High-Temperature Tribo-Oxidative Wear of a Cu-Based Metal-Matrix Composite Dry Sliding Against Heat-Treated Steel

  • Priyadarshini Jayashree
  • Mauro Bortolotti
  • Simone Turani
  • Giovanni StraffeliniEmail author
Original Paper
  • 117 Downloads

Abstract

The tribo-oxidative wear of a Cu-based metal-matrix composite, dry sliding against a steel counterface, was investigated at 400 °C by means of pin-on-disc sliding tests. The applied pressure was 0.5 and 1 MPa, and the sliding velocity was 1.57 and 7 m/s. Special emphasis was given to the determination of the characteristics of the friction layers, whose constituents were identified and quantified by means of SEM and XRD measurements, and using the Rietveld analysis of the XRD patterns. The pin friction layers were found to be mainly made by compacted CuO/Cu2O oxides and by Fe oxides (mainly Fe3O4) transferred from the disc surface. The disc friction layers were made by CuO transferred from the pin surface and Fe3O4-rich regions, formed by direct asperity oxidation, due to the quite high (600 °C or more) flash temperatures achieved during sliding. This information was used to explain the experimental dependency of the coefficient of friction and the wear rate with the adopted tribological parameters.

Keywords

Tribo-oxidative wear Cu-based metal-matrix composite Friction layer Rietveld analysis 

Notes

Acknowledgements

The authors gratefully acknowledge the contribution of Luca Bresciani of Brembo for helpful discussions.

References

  1. 1.
    Quinn, T.F.J.: Oxidational wear. Wear 18, 413–419 (1971)Google Scholar
  2. 2.
    Quinn, T.F.J., Sullivan, J.L., Rowson, D.M.: Origins and development of oxidational wear at low ambient temperatures. Wear 94, 175–191 (1984)Google Scholar
  3. 3.
    Stott, F.H.: The role of oxidation in the wear of alloys. Tribol. Int. 31, 61–71 (1998)Google Scholar
  4. 4.
    Lim, F.C., Ashby, M.F.: Wear mechanism maps. Acta Metal. 35, 1–24 (1987)Google Scholar
  5. 5.
    Stott, F.H., Jordan, M.P.: The effects of load and substrate hardness on the development and maintenece of wear-protective layers during sliding at elevated temperatures. Wear 250, 391–400 (2001)Google Scholar
  6. 6.
    Vingsbo, O., Hogmark, S.: Wear of steels. In: Rigney, D.A. (ed.) Fundamentals of Friction and Wear of Materials, pp. 41–52. ASM, Materials Park (1980)Google Scholar
  7. 7.
    Zhang, Q.Y., Chen, K.M., Wang, L., Wang, S.Q.: Characteristics of oxidative wear and oxidative mild wear. Tribol. Int. 61, 214–223 (2013)Google Scholar
  8. 8.
    Straffelini, G., Trabucco, D., Molinari, A.: Oxidative wear of heat-treated steels. Wear 250, 485–491 (2001)Google Scholar
  9. 9.
    Straffelini, G., Trabucco, D., Molinari, A.: Sliding wear of austenitic and austenitic-ferritic stainless steels. Metal. Mater. Trans. 33A, 613–624 (2002)Google Scholar
  10. 10.
    Straffelini, G.: Experimental observations of subsurface damage and oxidative wear in Al-based metal-matrix composites. Wear 245, 216–222 (2000)Google Scholar
  11. 11.
    Stachowiak, G.W., Batchelor, A.W.: Engineering Tribology, Tribology Series 24. Elsevier, Amsterdam (1993)Google Scholar
  12. 12.
    Straffelini, G.: Friction and Wear, Methodologies for Design and Control. Springer, Cham (2015)Google Scholar
  13. 13.
    Wang, S.Q., Wang, L., Zhao, Y.T., Sun, Y., Yang, Z.R.: Mild-to-severe wear transition and transition region of oxidative wear in steels. Wear 306, 311–320 (2013)Google Scholar
  14. 14.
    Straffelini, G., Molinari, A.: Mild sliding wear of Fe-0.2%C, Ti-6%Al-4%V and Al-7072: a comparative study. Tribol. Lett. 41, 227–238 (2011)Google Scholar
  15. 15.
    Stott, F.H.: High-temperature sliding wear of metals. Tribol. Int. 35, 489–495 (2002)Google Scholar
  16. 16.
    Wang, S.Q., Wei, M.X., Wang, F., Zhao, Y.T.: Transition of elevated-temperature wear mechanisms and the oxidative delamination wear in hot-working die steels. Tribol. Int. 43, 577–584 (2010)Google Scholar
  17. 17.
    Sullivan, J.L., Hodgson, S.G.: A study of mild oxidational wear for conditions of low load and speed. Wear 121, 95–106 (1987)Google Scholar
  18. 18.
    Sullivan, J.L., Atwhwal, S.S.: Mild wear of a low alloy steel at temperatures up to 500 °C. Tribol. Int. 16, 123–131 (1983)Google Scholar
  19. 19.
    Blau, P.J.: Elevated-temperature tribology of metallic materials. Tribol. Int. 43, 1203–1208 (2010)Google Scholar
  20. 20.
    Mann, R., Magnier, V., Brunel, J.-F., Brunel, F., Dufrenoy, P., Henrion, M.: Relation between mechanical behavior and microstructure of a sintered material for braking application. Wear 386–387, 1–16 (2017)Google Scholar
  21. 21.
    Peng, T., Yan, Q., Li, G., Zhang, X.: The influence of Cu/Fe ratio on the tribological behavior of brake friction materials. Tribol. Lett. 66, 18 (2018)Google Scholar
  22. 22.
    Peng, T., Yan, Q., Li, G., Zhang, X., Wen, Z., Jin, X.: The braking behavior of Cu-based metallic brake pad for high-speed train under different initial braking speed. Tribol. Lett. 65, 135 (2017)Google Scholar
  23. 23.
    Xiao, Y., Zhang, Z., Yao, P., Fan, K., Zhou, H., Gong, T., Zhao, L., Deng, M.: Mechanical and tribological behaviors of copper metal matrix composites for brake pads used in high-speed trains. Tribol. Int. 119, 585–592 (2018)Google Scholar
  24. 24.
    Priyadarshini, J., Federici, M., Bresciani, L., Turani, S., Sicigliano, R., Straffelini, G.: Effect of steel counterface on the dry sliding behavior of a Cu-based metal matrix composite. Tribol. Lett. 66, 123 (2018)Google Scholar
  25. 25.
    Zhou, H., Yao, P., Xiao, Y., Fan, K., Zhang, Z., Gong, T., Zhao, L., Deng, M., Liu, C., Ling, P.: Friction and wear maps of copper metal matrix composites with different iron volume content. Tribol. Int. 132, 199–210 (2019)Google Scholar
  26. 26.
    Altomare, A., Corriero, N., Cuocci, C., Falcicchio, A., Moliterni, A., Rizzi, R.: QUALX2.0: a qualitative phase analysis software using the freely available database POW-COD. J. Appl. Crystallogr. 48, 598–603 (2015)Google Scholar
  27. 27.
    Gražulis, S., Daškevič, A., Merkys, A., Chateigner, D., Lutterotti, L., Quirós, M., Serebryanaya, N.R., Moeck, P., Downs, R.T., Le Bail, A.: Crystallography open database (COD): an open-access collection of crystal structures and platform for world-wide collaboration. Nucleic Acids Res. 40, D420–D427 (2012)Google Scholar
  28. 28.
    Lutterotti, L., Bortolotti, M., Ischia, G., Lonardelli, I., Wenk, H.R.: Rietveld texture analysis from diffraction images. Zeitschrift Für Krist. Suppl. 2007, 125–130 (2007)Google Scholar
  29. 29.
    Matthies, S.: Standard functions in the texture analysis. Phys. Status Solidi 101, K111–K115 (1980)Google Scholar
  30. 30.
    Young, R.: (1993) In: Young, R.A. (ed.) The Rietveld Method, p. 312. Oxford Univ. Press, OxfordGoogle Scholar
  31. 31.
    Straffelini, G., Verlinsky, S., Verma, P.C., Valota, G., Gialanella, S.: Wear and contact temperature evolution in Pin-on-Disc tribotesting of low metallic friction material sliding against pearlitic cast iron. Tribol. Lett. 62, 36 (2016)Google Scholar
  32. 32.
    Federici, M., Straffelini, G., Gialanella, S.: Pin-on-Disc testing of low metallic friction material sliding against HVOF coated cast iron: modelling of the contact temperature evolution. Tribol. Lett. 65, 121 (2017)Google Scholar
  33. 33.
    Lee, P.W., Filip, P.: Friction and wear of Cu-free and Sb-free environmental friendly automotive brake materials. Wear 302, 1404–1413 (2013)Google Scholar
  34. 34.
    Verma, P.C., Menapace, L., Bonfanti, A., Ciudin, R., Gialanella, S., Straffelini, G.: Braking pad-disc system: wear mechanisms and formation of wear fragents. Wear 322–232, 251–258 (2015)Google Scholar
  35. 35.
    Henke, B.L., Gullikson, E.M., Davis, J.C.: X-ray interactions: photoabsorption, scattering, transmission, and reflection at E = 50–30000 eV, Z = 1–92. At Data Nucl Data Tables 54(2), 181–342 (1993)Google Scholar
  36. 36.
    Ragone, D.V.: Thermodynamics of materials. Wiley, New York (1995)Google Scholar
  37. 37.
    Palkar, V.R., Ayyub, P., Chattopadhyay, S., Multani, M.: Size-induced structural transitions in the Cu-O and Ce-O systems. Phys. Rev. B 53, 2167 (1996)Google Scholar
  38. 38.
    Scardi, P., Leoni, M., Straffelini, G., De Giudici, G.: Microstructure of Cu-Be alloy triboxidative wear debris. Acta Mater. 55, 2531–2538 (2007)Google Scholar
  39. 39.
    Xiao, X., Yin, Y., Bao, J., Lu, L., Feng, X.: Review on the friction and wear of brake materials. Adv. Mech. Eng. 8(5), 1–10 (2016)Google Scholar
  40. 40.
    Lim, S.C., Ashby, M.F., Brunton, J.H.: The effects of sliding conditions on the dry friction of metals. Acta Metal. 37, 767–772 (1989)Google Scholar
  41. 41.
    Rodrigues, A.C.P., Osterle, W., Gradt, T., Azevedo, G.R.F.: Impact of copper nanoparticles on tribofilm formation determined by pin-on-disc tests with powder supply: addition of artificial third body consisting of Fe3O4, Cu and graphite. Tribol. Int. 110, 103–112 (2017)Google Scholar
  42. 42.
    Pasaribu, H.T., Sloetjes, J.W., Shipper, D.J.: Friction reduction by adding copper oxide into alumina and zirconia ceramics. Wear 225, 699–707 (2003)Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Department of Industrial EngineeringUniversity of TrentoTrentoItaly
  2. 2.Brembo s.p.ACurnoItaly

Personalised recommendations