffler M, Tkatchenko A (2012) Benzene adsorbed on metals: concerted effect of covalency and van der Waals bonding. Phys Rev B 86(24):245405CrossRefGoogle Scholar
  21. Liu Y, Zhang P (2017) Removing surface hydroxyl groups of Ce-modified MnO2 to significantly improve its stability for gaseous ozone decomposition. J Phys Chem C 121:23488–23497CrossRefGoogle Scholar
  22. Ma X, Li J, Rankin MA, Croll LM, Dahn JR (2017) Highly porous MnOx prepared from MnC2O4·3H2O as an adsorbent for the removal of SO2 and NH3. Microporous Mesoporous Mater 244:192–198CrossRefGoogle Scholar
  23. Mizuno A (2013) Generation of non-thermal plasma combined with catalysts and their application in environmental technology. Catal Today 211:2–8CrossRefGoogle Scholar
  24. Mustafa MF, Fu X, Liu Y, Abbas Y, Wang H, Lu W (2018) Volatile organic compounds (VOCs) removal in non-thermal plasma double dielectric barrier discharge reactor. J Hazard Mater 347:317–324CrossRefGoogle Scholar
  25. Piumetti M, Fino D, Russo N (2015) Mesoporous manganese oxides prepared by solution combustion synthesis as catalysts for the total oxidation of VOCs. Appl Catal B Environ 163:277–287CrossRefGoogle Scholar
  26. Qin C, Huang X, Dang X, Huang J, Teng J, Kang Z (2016) Toluene removal by sequential adsorption-plasma catalytic process: effects of Ag and Mn impregnation sequence on Ag-Mn/γ-Al2O3. Chemosphere 162:125–130CrossRefGoogle Scholar
  27. Quoc An HT, Pham Huu T, Le Van T, Cormier JM, Khacef A (2011) Application of atmospheric non thermal plasma-catalysis hybrid system for air pollution control: toluene removal. Catal Today 176:474–477CrossRefGoogle Scholar
  28. Sivachandiran L, Thevenet F, Rousseau A (2015) Isopropanol removal using MnxOy packed bed non-thermal plasma reactor: comparison between continuous treatment and sequential sorption/regeneration. Chem Eng J 270:327–335CrossRefGoogle Scholar
  29. Strohmeier BR, Hercules DM (1985) Surface spectroscopic characterization of manganese/aluminum oxide catalysts. Chemischer Informationsdienst 16:4922–4929Google Scholar
  30. Sudhakaran MSP, Trinh HQ, Karuppiah J, Hossian MM, Mok YS (2017) Plasma catalytic removal of p-xylene from air stream using γ-Al2O3 supported manganese catalyst. Top Catal 60:1–11CrossRefGoogle Scholar
  31. Tang W, Wu X, Li D, Wang Z, Liu G, Liu H, Chen Y (2014) Oxalate route for promoting activity of manganese oxide catalysts in total VOCs’ oxidation: effect of calcination temperature and preparation method. J Mater Chem A 2:2544–2554CrossRefGoogle Scholar
  32. Tao J, Tang H, Patra A, Bhattarai P, Perdew JP (2018) Modeling the physisorption of graphene on metals. Phys Rev B 97(16):165403CrossRefGoogle Scholar
  33. Tomatis M, Xu H-H, He J, Zhang X-D (2016) Recent development of catalysts for removal of volatile organic compounds in flue gas by combustion: a review. J Chem 2016:1–15CrossRefGoogle Scholar
  34. Trinh QH, Mok YS (2015) Effect of the adsorbent/catalyst preparation method and plasma reactor configuration on the removal of dilute ethylene from air stream. Catal Today 256:170–177CrossRefGoogle Scholar
  35. Vandenbroucke AM, Mora M, Jiménez-Sanchidrián C, Romero-Salguero FJ, De Geyter N, Leys C, Morent R (2014) TCE abatement with a plasma-catalytic combined system using MnO2 as catalyst. Appl Catal B Environ 156-157:94–100CrossRefGoogle Scholar
  36. Veerapandian S, Leys C, De Geyter N, Morent R (2017) Abatement of VOCs using packed bed non-thermal plasma reactors: a review. Catalysts 7(4):113CrossRefGoogle Scholar
  37. Wang B, Chi C, Xu M, Wang C, Meng D (2017) Plasma-catalytic removal of toluene over CeO2-MnOx catalysts in an atmosphere dielectric barrier discharge. Chem Eng J 322:679–692CrossRefGoogle Scholar
  38. Wang H, Huang Z, Jiang Z, Jiang Z, Zhang Y, Zhang Z, Shangguan W (2018) Trifunctional C@MnO catalyst for enhanced stable simultaneously catalytic removal of formaldehyde and ozone. ACS Catal 8:3164–3180CrossRefGoogle Scholar
  39. Yang Y, Huang R, Chen L, Zhang J (1993) Redox behavior of trimanganese tetroxide catalysts. Appl Catal A Gen 101:233–252CrossRefGoogle Scholar
  40. Yao P, Liu H, Wang D, Chen J, Li G, An T (2018) Enhanced visible-light photocatalytic activity to volatile organic compounds degradation and deactivation resistance mechanism of titania confined inside a metal-organic framework. J Colloid Interface Sci 522:174–182CrossRefGoogle Scholar
  41. Zhang X, Junhui Y, Jing Y, Ting C, Bei X, Zhe L, Kunfeng Z, Ling Y, Dannong H (2018) Excellent low-temperature catalytic performance of nanosheet Co-Mn oxides for total benzene oxidation. Appl Catal A Gen 566:104–112CrossRefGoogle Scholar
  42. Zhang Z, Jiang Z, Shangguan W (2016) Low-temperature catalysis for VOCs removal in technology and application: a state-of-the-art review. Catal Today 264:270–278CrossRefGoogle Scholar
  43. Zhu R, Mao Y, Jiang L, Chen J (2015a) Performance of chlorobenzene removal in a nonthermal plasma catalysis reactor and evaluation of its byproducts. Chem Eng J 279:463–471CrossRefGoogle Scholar
  44. Zhu X, Gao X, Qin R, Zeng Y, Qu R, Zheng C, Tu X (2015b) Plasma-catalytic removal of formaldehyde over Cu-Ce catalysts in a dielectric barrier discharge reactor. Appl Catal B Environ 170-171:293–300CrossRefGoogle Scholar
  45. Zhu X, Tu X, Chen M, Yang Y, Zheng C, Zhou J, Gao X (2017) La0.8M0.2MnO3 (M = Ba, Ca, Ce, Mg and Sr) perovskite catalysts for plasma-catalytic oxidation of ethyl acetate. Catal Commun 92:35–39CrossRefGoogle Scholar
  46. Zuo H, Xu D, Liu W, Dan H, Liu X, Lin S, Hou P (2018) Heat-treated dolomite-palygorskite clay supported MnOx catalysts prepared by various methods for low temperature selective catalytic reduction (SCR) with NH3. Appl Clay Sci 152:276–283CrossRefGoogle Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Research Center for Combustion and Environmental TechnologyShanghai Jiao Tong UniversityShanghaiPeople’s Republic of China
  2. 2.Department of Energy and Material Sciences, Faculty of Engineering SciencesKyushu UniversityKasugaJapan

Personalised recommendations